Complete Set of CAMPUS® Data, ASTM Data, Biopolymer Database, Application Database, Tradename Database, Literature Database, Toolbox.

Material datasheets available free. Online registration at: www.materialdatacenter.com

Material Data Center is a leading international information system for the plastics industry. Material Data Center offers a comprehensive plastics database, calculation tools, CAE interfaces, a literature database and an application database. For more information about Material Data Center visit www.materialdatacenter.com.

This is the free Material Data Center Datasheet of SABIC® PPcompound 8620 - PP - Saudi Basic Industries Corporation (SABIC)

Material Data Center offers the following functions for SABIC® PPcompound 8620:
unit conversion, PDF datasheet print, comparison with other plastics, snap fit calculation, beam deflection calculation, CAE Interfaces

Check here, which other Sabic datasheets, application examples or technical articles are available in Material Data Center

Use the following short links to get directly to the properties of interest in this datasheet:
Processing/Physical Characteristics - 기계적 특성 - 열적 특성 - 기타 특성 - Processing Recommendation Injection Molding
Any use of this information falls under the rules of our disclaimer.
제품 설명서
SABIC® PPcompound 8620 is a mineral filled, impact modified polypropylene TPO. This material combines scratch resistance and good flow with exterior automotive weathering stability. It was originally designed for painted or unpainted automotive bumper fascia applications where a combination of high stiffness and cold temperature ductility is required. IMDS ID: 209747700
Processing/Physical Characteristics값단위시험규격
ISO 데이터
용융 흐름성, MFI 23 g/10min ISO 1133
온도 230 °C -
负荷 2.16 kg -
기계적 특성값단위시험규격
ISO 데이터
인장탄성률 1680 MPa ISO 527
항복강도 17 MPa ISO 527
항복변형률 4.4 % ISO 527
파단시 강도 11 MPa ISO 527
파단시 신율 39 % ISO 527
굴곡 계수, 23°C 1740 MPa ISO 178
챠피 노치드 충격 강도, +23°C 58 kJ/m² ISO 179/1eA
챠피 노치드 충격 강도, -30°C 7 kJ/m² ISO 179/1eA
아이조드 충격은 노치 6 kJ/m² ISO 180/1A
ASTM 데이터
인장탄성률 1900 MPa ASTM D 638
항복강도 17 MPa ASTM D 638
파단시 강도 12 MPa ASTM D 638
항복변형률 5 % ASTM D 638
파단시 신율 101 % ASTM D 638
굴곡 계수 1380 MPa ASTM D 790
쇼어 D 경도 54 - ASTM D 2240
열적 특성값단위시험규격
ISO 데이터
하중하에서의 변형온도, 1.80 MPa 56 °C ISO 75-1/-2
하중하에서의 변형온도, 0.45 MPa 100 °C ISO 75-1/-2
비카트 연화 온도, A 123 °C ISO 306
ASTM 데이터
DTUL @ 66 psi 98 °C ASTM D 648
DTUL @ 264 psi 52 °C ASTM D 648
기타 특성값단위시험규격
밀도 1030 kg/m³ ISO 1183
밀도 1030 kg/m³ ASTM D 792
Processing Recommendation Injection Molding값단위시험규격
Pre-drying - Temperature 80 - 100 °C -
Pre-drying - Time 2 - 4 h -
용융수지온도 210 - 270 °C -
성형온도 15 - 60 °C -
Zone 1 190 - 230 °C -
Zone 2 200 - 250 °C -
Zone 3 210 - 270 °C -
Nozzle temperature 210 - 270 °C -
Back pressure 1 - 1.5 MPa -
특징
특별 특성
고충격 또는 고충격 보강
Disclaimer
Copyright Altair Engineering GmbH. Altair Engineering GmbH assumes no liability for the system to be free of errors. The user takes sole responsibility for the use of this data under the exclusion of every liability from Altair Engineering GmbH; this is especially valid for claims of compensation resulting from consequential damages. Altair explicitly points out that any decision about the application of materials must be double checked with the producer of this material. This includes all contents of this system. Copyright laws are applicable for the content of this system.
Created: Source: www.materialdatacenter.com


Material Data Center is provided by M-Base Engineering + Software GmbH. M-Base Engineering + Software GmbH assumes no liability for the system to be free of errors. Any decision about the application of materials must be double checked with the producer of this material.

Additional information about this material, like producer contact address, etc. can be found at www.materialdatacenter.com. For access to this extra information a registration is requested. Free online registration is available.