Material Data Center is a leading international information system for the plastics industry. Material Data Center offers a comprehensive plastics database, calculation tools, CAE interfaces, a literature database and an application database. For more information about Material Data Center visit www.materialdatacenter.com.

This is the free Material Data Center Datasheet of LEXAN™ Copolymer FST9405T - Americas - PC - Saudi Basic Industries Corporation (SABIC)

Material Data Center offers the following functions for LEXAN™ Copolymer FST9405T - Americas:
unit conversion, PDF datasheet print, comparison with other plastics, snap fit calculation, beam deflection calculation, CAE Interfaces

Check here, which other Lexan datasheets, application examples or technical articles are available in Material Data Center

Use the following short links to get directly to the properties of interest in this datasheet:
Caractéristiques des transformations/physiques - Propriétés mécaniques - Propriétés thermiques - Propriétés diverses - Recommandations pour la transformation Moulage par injection
Any use of this information falls under the rules of our disclaimer.
Informations produit
LEXAN FST9405T resin is a high flow PC Copolymer Resin, suitable for injection molding. This halogen-free flame retardant resin is OSU55/55 and FAR25.853 compliant and an ideal candidate for aircraft interior applications. Available in transparent and/or translucent colors only
Caractéristiques des transformations/physiquesValeurUnitéNorme du test
ISO Data
Indice de fluidité à chaud en volume, MVR 10 cm³/10min ISO 1133
Température 300 °C -
Charge 1.2 kg -
ASTM Data
Indice de fluidité, MFI 9 g/10min ASTM D 1238
Température 300 °C -
Charge 1.2 kg -
Propriétés mécaniquesValeurUnitéNorme du test
ISO Data
Module en traction 2600 MPa ISO 527
Contrainte d'écoulement 77 MPa ISO 527
Déformation au seuil d'écoulement 6 % ISO 527
Contrainte à la rupture 70 MPa ISO 527
Déformation à la rupture 50 % ISO 527
Module de flexion 2500 MPa ISO 178
Résistance au choc Charpy, +23°C N kJ/m² ISO 179/1eU
Résistance au choc Charpy, -30°C N kJ/m² ISO 179/1eU
Résistance au choc Charpy, +23°C, 3mm N kJ/m² ISO 179/1eU
Résistance au choc Charpy, -30°C, 3mm N kJ/m² ISO 179/1eU
Résistance au choc Charpy (entaillé), +23°C N kJ/m² ISO 179/1eA
Résistance au choc Charpy (entaillé), -30°C N kJ/m² ISO 179/1eA
Résistance au choc Charpy (entaillé), +23°C, 3mm N kJ/m² ISO 179/1eA
Résistance au choc Charpy (entaillé), -30°C, 3mm N kJ/m² ISO 179/1eA
Résistance au choc Izod, +23°C N kJ/m² ISO 180/1U
Résistance au choc Izod (entaillé), +23°C, 4mm 11 kJ/m² ISO 180/1A
Résistance au choc Izod (entaillé), -30°C, 4mm 9 kJ/m² ISO 180/1A
Résistance au choc Izod (entaillé), +23°C, 3mm 12 kJ/m² ISO 180/1A
ASTM Data
Module en traction 2600 MPa ASTM D 638
Module de traction d’élasticité 77 MPa ASTM D 638
Résistance de traction à la rupture 70 MPa ASTM D 638
Allongement d’élasticité 6 % ASTM D 638
Allongement à la rupture 75 % ASTM D 638
Module de flexion 2700 MPa ASTM D 790
Izod choc avec entaille, 1/8 in 130 J/m ASTM D 256
Izod choc avec entaille, bas température 85 J/m ASTM D 256
Température -30 °C -
Propriétés thermiquesValeurUnitéNorme du test
ISO Data
Température de fléchissement s/chrg, 1.80 MPa 94 °C ISO 75-1/-2
Température de fléchissement s/chrg, 0.45 MPa 104 °C ISO 75-1/-2
Température de ramolliss. Vicat, 120°C/h 50N 113 °C ISO 306
ASTM Data
DTUL à 66 psi 105 °C ASTM D 648
DTUL à 264 psi 95 °C ASTM D 648
Vicat température 114 °C ASTM D 1525
Propriétés diversesValeurUnitéNorme du test
Masse volumique 1330 kg/m³ ISO 1183
Densité 1330 kg/m³ ASTM D 792
Recommandations pour la transformation Moulage par injectionValeurUnitéNorme du test
Pré-séchage - température 95 - 100 °C -
Pré-séchage - temps 6 - 8 h -
Température de la matière fondue 250 - 280 °C -
Température du moule 50 - 80 °C -
Zone 1 230 - 250 °C -
Zone 2 240 - 270 °C -
Zone 3 250 - 280 °C -
Vitesse de rotation de vis 40 - 70 rpm -
Contre-pression 0.3 - 0.7 MPa -
Caractéristiques
Transformation
Moulage par injection
Additifs
Agent ignifugeant
Propriétés spéciales
Ignifugé, Transparent
Applications
Automobile
Disponibilité régionale
Amérique du nord
Conditions générales
Copyright Altair Engineering GmbH. Altair Engineering GmbH assumes no liability for the system to be free of errors. The user takes sole responsibility for the use of this data under the exclusion of every liability from Altair Engineering GmbH; this is especially valid for claims of compensation resulting from consequential damages. Altair explicitly points out that any decision about the application of materials must be double checked with the producer of this material. This includes all contents of this system. Copyright laws are applicable for the content of this system.
Created: Source: www.materialdatacenter.com