Material Data Center is a leading international information system for the plastics industry. Material Data Center offers a comprehensive plastics database, calculation tools, CAE interfaces, a literature database and an application database. For more information about Material Data Center visit www.materialdatacenter.com.

This is the free Material Data Center Datasheet of NORYL™ Resin EM6100 - Americas - (PPE+PS) - Saudi Basic Industries Corporation (SABIC)

Material Data Center offers the following functions for NORYL™ Resin EM6100 - Americas:
unit conversion, PDF datasheet print, comparison with other plastics, snap fit calculation, beam deflection calculation, CAE Interfaces

Check here, which other Noryl datasheets, application examples or technical articles are available in Material Data Center

Use the following short links to get directly to the properties of interest in this datasheet:
Processing/Physical Characteristics - Mechanical properties - Thermal properties - Other properties - Processing Recommendation Injection Molding
Any use of this information falls under the rules of our disclaimer.
Product Texts
NORYL™ EM6100 is a non-reinforced blend of polyphenylene ether (PPE) + high impact polystyrene (HIPS). This grade exhibits a balance of flow/heat/impact, dimensional stability, along with paint adhesion. NORYL EM6100 resin is suitable for the automotive interior market in applications such as HVAC housings and radio components. MS-DB424, WSBM4D844-A9, GMP.PPE.007.

UL Yellow Card Link E121562-221232
Processing/Physical CharacteristicsValueUnitTest Standard
ISO Data
Melt volume-flow rate, MVR 15 cm³/10min ISO 1133
Temperature 280 °C -
Load 5 kg -
ASTM Data
Melt Flow Index, MFI 15 g/10min ASTM D 1238
Temperature 280 °C -
Load 5 kg -
Mechanical propertiesValueUnitTest Standard
ISO Data
Tensile Modulus 2050 MPa ISO 527
Yield stress 42 MPa ISO 527
Yield strain 2.8 % ISO 527
Stress at break 40 MPa ISO 527
Strain at break 50 % ISO 527
Flexural modulus 2100 MPa ISO 178
Flexural strength 65 MPa ISO 178
Izod notched impact strength, +23°C, 4mm 33 kJ/m² ISO 180/1A
Izod notched impact strength, -30°C, 4mm 15 kJ/m² ISO 180/1A
ASTM Data
Tensile Modulus 1900 MPa ASTM D 638
Tensile Strength at Yield 43 MPa ASTM D 638
Tensile Strength at Break 40 MPa ASTM D 638
Elongation at Yield 3 % ASTM D 638
Elongation at Break 65 % ASTM D 638
Flexural Modulus 2100 MPa ASTM D 790
Izod Impact notched, 1/8 in 453 J/m ASTM D 256
Izod Impact notched, Low-Temperature 250 J/m ASTM D 256
Temperature -30 °C -
Thermal propertiesValueUnitTest Standard
ISO Data
Temp. of deflection under load, 1.80 MPa 110 °C ISO 75-1/-2
Temp. of deflection under load, 0.45 MPa 126 °C ISO 75-1/-2
Vicat softening temperature, B 119 °C ISO 306
Vicat softening temperature, 120°C/h 50N 123 °C ISO 306
Burning behav. at 1.5 mm nom. thickn. HB class IEC 60695-11-10
Thickness tested 1.5 mm -
ASTM Data
DTUL @ 66 psi 124 °C ASTM D 648
DTUL @ 264 psi 106 °C ASTM D 648
Other propertiesValueUnitTest Standard
Density 1050 kg/m³ ASTM D 792
Processing Recommendation Injection MoldingValueUnitTest Standard
Pre-drying - Temperature 95 - 105 °C -
Pre-drying - Time 3 - 4 h -
Processing humidity ≤0.02 % -
Melt temperature 265 - 295 °C -
Mold temperature 65 - 95 °C -
Zone 1 230 - 280 °C -
Zone 2 245 - 290 °C -
Zone 3 255 - 295 °C -
Screw speed 20 - 100 rpm -
Back pressure 0.3 - 0.7 MPa -
Characteristics
Processing
Injection Molding
Applications
Automotive
Regional Availability
North America
Disclaimer
Copyright Altair Engineering GmbH. Altair Engineering GmbH assumes no liability for the system to be free of errors. The user takes sole responsibility for the use of this data under the exclusion of every liability from Altair Engineering GmbH; this is especially valid for claims of compensation resulting from consequential damages. Altair explicitly points out that any decision about the application of materials must be double checked with the producer of this material. This includes all contents of this system. Copyright laws are applicable for the content of this system.
Created: Source: www.materialdatacenter.com