Material Data Center is a leading international information system for the plastics industry. Material Data Center offers a comprehensive plastics database, calculation tools, CAE interfaces, a literature database and an application database. For more information about Material Data Center visit www.materialdatacenter.com.

This is the free Material Data Center Datasheet of LEXAN™ FR Resin JK2500 - (PC+ABS)-CF20 - Saudi Basic Industries Corporation (SABIC)

Material Data Center offers the following functions for LEXAN™ FR Resin JK2500:
unit conversion, PDF datasheet print, comparison with other plastics, snap fit calculation, beam deflection calculation, CAE Interfaces

Check here, which other Lexan datasheets, application examples or technical articles are available in Material Data Center

Use the following short links to get directly to the properties of interest in this datasheet:
加工/物理特性 - 机械性能 - 热性能 - 电性能 - 其它性能 - 加工推荐（注塑）
Any use of this information falls under the rules of our disclaimer.
材料文字说明
LEXAN JK2500 compound is based on Polycarbonate/Acrylonitrile Butadiene Styrene (PC/ABS) blend containing 20% carbon fiber. Added features of this grade include: Electrically Conductive, EMI/RFI Shielding Effectiveness of 21 dB at 1.5 mm, Non-Brominated, Non-Chlorinated Flame Retardant.

UL Yellow Card Link E207780-228503
加工/物理特性价值单位Test Standard
ASTM数据
熔融指数, MFI 25 g/10min ASTM D 1238
温度 300 °C -
负载 1.2 kg -
机械性能价值单位Test Standard
ISO数据
拉伸模量 11100 MPa ISO 527
屈服应力 63 MPa ISO 527
屈服伸长率 2.2 % ISO 527
断裂应力 63 MPa ISO 527
断裂伸长率 2.3 % ISO 527
弯曲模量 10100 MPa ISO 178
Izod impact strength, +23°C, 4mm 15 kJ/m² ISO 180/1U
悬臂梁缺口冲击强度, +23°C, 4mm 5 kJ/m² ISO 180/1A
ASTM数据
拉伸模量 11030 MPa ASTM D 638
屈服应力 63 MPa ASTM D 638
断裂拉伸强度 63 MPa ASTM D 638
屈服伸长率 2.3 % ASTM D 638
断裂伸长率 2.4 % ASTM D 638
弯曲模量 9230 MPa ASTM D 790
悬臂梁缺口冲击强度, 1/8 in 53 J/m ASTM D 256
Izod冲击强度, 1/8 in 224 J/m ASTM D 256
热性能价值单位Test Standard
ISO数据
维卡软化温度, 120°C/h 50N 100 °C ISO 306
厚度为h时的燃烧性 V-0 class IEC 60695-11-10
测试用试样的厚度 1.0 mm -
ASTM数据
DTUL @ 66 psi 98 °C ASTM D 648
DTUL @ 264 psi 93 °C ASTM D 648
维卡温度 111 °C ASTM D 1525
电性能价值单位Test Standard
ASTM数据
表面电阻率 10000 Ohm ASTM D 257
体积电阻率 100 Ohm*cm ASTM D 257
其它性能价值单位Test Standard
密度 1310 kg/m³ ASTM D 792
加工推荐（注塑）价值单位Test Standard
预干燥-温度 80 - 90 °C -
预干燥-时间 3 - 4 h -
注塑熔体温度 270 - 310 °C -
模具温度 50 - 95 °C -
1区 260 - 275 °C -
2区 270 - 290 °C -
3区 270 - 300 °C -
螺杆转速 35 - 75 rpm -
背压 0.3 - 0.7 MPa -
典型数据
加工方法
注塑
添加剂
阻燃剂
特殊性能
提高导电性, 阻燃的
特征
EMI衰减/防护
地区供应
北美, 欧洲, 亚太
权利义务的法律声明
Copyright Altair Engineering GmbH. Altair Engineering GmbH assumes no liability for the system to be free of errors. The user takes sole responsibility for the use of this data under the exclusion of every liability from Altair Engineering GmbH; this is especially valid for claims of compensation resulting from consequential damages. Altair explicitly points out that any decision about the application of materials must be double checked with the producer of this material. This includes all contents of this system. Copyright laws are applicable for the content of this system.
Created: Source: www.materialdatacenter.com


Material Data Center is provided by M-Base Engineering + Software GmbH. M-Base Engineering + Software GmbH assumes no liability for the system to be free of errors. Any decision about the application of materials must be double checked with the producer of this material.

Additional information about this material, like producer contact address, etc. can be found at www.materialdatacenter.com. For access to this extra information a registration is requested. Free online registration is available.