Material Data Center is a leading international information system for the plastics industry. Material Data Center offers a comprehensive plastics database, calculation tools, CAE interfaces, a literature database and an application database. For more information about Material Data Center visit www.materialdatacenter.com.

This is the free Material Data Center Datasheet of Rilsan® BZM 8 O T3L - PA11-GF8 - ARKEMA

Material Data Center offers the following functions for Rilsan® BZM 8 O T3L:
unit conversion, PDF datasheet print, comparison with other plastics

Check here, which other Rilsan datasheets, application examples or technical articles are available in Material Data Center

Use the following short links to get directly to the properties of interest in this datasheet:
Any use of this information falls under the rules of our disclaimer.
商品の説明文
PA11, MHLR, 18-030, GF8

Rilsan® BZM 8 O T3L is a fiberglass reinforced polyamide 11 produced from a renewable source.
This natural grade is designed for injection. This grade has been engineered and stabilized to improve color stability.

According to ASTM D6866, the biobased carbon content is measured at 100%.

Note that this document is a temporary technical data sheet.



Main applications:
  • Spring for quick connectors
  • Outsoles

Packaging:
This grade is delivered dried in sealed packaging (25 kg bags) ready to be processed.

Shelf Life:
Two years from the delivery. For any use above this limit, please refer to our technical services.
Processing/Physical Characteristics乾燥/調湿単位テスト基準
ISO データ
メルトボリュームレイト, MVR 15 / * cm³/10min ISO 1133
温度 235 / * °C -
荷重 5 / * kg -
成形収縮率, 平行 1.1 / * % ISO 294-4, 2577
成形収縮率, 直角 0.8 / * % ISO 294-4, 2577
機械的特性乾燥/調湿単位テスト基準
ISO データ
引張弾性率 - / 2300 MPa ISO 527
破壊応力 - / 56 MPa ISO 527
破壊ひずみ - / 26 % ISO 527
ノッチ付きシャルピー衝撃強さ, +23°C - / 12 kJ/m² ISO 179/1eA
ノッチ付きシャルピー衝撃強さ, -30°C - / 7.8 kJ/m² ISO 179/1eA
ショア硬さD 73 / * - ISO 7619-1
熱的特性乾燥/調湿単位テスト基準
ISO データ
溶融温度, 10°C/min 189 / * °C ISO 11357-1/-3
その他の特性.乾燥/調湿単位テスト基準
密度 1080 / 1080 kg/m³ ISO 1183
Biobased content 97 % -
機能
 応力-ひずみ. , Rilsan® BZM 8 O T3L (乾燥), PA11-GF8, ARKEMA
 割線弾性率−ひずみ. , Rilsan® BZM 8 O T3L (乾燥), PA11-GF8, ARKEMA
特殊な特性
成形加工法.
射出成形.
納入形状.
ペレット.
特殊な特性.
光安定化., 紫外線安定化., 熱安定化.
Certifications
Contains renewable resources
領域別の利用可能性
その他の情報
村遜速揃

Processing conditions:

- Typical melt temperature (Min / Recommended / Max) : 250°C / 270°C / 290°C.
- Mold temperature : 40 - 90°C

- Drying time and temperature (only necessary for bags opened for more than two hours) : 4-6 hours at 80-90°C.

Disclaimer
Copyright Altair Engineering GmbH. Altair Engineering GmbH assumes no liability for the system to be free of errors. The user takes sole responsibility for the use of this data under the exclusion of every liability from Altair Engineering GmbH; this is especially valid for claims of compensation resulting from consequential damages. Altair explicitly points out that any decision about the application of materials must be double checked with the producer of this material. This includes all contents of this system. Copyright laws are applicable for the content of this system.
Created: Source: www.materialdatacenter.com


Material Data Center is provided by M-Base Engineering + Software GmbH. M-Base Engineering + Software GmbH assumes no liability for the system to be free of errors. Any decision about the application of materials must be double checked with the producer of this material.

Additional information about this material, like producer contact address, etc. can be found at www.materialdatacenter.com. For access to this extra information a registration is requested. Free online registration is available.