Material Data Center is a leading international information system for the plastics industry. Material Data Center offers a comprehensive plastics database, calculation tools, CAE interfaces, a literature database and an application database. For more information about Material Data Center visit www.materialdatacenter.com.

This is the free Material Data Center Datasheet of NORYL™ Resin NH5020 - Asia - (PPE+PS) - Saudi Basic Industries Corporation (SABIC)

Check here, which other Noryl datasheets, application examples or technical articles are available in Material Data Center

Processing/Physical Characteristics - 機械的特性 - 熱的特性 - その他の特性. - Processing Recommendation Injection Molding - 機能

Any use of this information falls under the rules of our disclaimer.

商品の説明文

NORYL™ NH5020 resin is a non-reinforced blend of polyphenylene ether (PPE) + high impact polystyrene (HIPS). This injection moldable grade contains non-brominated, non-chlorinated flame retardant and exhibits high heat resistance with thin-wall FR performance. NORYL NH5020 resin carries a UL94 flame rating of V0 at 0.75mm along with a UL746C Outdoor Suitability rating of F1. The material offers a good balance of affordable high heat, flow, hydrolytic stability, excellent creep resistance, dimensional stability and is a good candidate for photovoltaic / solar connectors, UPS Inverters / chargers, and outdoor enclosure applications.

Processing/Physical Characteristics	値	単位	テスト基準
ISO データ
メルトボリュームレイト, MVR	10	cm³/10min	ISO 1133
温度	280	°C	-
荷重	5	kg	-
溶融時の密度	1010	kg/m³	-
溶融時の熱伝導率	0.2	W/(m K)	-
溶融時の比熱	1780	J/(kg K)	-
突き出し時の時の温度	127	°C	-
ASTM数据
メルトフローレイト, MFI	9.8	g/10min	ASTM D 1238
温度	280	°C	-
荷重	5	kg	-

機械的特性	値	単位	テスト基準
ISO データ
引張弾性率	3050	MPa	ISO 527
降伏応力	80	MPa	ISO 527
降伏ひずみ	4.7	%	ISO 527
破壊応力	77	MPa	ISO 527
破壊ひずみ	5.6	%	ISO 527
曲げ弾性率	2980	MPa	ISO 178
ノッチ付きシャルピー衝撃強さ, +23°C	7	kJ/m²	ISO 179/1eA
ノッチ付きアイゾット衝撃強さ, +23°C, 4mm	8	kJ/m²	ISO 180/1A
ノッチ付きアイゾット衝撃強さ, -30°C, 4mm	6	kJ/m²	ISO 180/1A
ASTM数据
引張弾性率	2720	MPa	ASTM D 638
降伏応力	79	MPa	ASTM D 638
破壊応力	62	MPa	ASTM D 638
降伏点伸び	5	%	ASTM D 638
破断伸び	15	%	ASTM D 638
曲げ弾性率	3000	MPa	ASTM D 790
ノッチ付きIzod衝撃強さ, 1/8 in	91	J/m	ASTM D 256
ノッチ付きIzod衝撃強さ, Low-Temperature	59	J/m	ASTM D 256
温度	-30	°C	-

熱的特性	値	単位	テスト基準
ISO データ
荷重たわみ温度, 1.80 MPa	119	°C	ISO 75-1/-2
ビカット軟化温度, B	138	°C	ISO 306
ビカット軟化温度, 120°C/h 50N	139	°C	ISO 306
線膨張係数, 平行	83.8	E-6/K	ISO 11359-1/-2
線膨張係数, 直角	85.8	E-6/K	ISO 11359-1/-2
ASTM数据
DTUL @ 66 psi	122	°C	ASTM D 648
DTUL @ 264 psi	117	°C	ASTM D 648
ビカット軟化温度	137	°C	ASTM D 1525

その他の特性.	値	単位	テスト基準
吸水率.	0.25	%	Sim. to ISO 62
吸湿率	0.05	%	Sim. to ISO 62
密度.	1110	kg/m³	ISO 1183
密度	1110	kg/m³	ASTM D 792

Processing Recommendation Injection Molding	値	単位	テスト基準
Pre-drying - Temperature	105 - 110	°C	-
Pre-drying - Time	3 - 4	h	-
Processing humidity	≤0.02	%	-
樹脂温度	275 - 305	°C	-
金型温度	70 - 100	°C	-
Zone 1	245 - 295	°C	-
Zone 2	255 - 300	°C	-
Zone 3	265 - 305	°C	-
Screw speed	20 - 100	rpm	-
Back pressure	0.3 - 0.7	MPa	-

機能

特殊な特性

成形加工法.

射出成形.

添加剤.

難燃剤.

特殊な特性.

難燃.

耐薬品性

Hydrolytically Stable

領域別の利用可能性

アジア/太平洋地域.

Disclaimer

Copyright Altair Engineering GmbH. Altair Engineering GmbH assumes no liability for the system to be free of errors. The user takes sole responsibility for the use of this data under the exclusion of every liability from Altair Engineering GmbH; this is especially valid for claims of compensation resulting from consequential damages. Altair explicitly points out that any decision about the application of materials must be double checked with the producer of this material. This includes all contents of this system. Copyright laws are applicable for the content of this system.

Created: Source: www.materialdatacenter.com

Material Data Center is provided by M-Base Engineering + Software GmbH. M-Base Engineering + Software GmbH assumes no liability for the system to be free of errors. Any decision about the application of materials must be double checked with the producer of this material.

Additional information about this material, like producer contact address, etc. can be found at www.materialdatacenter.com. For access to this extra information a registration is requested. Free online registration is available.