Material Data Center is a leading international information system for the plastics industry. Material Data Center offers a comprehensive plastics database, calculation tools, CAE interfaces, a literature database and an application database. For more information about Material Data Center visit www.materialdatacenter.com.

This is the free Material Data Center Datasheet of Rilsan® BZM 8 O T3L - PA11-GF8 - ARKEMA

Material Data Center offers the following functions for Rilsan® BZM 8 O T3L:
unit conversion, PDF datasheet print, comparison with other plastics

Check here, which other Rilsan datasheets, application examples or technical articles are available in Material Data Center

Use the following short links to get directly to the properties of interest in this datasheet:
Any use of this information falls under the rules of our disclaimer.
材料文字说明
PA11, MHLR, 18-030, GF8

Rilsan® BZM 8 O T3L is a fiberglass reinforced polyamide 11 produced from a renewable source.
This natural grade is designed for injection. This grade has been engineered and stabilized to improve color stability.

The percentage of renewable carbon is 97% (calculated value, based on ASTM D6866).
Note that this document is a temporary technical data sheet.



Main applications:
  • Spring for quick connectors
  • Outsoles

Packaging:
This grade is delivered dried in sealed packaging (25 kg bags) ready to be processed.

Shelf Life:
Two years from the delivery. For any use above this limit, please refer to our technical services.
加工/物理特性干 / 已调节单位Test Standard
ISO数据
熔体体积流动速度, MVR 15 / * cm³/10min ISO 1133
温度 235 / * °C -
载荷 5 / * kg -
模塑收缩率, 平行 1.1 / * % ISO 294-4, 2577
模塑收缩率, 垂直 0.9 / * % ISO 294-4, 2577
机械性能干 / 已调节单位Test Standard
ISO数据
拉伸模量 - / 2300 MPa ISO 527
断裂应力 - / 56 MPa ISO 527
断裂伸长率 - / 26 % ISO 527
简支梁缺口冲击强度, +23°C - / 12 kJ/m² ISO 179/1eA
简支梁缺口冲击强度, -30°C - / 7.8 kJ/m² ISO 179/1eA
肖氏硬度D 73 / * - ISO 7619-1
热性能干 / 已调节单位Test Standard
ISO数据
熔融温度, 10°C/min 189 / * °C ISO 11357-1/-3
其它性能干 / 已调节单位Test Standard
密度 1080 / 1080 kg/m³ ISO 1183
Biobased content 97 % -
函数
应力-应变.  , Rilsan® BZM 8 O T3L (烘干), PA11-GF8, ARKEMA
正割模量-应变.  , Rilsan® BZM 8 O T3L (烘干), PA11-GF8, ARKEMA
典型数据
加工方法
注塑
供货形式
粒料
特殊性能
经光稳处理的/耐光的, 经耐紫外线处理的/耐气候的, 经热稳处理的/耐热的
Certifications
生物相容
地区供应
其他信息
注塑成型

Processing conditions:

- Typical melt temperature (Min / Recommended / Max) : 250°C / 270°C / 290°C.
- Mold temperature : 40 - 90°C

- Drying time and temperature (only necessary for bags opened for more than two hours) : 4-6 hours at 80-90°C.

权利义务的法律声明
Copyright Altair Engineering GmbH. Altair Engineering GmbH assumes no liability for the system to be free of errors. The user takes sole responsibility for the use of this data under the exclusion of every liability from Altair Engineering GmbH; this is especially valid for claims of compensation resulting from consequential damages. Altair explicitly points out that any decision about the application of materials must be double checked with the producer of this material. This includes all contents of this system. Copyright laws are applicable for the content of this system.
Created: Source: www.materialdatacenter.com


Material Data Center is provided by M-Base Engineering + Software GmbH. M-Base Engineering + Software GmbH assumes no liability for the system to be free of errors. Any decision about the application of materials must be double checked with the producer of this material.

Additional information about this material, like producer contact address, etc. can be found at www.materialdatacenter.com. For access to this extra information a registration is requested. Free online registration is available.