Material Data Center is a leading international information system for the plastics industry. Material Data Center offers a comprehensive plastics database, calculation tools, CAE interfaces, a literature database and an application database. For more information about Material Data Center visit www.materialdatacenter.com.

This is the free Material Data Center Datasheet of Texin® RxT65D - TPU - Covestro Deutschland AG

Material Data Center offers the following functions for Texin® RxT65D:
unit conversion, PDF datasheet print, comparison with other plastics

Check here, which other Texin datasheets, application examples or technical articles are available in Material Data Center

Use the following short links to get directly to the properties of interest in this datasheet:
Processing/Physical Characteristics - 機械的特性 - 熱的特性 - その他の特性. - Processing Recommendation Injection Molding - Processing Recommendation Extrusion
Any use of this information falls under the rules of our disclaimer.
Processing/Physical Characteristics値単位テスト基準
ISO データ
メルトフローレート, MFI 4 g/10min ISO 1133
温度 220 °C -
荷重 2.16 kg -
成形収縮率, 平行 0.8 % ISO 294-4, 2577
成形収縮率, 直角 0.8 % ISO 294-4, 2577
機械的特性値単位テスト基準
ISO データ
曲げ弾性率, 23°C 421 MPa ISO 178
伸び率100%時の応力 24.8 MPa ISO 527
伸び率300%時の応力 42.1 MPa ISO 527
引張強度 51.7 MPa ISO 37
破壊ひずみ 370 % ISO 37
引裂強さ 210 kN/m ISO 34-1
ショア硬さD 65 - ISO 7619-1
熱的特性値単位テスト基準
ISO データ
ビカット軟化温度, A 138 °C ISO 306
その他の特性.値単位テスト基準
密度. 1170 kg/m³ ISO 1183
Processing Recommendation Injection Molding値単位テスト基準
Pre-drying - Temperature 93 - 104 °C -
Pre-drying - Time ≥2 h -
Processing humidity ≤0.03 % -
樹脂温度 204 - 216 °C -
金型温度 16 - 38 °C -
Zone 1 199 - 210 °C -
Zone 2 202 - 213 °C -
Zone 3 202 - 213 °C -
Nozzle temperature 204 - 216 °C -
Screw speed 40 - 80 rpm -
Injection pressure 41.4 - 103 MPa -
Back pressure ≤5.5 MPa -
後硬化時間 24.8 - 82.7 MPa -
Processing Recommendation Extrusion値単位テスト基準
Pre-drying - Temperature 93 - 104 °C -
Pre-drying - Time ≥2 h -
Processing humidity ≤0.03 % -
樹脂温度 204 - 216 °C -
Feed temperature 188 - 199 °C -
Zone 1 199 - 210 °C -
Zone 2 199 - 210 °C -
Nozzle temperature 199 - 216 °C -
特殊な特性
成形加工法.
射出成形., フィルム押出成形., Pipe/Tube Extrusion, 異形押出成形., その他の押出成形., ブロー成形.
納入形状.
ナチュラルカラー
特殊な特性.
高耐衝撃及び耐衝撃改良., 熱安定化., 滅菌可能, エチレンオキシド滅菌(EtO), Gamma irradiation sterilization
耐薬品性
Hydrolytically Stable, Radiation Resistance
Certifications
Medical Grade, Biocompatibility ISO 10993
アプリケーション
医療の
領域別の利用可能性
北アメリカ., 南・中央アメリカ.
Disclaimer
Copyright Altair Engineering GmbH. Altair Engineering GmbH assumes no liability for the system to be free of errors. The user takes sole responsibility for the use of this data under the exclusion of every liability from Altair Engineering GmbH; this is especially valid for claims of compensation resulting from consequential damages. Altair explicitly points out that any decision about the application of materials must be double checked with the producer of this material. This includes all contents of this system. Copyright laws are applicable for the content of this system.
Created: Source: www.materialdatacenter.com


Material Data Center is provided by M-Base Engineering + Software GmbH. M-Base Engineering + Software GmbH assumes no liability for the system to be free of errors. Any decision about the application of materials must be double checked with the producer of this material.

Additional information about this material, like producer contact address, etc. can be found at www.materialdatacenter.com. For access to this extra information a registration is requested. Free online registration is available.