Processing/Physical Characteristics | 値 | 単位 | テスト基準 |
ISO データ |
メルトボリュームレイト, MVR |
18 |
cm³/10min |
ISO 1133 |
温度 |
190 |
°C |
- |
荷重 |
2.16 |
kg |
- |
Other Standards[S] |
成形収縮率, 平行 |
3.0 |
% |
|
S: | These properties are reported by the producer according standards that are different to our defaults. |
機械的特性 | 値 | 単位 | テスト基準 |
ISO データ |
ショア硬さA |
88 |
- |
ISO 7619-1 |
Other Standards[S] |
曲げ弾性率, 23°C |
27 |
MPa |
ISO 6721-1 |
曲げ弾性率 |
72 |
MPa |
ISO 6721-1 |
曲げ弾性率 - 温度 |
60 |
°C |
- |
S: | These properties are reported by the producer according standards that are different to our defaults. |
熱的特性 | 値 | 単位 | テスト基準 |
ISO データ |
溶融温度, 10゚C/min |
160 |
°C |
ISO 11357-1/-3 |
ビカット軟化温度, A |
90 |
°C |
ISO 306 |
Other Standards[S] |
ガラス転移点, 10゚C/min |
-13.6 |
°C |
ISO 6721-1 |
S: | These properties are reported by the producer according standards that are different to our defaults. |
その他の特性. | 値 | 単位 | テスト基準 |
密度. |
1200 |
kg/m³ |
ISO 1183 |
Bulk density |
457 |
kg/m³ |
- |
3D Data | 値 | 単位 | テスト基準 |
Other Standards[S] |
引張強度, flat |
20[1] |
MPa |
DIN 53504 |
引張強度, upright |
15[2] |
MPa |
DIN 53504 |
破壊ひずみ, flat |
520[1] |
% |
DIN 53504 |
破壊ひずみ, upright |
500[2] |
% |
DIN 53504 |
1: | XY-direction | 2: | ZX-direction | S: | These properties are reported by the producer according standards that are different to our defaults. |
特殊な特性
成形加工法.
Additive Manufacturing, Laser Sintering
納入形状.
パウダー., 白
アプリケーション
スポーツ用品
領域別の利用可能性
北アメリカ., ヨーロッパ., アジア/太平洋地域., 南・中央アメリカ.
Disclaimer
Copyright Altair Engineering GmbH. Altair Engineering GmbH assumes no liability for the system to be free of errors. The user takes sole responsibility for the use of this data under the exclusion of every liability from Altair Engineering GmbH; this is especially valid for claims of compensation resulting from consequential damages. Altair explicitly points out that any decision about the application of materials must be double checked with the producer of this material. This includes all contents of this system. Copyright laws are applicable for the content of this system.
Created: Source: www.materialdatacenter.com