Material Data Center is a leading international information system for the plastics industry. Material Data Center offers a comprehensive plastics database, calculation tools, CAE interfaces, a literature database and an application database. For more information about Material Data Center visit www.materialdatacenter.com.

This is the free Material Data Center Datasheet of Rilsan® BZM 8 O T3L - PA11-GF8 - ARKEMA

Check here, which other Rilsan datasheets, application examples or technical articles are available in Material Data Center

加工/物理特性 - 机械性能 - 热性能 - 其它性能 - 函数

Any use of this information falls under the rules of our disclaimer.

材料文字说明

PA11, MHLR, 18-030, GF8

Rilsan® BZM 8 O T3L is a fiberglass reinforced polyamide 11 produced from a renewable source.
This natural grade is designed for injection. This grade has been engineered and stabilized to improve color stability.

According to ASTM D6866, the biobased carbon content is measured at 100%.

Note that this document is a temporary technical data sheet.

Main applications:

• Spring for quick connectors
• Outsoles

Packaging:
This grade is delivered dried in sealed packaging (25 kg bags) ready to be processed.

Shelf Life:
Two years from the delivery. For any use above this limit, please refer to our technical services.

加工/物理特性	干 / 已调节	单位	Test Standard
ISO数据
熔体体积流动速度, MVR	15 / *	cm³/10min	ISO 1133
温度	235 / *	°C	-
载荷	5 / *	kg	-
模塑收缩率, 平行	1.1 / *	%	ISO 294-4, 2577
模塑收缩率, 垂直	0.8 / *	%	ISO 294-4, 2577

机械性能	干 / 已调节	单位	Test Standard
ISO数据
拉伸模量	- / 2300	MPa	ISO 527
断裂应力	- / 56	MPa	ISO 527
断裂伸长率	- / 26	%	ISO 527
简支梁缺口冲击强度, +23°C	- / 12	kJ/m²	ISO 179/1eA
简支梁缺口冲击强度, -30°C	- / 7.8	kJ/m²	ISO 179/1eA
肖氏硬度D	73 / *	-	ISO 7619-1

热性能	干 / 已调节	单位	Test Standard
ISO数据
熔融温度, 10°C/min	189 / *	°C	ISO 11357-1/-3

其它性能	干 / 已调节	单位	Test Standard
密度	1080 / 1080	kg/m³	ISO 1183
Biobased content	97	%	-

函数

典型数据

加工方法

注塑

供货形式

粒料

特殊性能

经光稳处理的/耐光的, 经耐紫外线处理的/耐气候的, 经热稳处理的/耐热的

Certifications

生物相容

地区供应

北美, 欧洲, 亚太, 中南美洲, 中东/非洲

其他信息

注塑成型

Processing conditions:

- Typical melt temperature (Min / Recommended / Max) : 250°C / 270°C / 290°C.
- Mold temperature : 40 - 90°C

- Drying time and temperature (only necessary for bags opened for more than two hours) : 4-6 hours at 80-90°C.

权利义务的法律声明

Copyright Altair Engineering GmbH. Altair Engineering GmbH assumes no liability for the system to be free of errors. The user takes sole responsibility for the use of this data under the exclusion of every liability from Altair Engineering GmbH; this is especially valid for claims of compensation resulting from consequential damages. Altair explicitly points out that any decision about the application of materials must be double checked with the producer of this material. This includes all contents of this system. Copyright laws are applicable for the content of this system.

Created: Source: www.materialdatacenter.com

Material Data Center is provided by M-Base Engineering + Software GmbH. M-Base Engineering + Software GmbH assumes no liability for the system to be free of errors. Any decision about the application of materials must be double checked with the producer of this material.

Additional information about this material, like producer contact address, etc. can be found at www.materialdatacenter.com. For access to this extra information a registration is requested. Free online registration is available.