Material Data Center is a leading international information system for the plastics industry. Material Data Center offers a comprehensive plastics database, calculation tools, CAE interfaces, a literature database and an application database. For more information about Material Data Center visit www.materialdatacenter.com.

This is the free Material Data Center Datasheet of Bakelite® PF 7582 - PF-(CF+X) - Bakelite Synthetics

Material Data Center offers the following functions for Bakelite® PF 7582:
unit conversion, PDF datasheet print, comparison with other plastics

Check here, which other Bakelite datasheets, application examples or technical articles are available in Material Data Center

Use the following short links to get directly to the properties of interest in this datasheet:
Any use of this information falls under the rules of our disclaimer.
제품 설명서

Product description:

Phenolic moulding compound, inorganically/organically filled, modified with graphite, good heat conductivity, good sliding properties, high dimension stability.

Application areas:

Modified with graphite, good heat conductivity, good sliding properties, high dimension stability, gas meter valves and grids.

Property Name Value Unit Standard No.
Apparent density (moulding compound) 0.78 g/cm³ ISO 60
Moulding shrinkage (compression moulding, longitudinal)  0.25 % ISO 2577
Post shrinkage (compression moulding, 168h/110°C) 0.15 % ISO 2577
Flexural strength (2mm/min) 80 MPa ISO 178
Flexural modulus 13000 MPa ISO 178
Water absorption (24h/23°C) 8 mg similar to ISO 62

Preparation of Test Specimens of Thermosetting Moulding Compound

  • Compression to ISO 295
  • Injection to ISO 10724


Storage capability
2 years (relative humidity of 50-60% and maximum storage temperature of approximately 20°C)

기계적 특성단위시험규격
ISO 데이터
챠피 충격 강도 , +23°C 3.5 kJ/m² ISO 179/1eU
챠피 노치드 충격 강도, +23°C 1.2 kJ/m² ISO 179/1eA
열적 특성단위시험규격
ISO 데이터
하중하에서의 변형온도, 8.00 MPa 180 °C ISO 75-1/-2
기타 특성단위시험규격
밀도 1600 kg/m³ ISO 1183
테스트 견본 생산단위시험규격
ISO 데이터
사출성형: 사출온도 115 °C ISO 10724
사출성형: 사출속도 170 mm/s ISO 10724
사출성형: 보압 100 MPa ISO 10724
사출성형: 경화시간 25 min ISO 10724
압축성형: 성형온도 160 °C ISO 295
압축성형: 경화시간 1 min ISO 295
기타 정보
사E성
VERARBEITUNG 
Temperature of material: 80 - 100 °C
Mould temperature: 160 - 190 °C
Curing time: 10-20 sec
 
Further Information:
Barrel temperature
  - Feed zone: 60-75 °C
  - Nozzle zone: 80-100 °C
Cavity moulding pressure: >15 MPa
Back pressure: 0.5-2 MPa
Holding pressure: 60% of injection pressure
압E성
PROCESSING
Mould temperature:160-190°C
Curing time:20-40sec
Cavity moulding pressure: >15MPa
Disclaimer
Copyright Altair Engineering GmbH. Altair Engineering GmbH assumes no liability for the system to be free of errors. The user takes sole responsibility for the use of this data under the exclusion of every liability from Altair Engineering GmbH; this is especially valid for claims of compensation resulting from consequential damages. Altair explicitly points out that any decision about the application of materials must be double checked with the producer of this material. This includes all contents of this system. Copyright laws are applicable for the content of this system.
Created: Source: www.materialdatacenter.com