Material Data Center is a leading international information system for the plastics industry. Material Data Center offers a comprehensive plastics database, calculation tools, CAE interfaces, a literature database and an application database. For more information about Material Data Center visit www.materialdatacenter.com.

This is the free Material Data Center Datasheet of LEXAN™ Copolymer HFD1232 - Europe - PC - Saudi Basic Industries Corporation (SABIC)

Material Data Center offers the following functions for LEXAN™ Copolymer HFD1232 - Europe:
unit conversion, PDF datasheet print, comparison with other plastics, snap fit calculation, beam deflection calculation, CAE Interfaces

Check here, which other Lexan datasheets, application examples or technical articles are available in Material Data Center

Use the following short links to get directly to the properties of interest in this datasheet:
加工/物理特性 - 机械性能 - 热性能 - 其它性能 - 加工推荐（注塑）
Any use of this information falls under the rules of our disclaimer.
材料文字说明
18 MFR LEXAN High Flow Ductile Copolymer UV-stabilized, available in transparent colors only

UL Yellow Card Link E45329-100987596
加工/物理特性价值单位Test Standard
ISO数据
熔体体积流动速度, MVR 17 cm³/10min ISO 1133
温度 300 °C -
载荷 1.2 kg -
ASTM数据
熔融指数, MFI 18 g/10min ASTM D 1238
温度 300 °C -
负载 1.2 kg -
机械性能价值单位Test Standard
ISO数据
拉伸模量 2150 MPa ISO 527
屈服应力 62 MPa ISO 527
屈服伸长率 6 % ISO 527
断裂应力 66 MPa ISO 527
断裂伸长率 50 % ISO 527
弯曲模量 2120 MPa ISO 178
简支梁冲击强度, +23°C, 3mm N kJ/m² ISO 179/1eU
简支梁冲击强度, -30°C, 3mm N kJ/m² ISO 179/1eU
简支梁缺口冲击强度, +23°C, 3mm 79 kJ/m² ISO 179/1eA
简支梁缺口冲击强度, -30°C, 3mm 14 kJ/m² ISO 179/1eA
Izod冲击强度, +23°C N kJ/m² ISO 180/1U
悬臂梁缺口冲击强度, +23°C, 3mm 67 kJ/m² ISO 180/1A
悬臂梁缺口冲击强度, -30°C, 3mm 22 kJ/m² ISO 180/1A
ASTM数据
拉伸模量 2240 MPa ASTM D 638
屈服应力 58 MPa ASTM D 638
断裂拉伸强度 63 MPa ASTM D 638
屈服伸长率 6 % ASTM D 638
断裂伸长率 135 % ASTM D 638
弯曲模量 2220 MPa ASTM D 790
洛克硬度 R 120 - ASTM D 785
悬臂梁缺口冲击强度, 1/8 in 887 J/m ASTM D 256
低温悬臂梁缺口冲击强度, Low-Temperature 145 J/m ASTM D 256
温度 -30 °C -
热性能价值单位Test Standard
ISO数据
热变形温度, 1.80 MPa 115 °C ISO 75-1/-2
维卡软化温度, B 129 °C ISO 306
维卡软化温度, 120°C/h 50N 130 °C ISO 306
厚度为h时的燃烧性 HB class IEC 60695-11-10
测试用试样的厚度 0.8 mm -
ASTM数据
DTUL @ 66 psi 123 °C ASTM D 648
DTUL @ 264 psi 113 °C ASTM D 648
维卡温度 136 °C ASTM D 1525
其它性能价值单位Test Standard
吸水性 0.3 % 类似ISO 62
吸湿性 0.15 % 类似ISO 62
密度 1200 kg/m³ ISO 1183
密度 1200 kg/m³ ASTM D 792
加工推荐（注塑）价值单位Test Standard
预干燥-温度 105 - 110 °C -
预干燥-时间 3 - 4 h -
注塑熔体温度 260 - 305 °C -
模具温度 50 - 80 °C -
1区 240 - 280 °C -
2区 250 - 295 °C -
3区 260 - 305 °C -
螺杆转速 35 - 75 rpm -
背压 0.3 - 0.7 MPa -
典型数据
加工方法
注塑
特殊性能
透明.
地区供应
欧洲
权利义务的法律声明
Copyright Altair Engineering GmbH. Altair Engineering GmbH assumes no liability for the system to be free of errors. The user takes sole responsibility for the use of this data under the exclusion of every liability from Altair Engineering GmbH; this is especially valid for claims of compensation resulting from consequential damages. Altair explicitly points out that any decision about the application of materials must be double checked with the producer of this material. This includes all contents of this system. Copyright laws are applicable for the content of this system.
Created: Source: www.materialdatacenter.com