Material Data Center is a leading international information system for the plastics industry. Material Data Center offers a comprehensive plastics database, calculation tools, CAE interfaces, a literature database and an application database. For more information about Material Data Center visit www.materialdatacenter.com.

This is the free Material Data Center Datasheet of NORYL™ Resin PCN2910 - Asia - (PPE+PS)-(GF+P)35 - Saudi Basic Industries Corporation (SABIC)

Material Data Center offers the following functions for NORYL™ Resin PCN2910 - Asia:
unit conversion, PDF datasheet print, comparison with other plastics, snap fit calculation, beam deflection calculation, CAE Interfaces

Check here, which other Noryl datasheets, application examples or technical articles are available in Material Data Center

Use the following short links to get directly to the properties of interest in this datasheet:
Processing/Physical Characteristics - 기계적 특성 - 열적 특성 - 기타 특성 - Processing Recommendation Injection Molding
Any use of this information falls under the rules of our disclaimer.
제품 설명서
NORYL™ PCN2910 resin is a 35% glass/mica filled blend of polyphenylene ether (PPE) + high impact polystyrene (HIPS). This high modulus, injection moldable grade contains non-brominated, non-chlorinated flame retardant and carries a UL94 flame rating of 5VB at 2.3mm, V0 at 3mm, and V1 at 1.5mm. NORYL PCN2910 resin exhibits good dimensional stability, low specific gravity, and Low Warpage. It is an excellent candidate for printer chassis applications where high modulus and tight tolerance molding are required.

UL Yellow Card Link E45587-237063
Processing/Physical Characteristics값단위시험규격
ASTM 데이터
용융 흐름성, MFI 11 g/10min ASTM D 1238
온도 300 °C -
하중 2.16 kg -
기계적 특성값단위시험규격
ISO 데이터
인장탄성률 10600 MPa ISO 527
항복강도 106 MPa ISO 527
파단시 신율 1.3 % ISO 527
굴곡 계수 9130 MPa ISO 178
챠피 충격 강도, +23°C 20 kJ/m² ISO 179/1eU
Izod impact strength, +23°C, 4mm 14 kJ/m² ISO 180/1U
아이조드 노치 충격 강도, +23°C, 4mm 5 kJ/m² ISO 180/1A
ASTM 데이터
인장탄성률 11370 MPa ASTM D 638
항복강도 123 MPa ASTM D 638
파단시 신율 1.5 % ASTM D 638
아이조드 충격은 노치, 1/8 in 68 J/m ASTM D 256
Izod충격강도, 1/8 in 331 J/m ASTM D 256
열적 특성값단위시험규격
ISO 데이터
하중하에서의 변형온도, 1.80 MPa 129 °C ISO 75-1/-2
1.5mm 평균두께에서의 난연성 V-1 class IEC 60695-11-10
테스트 두께 1.5 mm -
두께 H인 제품의 난연성 V-0 class IEC 60695-11-10
테스트 두께 3.0 mm -
두께가 h인 제품의 난연성 등급 5V 5VB class IEC 60695-11-20
테스트 두께 2.3 mm -
ASTM 데이터
비카트 연화 온도 140 °C ASTM D 1525
기타 특성값단위시험규격
밀도 1380 kg/m³ ASTM D 792
Processing Recommendation Injection Molding값단위시험규격
Pre-drying - Temperature 105 - 110 °C -
Pre-drying - Time 3 - 4 h -
Processing humidity ≤0.02 % -
용융수지온도 295 - 315 °C -
성형온도 75 - 105 °C -
Zone 1 260 - 305 °C -
Zone 2 270 - 310 °C -
Zone 3 280 - 315 °C -
Screw speed 20 - 100 rpm -
Back pressure 0.3 - 0.7 MPa -
특징
생산 공정
사출 성형
부가물
난연제
특별 특성
난연성
지역별 검색
쩐횈쩍횄쩐횈 횇횂횈챵쩐챌 횁철쩔짧
Disclaimer
Copyright Altair Engineering GmbH. Altair Engineering GmbH assumes no liability for the system to be free of errors. The user takes sole responsibility for the use of this data under the exclusion of every liability from Altair Engineering GmbH; this is especially valid for claims of compensation resulting from consequential damages. Altair explicitly points out that any decision about the application of materials must be double checked with the producer of this material. This includes all contents of this system. Copyright laws are applicable for the content of this system.
Created: Source: www.materialdatacenter.com