Material Data Center is a leading international information system for the plastics industry. Material Data Center offers a comprehensive plastics database, calculation tools, CAE interfaces, a literature database and an application database. For more information about Material Data Center visit www.materialdatacenter.com.

This is the free Material Data Center Datasheet of FORTRON® 4184L6 DW - PPS-(MD+GF)53 - Celanese

Check here, which other Fortron datasheets, application examples or technical articles are available in Material Data Center

Processing/Physical Characteristics - 機械的特性 - 熱的特性 - 電気的特性. - その他の特性. - 機能

Any use of this information falls under the rules of our disclaimer.

商品の説明文

Fortron 4184L6 is an easier flow version of Fortron 4184L4. for drinking water applications.  It offers similar characteristics to the 4184L4. This grade is especially used for thin walled parts requiring long flow lengths, stiffness and dimensional control. Applications made of this grade are typically electronic components.

Flammability @1.6mm nom. thickn.	V-0	-
Flammability at thickness h (0.75 mm)	V-0	-

Processing/Physical Characteristics	値	単位	テスト基準
ISO データ
成形収縮率, 平行	0.3	%	ISO 294-4, 2577
成形収縮率, 直角	0.6	%	ISO 294-4, 2577
溶融時の比熱	1500	J/(kg K)	-

機械的特性	値	単位	テスト基準
ISO データ
引張弾性率	16600	MPa	ISO 527
破壊応力	165	MPa	ISO 527
破壊ひずみ	1.4	%	ISO 527
シャルピー衝撃強さ, +23°C	29	kJ/m²	ISO 179/1eU
シャルピー衝撃強さ, -30°C	29	kJ/m²	ISO 179/1eU
ノッチ付きシャルピー衝撃強さ, +23°C	7	kJ/m²	ISO 179/1eA
ノッチ付きシャルピー衝撃強さ, -30°C	7	kJ/m²	ISO 179/1eA

熱的特性	値	単位	テスト基準
ISO データ
溶融温度, 10°C/min	280	°C	ISO 11357-1/-3
ガラス転移点, 10°C/min	90	°C	ISO 11357-1/-2
荷重たわみ温度, 1.80 MPa	270	°C	ISO 75-1/-2
荷重たわみ温度, 8.00 MPa	215	°C	ISO 75-1/-2
線膨張係数, 平行	24	E-6/K	ISO 11359-1/-2
線膨張係数, 直角	32	E-6/K	ISO 11359-1/-2
1.5mm厚さでの燃焼性	V-0	class	IEC 60695-11-10
試験片の厚さ	1.5	mm	-
厚さhでの燃焼性	V-0	class	IEC 60695-11-10
試験片の厚さ	0.8	mm	-

電気的特性.	値	単位	テスト基準
ISO データ
比誘電率, 1MHz	4.7	-	IEC 62631-2-1
誘電正接, 1MHz	20	E-4	IEC 62631-2-1
体積抵抗率	>1E13	Ohm*m	IEC 62631-3-1
表面抵抗率	>1E15	Ohm	IEC 62631-3-2
耐電圧	27	kV/mm	IEC 60243-1

その他の特性.	値	単位	テスト基準
吸水率	0.02	%	Sim. to ISO 62
密度	1800	kg/m³	ISO 1183

機能

特殊な特性

成形加工法.

射出成形.

納入形状.

ペレット.

添加剤.

離型剤.

特殊な特性.

光安定化., 熱安定化.

その他の情報

村遜速揃

Predrying in a dehumidified air dryer at 130 - 140 degC/3-4 hours is recommended.
On injection molding machines with 15-25 D long three-section screws, as are usual in the trade, the FORTRON is processable. A shut-off nozzle is preferred to a free-flow nozzle.

Melt temperature 320-340 degC
Mold wall temperature at least 140 degC

A medium injection rate is normally preferred. All mold cavities must be effectively vented.
Tool temperature of at least 135 degC is recommended for parts to achieve maximum crystallizable potential.

Disclaimer

Copyright Altair Engineering GmbH. Altair Engineering GmbH assumes no liability for the system to be free of errors. The user takes sole responsibility for the use of this data under the exclusion of every liability from Altair Engineering GmbH; this is especially valid for claims of compensation resulting from consequential damages. Altair explicitly points out that any decision about the application of materials must be double checked with the producer of this material. This includes all contents of this system. Copyright laws are applicable for the content of this system.

Created: Source: www.materialdatacenter.com

Material Data Center is provided by M-Base Engineering + Software GmbH. M-Base Engineering + Software GmbH assumes no liability for the system to be free of errors. Any decision about the application of materials must be double checked with the producer of this material.

Additional information about this material, like producer contact address, etc. can be found at www.materialdatacenter.com. For access to this extra information a registration is requested. Free online registration is available.