Material Data Center is a leading international information system for the plastics industry. Material Data Center offers a comprehensive plastics database, calculation tools, CAE interfaces, a literature database and an application database. For more information about Material Data Center visit www.materialdatacenter.com.

This is the free Material Data Center Datasheet of RAVAMID® R200 T80 - PA6 - Ravago Group

Material Data Center offers the following functions for RAVAMID® R200 T80:
unit conversion, PDF datasheet print, comparison with other plastics

Check here, which other Ravamid datasheets, application examples or technical articles are available in Material Data Center

Use the following short links to get directly to the properties of interest in this datasheet:
Any use of this information falls under the rules of our disclaimer.
Processing/Physical Characteristics単位テスト基準
ASTM数据
成形収縮率., 平行 0.011 mm/mm ASTM D 955
機械的特性単位テスト基準
ISO データ
降伏応力 45 MPa ISO 527
破壊応力 45 MPa ISO 527
破壊ひずみ 80 % ISO 527
曲げ弾性率, 23°C 1800 MPa ISO 178
ノッチ付きIzod衝撃強さ, +23°C 9 kJ/m² ISO 180/1A
ノッチ付きIzod衝撃強さ 5 kJ/m² ISO 180/1A
温度 -30 °C -
熱的特性単位テスト基準
ISO データ
溶融温度, 10゚C/min 220 °C ISO 11357-1/-3
荷重たわみ温度, 1.80 MPa 50 °C ISO 75-1/-2
1.5mm厚さでの燃焼性 HB class IEC 60695-11-10
試験片の厚さ 1.6 mm -
厚さhでの燃焼性 HB class IEC 60695-11-10
試験片の厚さ 3.2 mm -
グローワイヤ燃焼性指数 (GWFI) 650 °C IEC 60695-2-12
GWFI - 試験片の厚さ 2 mm -
電気的特性.単位テスト基準
ISO データ
耐電圧 18 kV/mm IEC 60243-1
耐トラッキング性 600 - IEC 60112
その他の特性.単位テスト基準
密度. 1080 kg/m³ ISO 1183
吸水率, 24hr 2.5 % ASTM D 570
Processing Recommendation Injection Molding単位テスト基準
Pre-drying - Temperature 75 °C -
Pre-drying - Time 3 - 4 h -
Processing humidity ≤0.12 % -
樹脂温度 240 - 270 °C -
金型温度 70 - 90 °C -
Zone 1 220 - 230 °C -
Zone 2 230 - 245 °C -
Zone 3 250 - 260 °C -
Nozzle temperature 250 - 260 °C -
Screw speed 50 - 80 rpm -
Back pressure 0.4 - 0.8 MPa -
後硬化時間 6 - 8 MPa -
特殊な特性
特殊な特性.
高耐衝撃及び耐衝撃改良., 紫外線安定化., 熱安定化.
領域別の利用可能性
ヨーロッパ.
Disclaimer
Copyright Altair Engineering GmbH. Altair Engineering GmbH assumes no liability for the system to be free of errors. The user takes sole responsibility for the use of this data under the exclusion of every liability from Altair Engineering GmbH; this is especially valid for claims of compensation resulting from consequential damages. Altair explicitly points out that any decision about the application of materials must be double checked with the producer of this material. This includes all contents of this system. Copyright laws are applicable for the content of this system.
Created: Source: www.materialdatacenter.com