Material Data Center is a leading international information system for the plastics industry. Material Data Center offers a comprehensive plastics database, calculation tools, CAE interfaces, a literature database and an application database. For more information about Material Data Center visit www.materialdatacenter.com.

This is the free Material Data Center Datasheet of SABIC® PPcompound 8620 - PP - Saudi Basic Industries Corporation (SABIC)

Material Data Center offers the following functions for SABIC® PPcompound 8620:
unit conversion, PDF datasheet print, comparison with other plastics, snap fit calculation, beam deflection calculation, CAE Interfaces

Check here, which other Sabic datasheets, application examples or technical articles are available in Material Data Center

Use the following short links to get directly to the properties of interest in this datasheet:
Processing/Physical Characteristics - 機械的特性 - 熱的特性 - その他の特性. - Processing Recommendation Injection Molding
Any use of this information falls under the rules of our disclaimer.
商品の説明文
SABIC® PPcompound 8620 is a mineral filled, impact modified polypropylene TPO. This material combines scratch resistance and good flow with exterior automotive weathering stability. It was originally designed for painted or unpainted automotive bumper fascia applications where a combination of high stiffness and cold temperature ductility is required. IMDS ID: 209747700
Processing/Physical Characteristics値単位テスト基準
ISO データ
メルトフローレート, MFI 23 g/10min ISO 1133
温度 230 °C -
荷重 2.16 kg -
機械的特性値単位テスト基準
ISO データ
引張弾性率 1680 MPa ISO 527
降伏応力 17 MPa ISO 527
降伏ひずみ 4.4 % ISO 527
破壊応力 11 MPa ISO 527
破壊ひずみ 39 % ISO 527
曲げ弾性率, 23°C 1740 MPa ISO 178
ノッチ付きシャルピー衝撃強さ, +23°C 58 kJ/m² ISO 179/1eA
ノッチ付きシャルピー衝撃強さ, -30ﾟC 7 kJ/m² ISO 179/1eA
ノッチ付きIzod衝撃強さ 6 kJ/m² ISO 180/1A
ASTM数据
引張弾性率 1900 MPa ASTM D 638
降伏応力 17 MPa ASTM D 638
破壊応力 12 MPa ASTM D 638
降伏点伸び 5 % ASTM D 638
破断伸び 101 % ASTM D 638
曲げ弾性率 1380 MPa ASTM D 790
ショア硬さD 54 - ASTM D 2240
熱的特性値単位テスト基準
ISO データ
荷重たわみ温度, 1.80 MPa 56 °C ISO 75-1/-2
荷重たわみ温度, 0.45 MPa 100 °C ISO 75-1/-2
ビカット軟化温度, A 123 °C ISO 306
ASTM数据
DTUL @ 66 psi 98 °C ASTM D 648
DTUL @ 264 psi 52 °C ASTM D 648
その他の特性.値単位テスト基準
密度. 1030 kg/m³ ISO 1183
密度 1030 kg/m³ ASTM D 792
Processing Recommendation Injection Molding値単位テスト基準
Pre-drying - Temperature 80 - 100 °C -
Pre-drying - Time 2 - 4 h -
樹脂温度 210 - 270 °C -
金型温度 15 - 60 °C -
Zone 1 190 - 230 °C -
Zone 2 200 - 250 °C -
Zone 3 210 - 270 °C -
Nozzle temperature 210 - 270 °C -
Back pressure 1 - 1.5 MPa -
特殊な特性
特殊な特性.
高耐衝撃及び耐衝撃改良.
Disclaimer
Copyright Altair Engineering GmbH. Altair Engineering GmbH assumes no liability for the system to be free of errors. The user takes sole responsibility for the use of this data under the exclusion of every liability from Altair Engineering GmbH; this is especially valid for claims of compensation resulting from consequential damages. Altair explicitly points out that any decision about the application of materials must be double checked with the producer of this material. This includes all contents of this system. Copyright laws are applicable for the content of this system.
Created: Source: www.materialdatacenter.com