Material Data Center is a leading international information system for the plastics industry. Material Data Center offers a comprehensive plastics database, calculation tools, CAE interfaces, a literature database and an application database. For more information about Material Data Center visit www.materialdatacenter.com.

This is the free Material Data Center Datasheet of FORTRON® 4184L6 DW - PPS-(MD+GF)53 - Celanese

Check here, which other Fortron datasheets, application examples or technical articles are available in Material Data Center

Processing/Physical Characteristics - 기계적 특성 - 열적 특성 - 전기적 특성 - 기타 특성 - 도표

Any use of this information falls under the rules of our disclaimer.

제품 설명서

Fortron 4184L6 is an easier flow version of Fortron 4184L4. for drinking water applications.  It offers similar characteristics to the 4184L4. This grade is especially used for thin walled parts requiring long flow lengths, stiffness and dimensional control. Applications made of this grade are typically electronic components.

Flammability @1.6mm nom. thickn.	V-0	-
Flammability at thickness h (0.75 mm)	V-0	-

Processing/Physical Characteristics	값	단위	시험규격
ISO 데이터
성형 수축률, 평행	0.3	%	ISO 294-4, 2577
성형 수축률, 수직	0.6	%	ISO 294-4, 2577
용융 비열용량	1500	J/(kg K)	-

기계적 특성	값	단위	시험규격
ISO 데이터
인장탄성률	16600	MPa	ISO 527
파단시 강도	165	MPa	ISO 527
파단시 신율	1.4	%	ISO 527
챠피 충격 강도 , +23°C	29	kJ/m²	ISO 179/1eU
챠피 충격 강도, -30°C	29	kJ/m²	ISO 179/1eU
챠피 노치드 충격 강도, +23°C	7	kJ/m²	ISO 179/1eA
챠피 노치드 충격 강도, -30°C	7	kJ/m²	ISO 179/1eA

열적 특성	값	단위	시험규격
ISO 데이터
녹는점, 10°C/min	280	°C	ISO 11357-1/-3
유리 전이 온도, 10 °C/min	90	°C	ISO 11357-1/-2
하중하에서의 변형온도, 1.80 MPa	270	°C	ISO 75-1/-2
하중하에서의 변형온도, 8.00 MPa	215	°C	ISO 75-1/-2
선형 열팽창 계수, 평행	24	E-6/K	ISO 11359-1/-2
선형 열팽창 계수, 수직	32	E-6/K	ISO 11359-1/-2
1.5mm 평균두께에서의 난연성	V-0	class	IEC 60695-11-10
테스트 두께	1.5	mm	-
두께 H인 제품의 난연성	V-0	class	IEC 60695-11-10
테스트 두께	0.8	mm	-

전기적 특성	값	단위	시험규격
ISO 데이터
상대 유전뮬, 1MHz	4.7	-	IEC 62631-2-1
소산 인자, 1MHz	20	E-4	IEC 62631-2-1
부피 저항	>1E13	Ohm*m	IEC 62631-3-1
표면 저항	>1E15	Ohm	IEC 62631-3-2
전기 압력	27	kV/mm	IEC 60243-1

기타 특성	값	단위	시험규격
물에서의 흡수성	0.02	%	ISO 62와 유사
밀도	1800	kg/m³	ISO 1183

도표

특징

생산 공정

사출 성형

인도 유형

펠렛 (입자,알갱이)

부가물

이형제

특별 특성

가시광선 안정성, 열안정성

기타 정보

사E성

Predrying in a dehumidified air dryer at 130 - 140 degC/3-4 hours is recommended.
On injection molding machines with 15-25 D long three-section screws, as are usual in the trade, the FORTRON is processable. A shut-off nozzle is preferred to a free-flow nozzle.

Melt temperature 320-340 degC
Mold wall temperature at least 140 degC

A medium injection rate is normally preferred. All mold cavities must be effectively vented.
Tool temperature of at least 135 degC is recommended for parts to achieve maximum crystallizable potential.

Disclaimer

Copyright Altair Engineering GmbH. Altair Engineering GmbH assumes no liability for the system to be free of errors. The user takes sole responsibility for the use of this data under the exclusion of every liability from Altair Engineering GmbH; this is especially valid for claims of compensation resulting from consequential damages. Altair explicitly points out that any decision about the application of materials must be double checked with the producer of this material. This includes all contents of this system. Copyright laws are applicable for the content of this system.

Created: Source: www.materialdatacenter.com

Material Data Center is provided by M-Base Engineering + Software GmbH. M-Base Engineering + Software GmbH assumes no liability for the system to be free of errors. Any decision about the application of materials must be double checked with the producer of this material.

Additional information about this material, like producer contact address, etc. can be found at www.materialdatacenter.com. For access to this extra information a registration is requested. Free online registration is available.