High-temperature polyamide with ceramic spheres, flame retardant, black.
Processing/Physical Characteristics | Value | Unit | Test Standard |
Other Standards[S] |
Molding shrinkage, parallel |
0.1 |
% |
DIN 16742 |
S: | These properties are reported by the producer according standards that are different to our defaults. |
Mechanical properties | Value | Unit | Test Standard |
ISO Data |
Tensile Modulus |
5500 |
MPa |
ISO 527 |
Tensile Strength |
55 |
MPa |
ISO 527 |
Thermal properties | Value | Unit | Test Standard |
ISO Data |
Temp. of deflection under load, 1.80 MPa |
90 |
°C |
ISO 75-1/-2 |
Burning behav. at thickness h |
V-0 |
class |
IEC 60695-11-10 |
Thickness tested |
0.4 |
mm |
- |
Electrical properties | Value | Unit | Test Standard |
Other Standards[S] |
Surface resistivity |
1E9 |
Ohm |
DIN 62631-3-2 |
S: | These properties are reported by the producer according standards that are different to our defaults. |
Other properties | Value | Unit | Test Standard |
Density |
1400 |
kg/m³ |
ISO 1183 |
Processing Recommendation Extrusion | Value | Unit | Test Standard |
Pre-drying - Temperature |
130 |
°C |
- |
Pre-drying - Time |
6 - 8 |
h |
- |
Zone 1 |
260 - 300 |
°C |
- |
Zone 2 |
260 - 300 |
°C |
- |
Zone 3 |
260 - 300 |
°C |
- |
Nozzle temperature |
250 - 290 |
°C |
- |
Characteristics
Processing
Additive Manufacturing
Delivery form
Pellets, Black
Special Characteristics
Flame retardant, Heat stabilized or stable to heat
Features
Low Warpage
Applications
Filament for 3D Printing
Regional Availability
North America, Europe, Asia Pacific, South and Central America
Disclaimer
Copyright Altair Engineering GmbH. Altair Engineering GmbH assumes no liability for the system to be free of errors. The user takes sole responsibility for the use of this data under the exclusion of every liability from Altair Engineering GmbH; this is especially valid for claims of compensation resulting from consequential damages. Altair explicitly points out that any decision about the application of materials must be double checked with the producer of this material. This includes all contents of this system. Copyright laws are applicable for the content of this system.
Created: Source: www.materialdatacenter.com