Processing/Physical Characteristics | Value | Unit | Test Standard |
ISO Data |
Melt flow index, MFI |
6 |
g/10min |
ISO 1133 |
Temperature |
200 |
°C |
- |
Load |
5 |
kg |
- |
Molding shrinkage, parallel |
0.5 |
% |
ISO 294-4, 2577 |
Mechanical properties | Value | Unit | Test Standard |
ISO Data |
Tensile Strength |
18 |
MPa |
ISO 527 |
Flexural modulus, 23°C |
1100 |
MPa |
ISO 178 |
Flexural strength |
21 |
MPa |
ISO 178 |
Charpy impact strength, +23°C |
N |
kJ/m² |
ISO 179/1eU |
Charpy notched impact strength, +23°C |
N |
kJ/m² |
ISO 179/1eA |
Type of failure |
(P) |
- |
- |
Shore D hardness |
55 |
- |
ISO 7619-1 |
Rockwell hardness |
R 10 |
- |
ISO 2039-2 |
Thermal properties | Value | Unit | Test Standard |
ISO Data |
Temp. of deflection under load, 1.80 MPa |
60 |
°C |
ISO 75-1/-2 |
Vicat softening temperature, A |
72 |
°C |
ISO 306 |
Optical properties | Value | Unit | Test Standard |
ISO Data |
Haze |
2 |
- |
ISO 14782 |
Other Standards[S] |
Light Transmittance |
89 |
% |
ISO 13468 |
S: | These properties are reported by the producer according standards that are different to our defaults. |
Other properties | Value | Unit | Test Standard |
Water absorption |
0.1 |
% |
Sim. to ISO 62 |
Density |
1010 |
kg/m³ |
ISO 1183 |
Processing Recommendation Injection Molding | Value | Unit | Test Standard |
Melt temperature |
180 - 220 |
°C |
- |
Mold temperature |
50 |
°C |
- |
Zone 1 |
180 - 200 |
°C |
- |
Nozzle temperature |
200 |
°C |
- |
Injection pressure |
67 |
MPa |
- |
Back pressure |
6 |
MPa |
- |
Processing Recommendation Extrusion | Value | Unit | Test Standard |
Mold temperature |
60 - 80 |
°C |
- |
Zone 1 |
170 |
°C |
- |
Zone 2 |
180 |
°C |
- |
Zone 3 |
185 |
°C |
- |
Zone 4 |
190 |
°C |
- |
Zone 5 |
200 |
°C |
- |
Nozzle temperature |
200 |
°C |
- |
Characteristics
Processing
Injection Molding, Other Extrusion
Special Characteristics
High impact or impact modified, Transparent
Features
High Gloss, Copolymer
Applications
Packaging
Regional Availability
North America, Europe, Asia Pacific, Near East/Africa
Disclaimer
Copyright Altair Engineering GmbH. Altair Engineering GmbH assumes no liability for the system to be free of errors. The user takes sole responsibility for the use of this data under the exclusion of every liability from Altair Engineering GmbH; this is especially valid for claims of compensation resulting from consequential damages. Altair explicitly points out that any decision about the application of materials must be double checked with the producer of this material. This includes all contents of this system. Copyright laws are applicable for the content of this system.
Created: Source: www.materialdatacenter.com