Material Data Center is a leading international information system for the plastics industry. Material Data Center offers a comprehensive plastics database, calculation tools, CAE interfaces, a literature database and an application database. For more information about Material Data Center visit www.materialdatacenter.com.

This is the free Material Data Center Datasheet of SABIC® PPcompound G3240A - PP - Saudi Basic Industries Corporation (SABIC)

Material Data Center offers the following functions for SABIC® PPcompound G3240A:
unit conversion, PDF datasheet print, comparison with other plastics, snap fit calculation, beam deflection calculation, CAE Interfaces

Check here, which other Sabic datasheets, application examples or technical articles are available in Material Data Center

Use the following short links to get directly to the properties of interest in this datasheet:
Mechanical properties - Thermal properties - Other properties - Processing Recommendation Injection Molding
Any use of this information falls under the rules of our disclaimer.
Product Texts
SABIC® PPcompound G3240A is a 40% short glass fiber reinforced Polypropylene for under-the-hood and structural applications. The base material is a PP homopolymer and is available in standard black. The glass fibres are chemically coupled to the PP matrix SABIC® PPcompound G3240A is a designated automotive grade. IMDS ID: 139448304
Mechanical propertiesValueUnitTest Standard
ISO Data
Tensile Modulus 8900 MPa ISO 527
Stress at break 110 MPa ISO 527
Strain at break 2.9 % ISO 527
Flexural modulus, 23°C 8900 MPa ISO 178
Charpy notched impact strength, +23°C 10 kJ/m² ISO 179/1eA
Charpy notched impact strength, -30°C 13 kJ/m² ISO 179/1eA
ASTM Data
Tensile Modulus 7610 MPa ASTM D 638
Tensile Strength at Break 120 MPa ASTM D 638
Elongation at Break 2.4 % ASTM D 638
Flexural Modulus 7800 MPa ASTM D 790
Thermal propertiesValueUnitTest Standard
ISO Data
Temp. of deflection under load, 1.80 MPa 153 °C ISO 75-1/-2
Temp. of deflection under load, 0.45 MPa 161 °C ISO 75-1/-2
Vicat softening temperature, A 164 °C ISO 306
ASTM Data
DTUL @ 66 psi 161 °C ASTM D 648
DTUL @ 264 psi 153 °C ASTM D 648
Other propertiesValueUnitTest Standard
Density 1220 kg/m³ ISO 1183
Density 1220 kg/m³ ASTM D 792
Processing Recommendation Injection MoldingValueUnitTest Standard
Pre-drying - Temperature 80 - 100 °C -
Pre-drying - Time 2 - 4 h -
Melt temperature 210 - 270 °C -
Mold temperature 15 - 60 °C -
Zone 1 190 - 230 °C -
Zone 2 200 - 250 °C -
Zone 3 210 - 270 °C -
Nozzle temperature 210 - 270 °C -
Back pressure 1 - 1.5 MPa -
Characteristics
Features
Homopolymer
Disclaimer
Copyright Altair Engineering GmbH. Altair Engineering GmbH assumes no liability for the system to be free of errors. The user takes sole responsibility for the use of this data under the exclusion of every liability from Altair Engineering GmbH; this is especially valid for claims of compensation resulting from consequential damages. Altair explicitly points out that any decision about the application of materials must be double checked with the producer of this material. This includes all contents of this system. Copyright laws are applicable for the content of this system.
Created: Source: www.materialdatacenter.com


Material Data Center is provided by M-Base Engineering + Software GmbH. M-Base Engineering + Software GmbH assumes no liability for the system to be free of errors. Any decision about the application of materials must be double checked with the producer of this material.

Additional information about this material, like producer contact address, etc. can be found at www.materialdatacenter.com. For access to this extra information a registration is requested. Free online registration is available.