Material Data Center is a leading international information system for the plastics industry. Material Data Center offers a comprehensive plastics database, calculation tools, CAE interfaces, a literature database and an application database. For more information about Material Data Center visit www.materialdatacenter.com.

This is the free Material Data Center Datasheet of LEXAN™ Copolymer EXL1132 - Americas - PC - Saudi Basic Industries Corporation (SABIC)

Material Data Center offers the following functions for LEXAN™ Copolymer EXL1132 - Americas:
unit conversion, PDF datasheet print, comparison with other plastics, snap fit calculation, beam deflection calculation, CAE Interfaces

Check here, which other Lexan datasheets, application examples or technical articles are available in Material Data Center

Use the following short links to get directly to the properties of interest in this datasheet:
Processing/Physical Characteristics - 機械的特性 - 熱的特性 - その他の特性. - Processing Recommendation Injection Molding
Any use of this information falls under the rules of our disclaimer.
商品の説明文
LEXAN EXL1132 polycarbonate (PC) siloxane copolymer resin is a high flow, UV stabilized injection molding grade. This resin offers good low temperature (-20 C) ductility in combination with high flow characteristics and excellent processability with opportunities for shorter IM cycle times compared to standard PC. LEXAN EXL1132 resin is a general purpose product available in a wide range of opaque colors and may be an excellent candidate for a broad range of applications.

UL Yellow Card Link E121562-575794
Processing/Physical Characteristics値単位テスト基準
ISO データ
メルトボリュームレイト, MVR 16 cm³/10min ISO 1133
温度 300 °C -
荷重 1.2 kg -
ASTM数据
メルトフローレイト, MFI 17 g/10min ASTM D 1238
温度 300 °C -
荷重 1.2 kg -
機械的特性値単位テスト基準
ISO データ
引張弾性率 2150 MPa ISO 527
降伏応力 57 MPa ISO 527
降伏ひずみ 5 % ISO 527
破壊応力 55 MPa ISO 527
破壊ひずみ 50 % ISO 527
曲げ弾性率 2240 MPa ISO 178
シャルピー衝撃強さ, +23°C, 3mm N kJ/m² ISO 179/1eU
シャルピー衝撃強さ, -30°C, 3mm N kJ/m² ISO 179/1eU
ノッチ付きシャルピー衝撃強さ, +23°C, 3mm 60 kJ/m² ISO 179/1eA
ノッチ付きシャルピー衝撃強さ, -30°C, 3mm 25 kJ/m² ISO 179/1eA
アイゾット衝撃試験, +23°C N kJ/m² ISO 180/1U
ノッチ付きアイゾット衝撃強さ, +23°C, 3mm 55 kJ/m² ISO 180/1A
ノッチ付きアイゾット衝撃強, -30°C, 3mm 20 kJ/m² ISO 180/1A
Ball indentation hardness 95 MPa ISO 2039-1
ASTM数据
引張弾性率 2280 MPa ASTM D 638
降伏応力 58 MPa ASTM D 638
破壊応力 58 MPa ASTM D 638
降伏点伸び 5.8 % ASTM D 638
破断伸び 109 % ASTM D 638
曲げ弾性率 2320 MPa ASTM D 790
ノッチ付きIzod衝撃強さ, 1/8 in 747 J/m ASTM D 256
ノッチ付きIzod衝撃強さ, Low-Temperature 667 J/m ASTM D 256
温度 -30 °C -
熱的特性値単位テスト基準
ISO データ
ビカット軟化温度, B 144 °C ISO 306
ビカット軟化温度, 120°C/h 50N 145 °C ISO 306
厚さhでの燃焼性 HB class IEC 60695-11-10
試験片の厚さ 0.8 mm -
グローワイヤ燃焼性指数 (GWFI) 960 °C IEC 60695-2-12
グローワイヤ燃焼性指数 (GWFI) 960 °C IEC 60695-2-12
グローワイヤ着火温度 (GWIT) 875 °C IEC 60695-2-13
GWIT - 試験片の厚さ 1 mm -
グローワイヤ着火温度 (GWIT) 875 °C IEC 60695-2-13
GWIT - 試験片の厚さ 3 mm -
ASTM数据
DTUL @ 66 psi 136 °C ASTM D 648
DTUL @ 264 psi 123 °C ASTM D 648
ビカット軟化温度 144 °C ASTM D 1525
その他の特性.値単位テスト基準
吸水率. 0.35 % Sim. to ISO 62
吸湿率 0.15 % Sim. to ISO 62
密度. 1190 kg/m³ ISO 1183
密度 1180 kg/m³ ASTM D 792
Processing Recommendation Injection Molding値単位テスト基準
Pre-drying - Temperature 120 °C -
Pre-drying - Time 3 - 4 h -
Processing humidity ≤0.02 % -
樹脂温度 295 - 315 °C -
金型温度 70 - 95 °C -
Zone 1 270 - 295 °C -
Zone 2 280 - 305 °C -
Zone 3 295 - 315 °C -
Screw speed 40 - 70 rpm -
Back pressure 0.3 - 0.7 MPa -
特殊な特性
成形加工法.
射出成形.
領域別の利用可能性
北アメリカ.
Disclaimer
Copyright Altair Engineering GmbH. Altair Engineering GmbH assumes no liability for the system to be free of errors. The user takes sole responsibility for the use of this data under the exclusion of every liability from Altair Engineering GmbH; this is especially valid for claims of compensation resulting from consequential damages. Altair explicitly points out that any decision about the application of materials must be double checked with the producer of this material. This includes all contents of this system. Copyright laws are applicable for the content of this system.
Created: Source: www.materialdatacenter.com