Material Data Center is a leading international information system for the plastics industry. Material Data Center offers a comprehensive plastics database, calculation tools, CAE interfaces, a literature database and an application database. For more information about Material Data Center visit www.materialdatacenter.com.

This is the free Material Data Center Datasheet of LEXAN™ Copolymer MPX2 - Asia - PC - Saudi Basic Industries Corporation (SABIC)

Material Data Center offers the following functions for LEXAN™ Copolymer MPX2 - Asia:
unit conversion, PDF datasheet print, comparison with other plastics

Check here, which other Lexan datasheets, application examples or technical articles are available in Material Data Center

Use the following short links to get directly to the properties of interest in this datasheet:
Processing/Physical Characteristics - 기계적 특성 - 열적 특성 - 기타 특성 - Processing Recommendation Injection Molding
Any use of this information falls under the rules of our disclaimer.
제품 설명서
LEXAN MPX2 polycarbonate (PC) siloxane copolymer resin is a injection molding (IM) grade with release properties. This resin offers good low temperature ductility in combination with medium flow characteristics and excellent processability with opportunities for shorter IM cycle times compared to standard IM PC resins. LEXAN MPX2 resin is a general purpose product available for wide range of colors and may be an excellent candidate for a broad range of applications.

UL Yellow Card Link E207780-102102565
Processing/Physical Characteristics값단위시험규격
ISO 데이터
용융 부피 - 흐름 속도, MVR 13 cm³/10min ISO 1133
온도 300 °C -
하중 1.2 kg -
ASTM 데이터
용융 흐름성, MFI 14 g/10min ASTM D 1238
온도 300 °C -
하중 1.2 kg -
기계적 특성값단위시험규격
ASTM 데이터
인장탄성률 2100 MPa ASTM D 638
항복강도 57 MPa ASTM D 638
파단시 강도 56 MPa ASTM D 638
항복변형률 4.8 % ASTM D 638
파단시 신율 90 % ASTM D 638
굴곡 계수 2100 MPa ASTM D 790
아이조드 충격은 노치, 1/8 in 810 J/m ASTM D 256
아이조드 충격은 노치, Low-Temperature 650 J/m ASTM D 256
온도 -30 °C -
열적 특성값단위시험규격
ISO 데이터
비카트 연화 온도, 120°C/h 50N 138 °C ISO 306
두께 H인 제품의 난연성 HB class IEC 60695-11-10
테스트 두께 0.5 mm -
ASTM 데이터
DTUL @ 264 psi 116 °C ASTM D 648
기타 특성값단위시험규격
물에서의 흡수성 0.12 % ISO 62와 유사
조건에서의 흡습성 0.09 % ISO 62와 유사
밀도 1190 kg/m³ ISO 1183
밀도 1180 kg/m³ ASTM D 792
Processing Recommendation Injection Molding값단위시험규격
Pre-drying - Temperature 120 °C -
Pre-drying - Time 3 - 4 h -
Processing humidity ≤0.02 % -
용융수지온도 295 - 315 °C -
성형온도 70 - 95 °C -
Zone 1 270 - 295 °C -
Zone 2 280 - 305 °C -
Zone 3 295 - 315 °C -
Screw speed 40 - 70 rpm -
Back pressure 0.3 - 0.7 MPa -
특징
생산 공정
사출 성형
지역별 검색
쩐횈쩍횄쩐횈 횇횂횈챵쩐챌 횁철쩔짧
Disclaimer
Copyright Altair Engineering GmbH. Altair Engineering GmbH assumes no liability for the system to be free of errors. The user takes sole responsibility for the use of this data under the exclusion of every liability from Altair Engineering GmbH; this is especially valid for claims of compensation resulting from consequential damages. Altair explicitly points out that any decision about the application of materials must be double checked with the producer of this material. This includes all contents of this system. Copyright laws are applicable for the content of this system.
Created: Source: www.materialdatacenter.com