Material Data Center is a leading international information system for the plastics industry. Material Data Center offers a comprehensive plastics database, calculation tools, CAE interfaces, a literature database and an application database. For more information about Material Data Center visit www.materialdatacenter.com.

This is the free Material Data Center Datasheet of CELANEX® 1632Z - PBT-GF15 - Celanese

Material Data Center offers the following functions for CELANEX® 1632Z:
unit conversion, PDF datasheet print, comparison with other plastics, snap fit calculation, beam deflection calculation, CAE Interfaces

Check here, which other Celanex datasheets, application examples or technical articles are available in Material Data Center

Use the following short links to get directly to the properties of interest in this datasheet:
Processing/Physical Characteristics - 機械的特性 - 熱的特性 - その他の特性.
Any use of this information falls under the rules of our disclaimer.
商品の説明文
Celanex 1632Z is a general purpose, 15% fiberglass reinforced polybutylene terephthalate with a good balance of mechanical properties and processability.

Flammability at thickness h (0.8 mm)HB-
Processing/Physical Characteristics値単位テスト基準
ISO データ
成形収縮率, 平行 0.5 % ISO 294-4, 2577
成形収縮率, 直角 1.0 % ISO 294-4, 2577
機械的特性値単位テスト基準
ISO データ
引張弾性率 5400 MPa ISO 527
破壊応力 95 MPa ISO 527
破壊ひずみ 5.4 % ISO 527
ノッチ付きシャルピー衝撃強さ, +23°C 5.4 kJ/m² ISO 179/1eA
熱的特性値単位テスト基準
ISO データ
溶融温度, 10°C/min 225 °C ISO 11357-1/-3
ガラス転移点, 10°C/min 60 °C ISO 11357-1/-2
荷重たわみ温度, 1.80 MPa 189 °C ISO 75-1/-2
荷重たわみ温度, 0.45 MPa 217 °C ISO 75-1/-2
線膨張係数, 平行 40 E-6/K ISO 11359-1/-2
線膨張係数, 直角 110 E-6/K ISO 11359-1/-2
厚さhでの燃焼性 HB class IEC 60695-11-10
試験片の厚さ 0.8 mm -
その他の特性.値単位テスト基準
吸湿率 0.1 % Sim. to ISO 62
密度 1410 kg/m³ ISO 1183
特殊な特性
成形加工法.
射出成形.
納入形状.
ペレット.
添加剤.
滑剤.
アプリケーション
汎用
領域別の利用可能性
北アメリカ., ヨーロッパ., アジア/太平洋地域., 南・中央アメリカ., 近東/アフリカ
その他の情報
村遜速揃
Injection speed, injection pressure and holding pressure have to be optimized to the individual article geometry. To avoid material degradation during processing low back pressure and minimum screw speed have to be used. Overheating of the material has to be avoided. Up to 25% clean and dry regrind may be used.
Disclaimer
Copyright Altair Engineering GmbH. Altair Engineering GmbH assumes no liability for the system to be free of errors. The user takes sole responsibility for the use of this data under the exclusion of every liability from Altair Engineering GmbH; this is especially valid for claims of compensation resulting from consequential damages. Altair explicitly points out that any decision about the application of materials must be double checked with the producer of this material. This includes all contents of this system. Copyright laws are applicable for the content of this system.
Created: Source: www.materialdatacenter.com


Material Data Center is provided by M-Base Engineering + Software GmbH. M-Base Engineering + Software GmbH assumes no liability for the system to be free of errors. Any decision about the application of materials must be double checked with the producer of this material.

Additional information about this material, like producer contact address, etc. can be found at www.materialdatacenter.com. For access to this extra information a registration is requested. Free online registration is available.