Material Data Center is a leading international information system for the plastics industry. Material Data Center offers a comprehensive plastics database, calculation tools, CAE interfaces, a literature database and an application database. For more information about Material Data Center visit www.materialdatacenter.com.

This is the free Material Data Center Datasheet of LEXAN™ Copolymer 143X - Asia - PC - Saudi Basic Industries Corporation (SABIC)

Material Data Center offers the following functions for LEXAN™ Copolymer 143X - Asia:
unit conversion, PDF datasheet print, comparison with other plastics, snap fit calculation, beam deflection calculation, CAE Interfaces

Check here, which other Lexan datasheets, application examples or technical articles are available in Material Data Center

Use the following short links to get directly to the properties of interest in this datasheet:
Processing/Physical Characteristics - 기계적 특성 - 열적 특성 - 기타 특성 - Processing Recommendation Injection Molding
Any use of this information falls under the rules of our disclaimer.
제품 설명서
Improved flow PC with excellent processability and mold release.
Processing/Physical Characteristics값단위시험규격
ASTM 데이터
용융 흐름성, MFI 12 g/10min ASTM D 1238
온도 300 °C -
하중 1.2 kg -
기계적 특성값단위시험규격
ISO 데이터
인장탄성률 2450 MPa ISO 527
항복강도 60 MPa ISO 527
항복변형률 6 % ISO 527
파단시 강도 59 MPa ISO 527
파단시 신율 50 % ISO 527
굴곡 계수 2310 MPa ISO 178
챠피 충격 강도, +23°C, 3mm N kJ/m² ISO 179/1eU
챠피 충격 강도, -30°C, 3mm N kJ/m² ISO 179/1eU
챠피 노치드 충격 강도, +23°C, 3mm 65 kJ/m² ISO 179/1eA
챠피 노치드 충격 강도, -30°C, 3mm 12 kJ/m² ISO 179/1eA
Izod충격강도, +23°C N kJ/m² ISO 180/1U
아이조드 노치 충격 강도, +23°C, 3mm 65 kJ/m² ISO 180/1A
아이조드 노치 충격 강도, -30°C, 3mm 11 kJ/m² ISO 180/1A
ASTM 데이터
인장탄성률 2320 MPa ASTM D 638
항복강도 60 MPa ASTM D 638
파단시 강도 60 MPa ASTM D 638
항복변형률 6 % ASTM D 638
파단시 신율 117 % ASTM D 638
굴곡 계수 2360 MPa ASTM D 790
아이조드 충격은 노치, 1/8 in 828 J/m ASTM D 256
아이조드 충격은 노치, Low-Temperature 242 J/m ASTM D 256
온도 -30 °C -
열적 특성값단위시험규격
ISO 데이터
하중하에서의 변형온도, 1.80 MPa 122 °C ISO 75-1/-2
비카트 연화 온도, B 141 °C ISO 306
비카트 연화 온도, 120°C/h 50N 143 °C ISO 306
ASTM 데이터
DTUL @ 264 psi 128 °C ASTM D 648
비카트 연화 온도 141 °C ASTM D 1525
기타 특성값단위시험규격
물에서의 흡수성 0.35 % ISO 62와 유사
조건에서의 흡습성 0.15 % ISO 62와 유사
밀도 1200 kg/m³ ISO 1183
밀도 1200 kg/m³ ASTM D 792
Processing Recommendation Injection Molding값단위시험규격
Pre-drying - Temperature 120 °C -
Pre-drying - Time 3 - 4 h -
Processing humidity ≤0.02 % -
용융수지온도 295 - 315 °C -
성형온도 70 - 95 °C -
Zone 1 270 - 295 °C -
Zone 2 280 - 305 °C -
Zone 3 295 - 315 °C -
Screw speed 40 - 70 rpm -
Back pressure 0.3 - 0.7 MPa -
특징
생산 공정
사출 성형
지역별 검색
쩐횈쩍횄쩐횈 횇횂횈챵쩐챌 횁철쩔짧
Disclaimer
Copyright Altair Engineering GmbH. Altair Engineering GmbH assumes no liability for the system to be free of errors. The user takes sole responsibility for the use of this data under the exclusion of every liability from Altair Engineering GmbH; this is especially valid for claims of compensation resulting from consequential damages. Altair explicitly points out that any decision about the application of materials must be double checked with the producer of this material. This includes all contents of this system. Copyright laws are applicable for the content of this system.
Created: Source: www.materialdatacenter.com