加工/物理特性 | 价值 | 单位 | Test Standard |
ISO数据 |
熔体体积流动速度, MVR |
18 |
cm³/10min |
ISO 1133 |
温度 |
190 |
°C |
- |
载荷 |
2.16 |
kg |
- |
Other Standards[S] |
模塑收缩率, 平行 |
3.0 |
% |
|
S: | These properties are reported by the producer according standards that are different to our defaults. |
机械性能 | 价值 | 单位 | Test Standard |
ISO数据 |
肖氏硬度A |
88 |
- |
ISO 7619-1 |
Other Standards[S] |
弯曲模量, 23°C |
27 |
MPa |
ISO 6721-1 |
弯曲模量 |
72 |
MPa |
ISO 6721-1 |
弯曲模量-温度 |
60 |
°C |
- |
S: | These properties are reported by the producer according standards that are different to our defaults. |
热性能 | 价值 | 单位 | Test Standard |
ISO数据 |
熔融温度, 10°C/min |
160 |
°C |
ISO 11357-1/-3 |
维卡软化温度, A |
90 |
°C |
ISO 306 |
Other Standards[S] |
玻璃化转变温度, 10°C/min |
-13.6 |
°C |
ISO 6721-1 |
S: | These properties are reported by the producer according standards that are different to our defaults. |
其它性能 | 价值 | 单位 | Test Standard |
密度 |
1200 |
kg/m³ |
ISO 1183 |
Bulk density |
457 |
kg/m³ |
- |
3D Data | 价值 | 单位 | Test Standard |
Other Standards[S] |
拉伸强度, flat |
20[1] |
MPa |
DIN 53504 |
拉伸强度, upright |
15[2] |
MPa |
DIN 53504 |
断裂伸长率, flat |
520[1] |
% |
DIN 53504 |
断裂伸长率, upright |
500[2] |
% |
DIN 53504 |
1: | XY-direction | 2: | ZX-direction | S: | These properties are reported by the producer according standards that are different to our defaults. |
典型数据
加工方法
Additive Manufacturing, 镭射烧结
供货形式
粉料, 白色
应用
运动器械
地区供应
北美, 欧洲, 亚太, 中南美洲
权利义务的法律声明
Copyright Altair Engineering GmbH. Altair Engineering GmbH assumes no liability for the system to be free of errors. The user takes sole responsibility for the use of this data under the exclusion of every liability from Altair Engineering GmbH; this is especially valid for claims of compensation resulting from consequential damages. Altair explicitly points out that any decision about the application of materials must be double checked with the producer of this material. This includes all contents of this system. Copyright laws are applicable for the content of this system.