Material Data Center is a leading international information system for the plastics industry. Material Data Center offers a comprehensive plastics database, calculation tools, CAE interfaces, a literature database and an application database. For more information about Material Data Center visit www.materialdatacenter.com.

This is the free Material Data Center Datasheet of CELANEX® 1600A - PBT - Celanese

Material Data Center offers the following functions for CELANEX® 1600A:
unit conversion, PDF datasheet print, comparison with other plastics, snap fit calculation, beam deflection calculation, CAE Interfaces

Check here, which other Celanex datasheets, application examples or technical articles are available in Material Data Center

Use the following short links to get directly to the properties of interest in this datasheet:
Any use of this information falls under the rules of our disclaimer.
商品の説明文
Celanex 1600A is a high molecular weight grade of unreinforced polybutylene terephthalate for use in both extrusion and injection molding applications.

Flammability at thickness h (0.75 mm)HB-
Processing/Physical Characteristics単位テスト基準
ISO データ
メルトボリュームレイト, MVR 9 cm³/10min ISO 1133
温度 250 °C -
荷重 2.16 kg -
成形収縮率, 平行 1.9 % ISO 294-4, 2577
成形収縮率, 直角 1.9 % ISO 294-4, 2577
機械的特性単位テスト基準
ISO データ
引張弾性率 2550 MPa ISO 527
降伏応力 60 MPa ISO 527
降伏ひずみ 5 % ISO 527
破壊呼びひずみ >50 % ISO 527
シャルピー衝撃強さ, +23°C N kJ/m² ISO 179/1eU
シャルピー衝撃強さ, -30°C 210 kJ/m² ISO 179/1eU
ノッチ付きシャルピー衝撃強さ, +23°C 7 kJ/m² ISO 179/1eA
ノッチ付きシャルピー衝撃強さ, -30°C 6.5 kJ/m² ISO 179/1eA
ショア硬さD 77 - ISO 7619-1
熱的特性単位テスト基準
ISO データ
溶融温度, 10°C/min 225 °C ISO 11357-1/-3
ガラス転移点, 10°C/min 60 °C ISO 11357-1/-2
荷重たわみ温度, 1.80 MPa 50 °C ISO 75-1/-2
荷重たわみ温度, 0.45 MPa 150 °C ISO 75-1/-2
ビカット軟化温度, B 185 °C ISO 306
線膨張係数, 平行 110 E-6/K ISO 11359-1/-2
線膨張係数, 直角 103 E-6/K ISO 11359-1/-2
厚さhでの燃焼性 HB class IEC 60695-11-10
試験片の厚さ 0.8 mm -
酸素指数 22 % ISO 4589-1/-2
電気的特性.単位テスト基準
ISO データ
比誘電率, 100Hz 4 - IEC 62631-2-1
比誘電率, 1MHz 3.5 - IEC 62631-2-1
誘電正接, 100Hz 14 E-4 IEC 62631-2-1
誘電正接, 1MHz 210 E-4 IEC 62631-2-1
体積抵抗率 >1E13 Ohm*m IEC 62631-3-1
表面抵抗率 >1E15 Ohm IEC 62631-3-2
耐電圧 23 kV/mm IEC 60243-1
その他の特性.単位テスト基準
吸水率 0.45 % Sim. to ISO 62
吸湿率 0.2 % Sim. to ISO 62
密度 1310 kg/m³ ISO 1183
機能
 せん断弾性率-温度. , CELANEX® 1600A, PBT, Celanese
 応力-ひずみ. , CELANEX® 1600A, PBT, Celanese
 割線弾性率−ひずみ. , CELANEX® 1600A, PBT, Celanese
特殊な特性
成形加工法.
射出成形., フィルム押出成形., 異形押出成形., シート押出成形., その他の押出成形.
納入形状.
ペレット.
領域別の利用可能性
北アメリカ., ヨーロッパ., アジア/太平洋地域., 南・中央アメリカ., 近東/アフリカ
その他の情報
村遜速揃
Injection speed, injection pressure and holding pressure have to be optimized to the individual article geometry. To avoid material degradation during processing low back pressure and minimum screw speed have to be used. Overheating of the material has to be avoided. Up to 25% clean and dry regrind may be used.
Disclaimer
Copyright Altair Engineering GmbH. Altair Engineering GmbH assumes no liability for the system to be free of errors. The user takes sole responsibility for the use of this data under the exclusion of every liability from Altair Engineering GmbH; this is especially valid for claims of compensation resulting from consequential damages. Altair explicitly points out that any decision about the application of materials must be double checked with the producer of this material. This includes all contents of this system. Copyright laws are applicable for the content of this system.
Created: Source: www.materialdatacenter.com


Material Data Center is provided by M-Base Engineering + Software GmbH. M-Base Engineering + Software GmbH assumes no liability for the system to be free of errors. Any decision about the application of materials must be double checked with the producer of this material.

Additional information about this material, like producer contact address, etc. can be found at www.materialdatacenter.com. For access to this extra information a registration is requested. Free online registration is available.