Material Data Center is a leading international information system for the plastics industry. Material Data Center offers a comprehensive plastics database, calculation tools, CAE interfaces, a literature database and an application database. For more information about Material Data Center visit www.materialdatacenter.com.

This is the free Material Data Center Datasheet of NORYL™ Resin 7310 - Asia - (PPE+PS) - Saudi Basic Industries Corporation (SABIC)

Material Data Center offers the following functions for NORYL™ Resin 7310 - Asia:
unit conversion, PDF datasheet print, comparison with other plastics, snap fit calculation, beam deflection calculation, CAE Interfaces

Check here, which other Noryl datasheets, application examples or technical articles are available in Material Data Center

Use the following short links to get directly to the properties of interest in this datasheet:
Processing/Physical Characteristics - Mechanical properties - Thermal properties - Other properties - Processing Recommendation Injection Molding
Any use of this information falls under the rules of our disclaimer.
Product Texts
NORYL™ 7310 resin is a non-reinforced blend of polyphenylene ether (PPE) + high impact polystyrene (HIPS). This injection moldable grade exhibits good surface appearance, high ductility, and good impact resistance along with low moisture absorption, creep resistance, dimensional stability, and hydrolytic stability. NORYL 7310 resin is an excellent candidate for a variety of applications.

UL Yellow Card Link E45587-237006
Processing/Physical CharacteristicsValueUnitTest Standard
ISO Data
Melt volume-flow rate, MVR 12 cm³/10min ISO 1133
Temperature 280 °C -
Load 5 kg -
ASTM Data
Melt Flow Index, MFI 11 g/10min ASTM D 1238
Temperature 280 °C -
Load 5 kg -
Mechanical propertiesValueUnitTest Standard
ISO Data
Tensile Modulus 2100 MPa ISO 527
Yield stress 40 MPa ISO 527
Yield strain 70 % ISO 527
Stress at break 40 MPa ISO 527
Strain at break 50 % ISO 527
Flexural modulus 2300 MPa ISO 178
Charpy notched impact strength, +23°C 13 kJ/m² ISO 179/1eA
Izod impact strength, +23°C, 4mm 60 kJ/m² ISO 180/1U
Izod impact strength, -30°C, 4mm 55 kJ/m² ISO 180/1U
Izod notched impact strength, +23°C, 4mm 16 kJ/m² ISO 180/1A
Izod notched impact strength, -30°C, 4mm 11 kJ/m² ISO 180/1A
ASTM Data
Tensile Modulus 2400 MPa ASTM D 638
Tensile Strength at Yield 54 MPa ASTM D 638
Tensile Strength at Break 45 MPa ASTM D 638
Elongation at Yield 4 % ASTM D 638
Elongation at Break 30 % ASTM D 638
Flexural Modulus 2100 MPa ASTM D 790
Izod Impact notched, 1/8 in 150 J/m ASTM D 256
Izod Impact notched, Low-Temperature 120 J/m ASTM D 256
Temperature -30 °C -
Izod Impact unnotched, 1/8 in 800 J/m ASTM D 256
Thermal propertiesValueUnitTest Standard
ISO Data
Temp. of deflection under load, 1.80 MPa 112 °C ISO 75-1/-2
Vicat softening temperature, B 133 °C ISO 306
Vicat softening temperature, 120°C/h 50N 135 °C ISO 306
Burning behav. at 1.5 mm nom. thickn. HB class IEC 60695-11-10
Thickness tested 1.5 mm -
ASTM Data
DTUL @ 264 psi 110 °C ASTM D 648
Vicat Temperature 133 °C ASTM D 1525
Other propertiesValueUnitTest Standard
Density 1080 kg/m³ ASTM D 792
Processing Recommendation Injection MoldingValueUnitTest Standard
Pre-drying - Temperature 105 - 110 °C -
Pre-drying - Time 3 - 4 h -
Processing humidity ≤0.02 % -
Melt temperature 280 - 310 °C -
Mold temperature 75 - 105 °C -
Zone 1 250 - 300 °C -
Zone 2 260 - 305 °C -
Zone 3 270 - 310 °C -
Screw speed 20 - 100 rpm -
Back pressure 0.3 - 0.7 MPa -
Characteristics
Processing
Injection Molding
Chemical Resistance
Hydrolytically Stable
Applications
Automotive
Regional Availability
Asia Pacific
Disclaimer
Copyright Altair Engineering GmbH. Altair Engineering GmbH assumes no liability for the system to be free of errors. The user takes sole responsibility for the use of this data under the exclusion of every liability from Altair Engineering GmbH; this is especially valid for claims of compensation resulting from consequential damages. Altair explicitly points out that any decision about the application of materials must be double checked with the producer of this material. This includes all contents of this system. Copyright laws are applicable for the content of this system.
Created: Source: www.materialdatacenter.com