Material Data Center is a leading international information system for the plastics industry. Material Data Center offers a comprehensive plastics database, calculation tools, CAE interfaces, a literature database and an application database. For more information about Material Data Center visit www.materialdatacenter.com.

This is the free Material Data Center Datasheet of ULTEM™ Resin DT1810EVUCL - PEI - Saudi Basic Industries Corporation (SABIC)

Material Data Center offers the following functions for ULTEM™ Resin DT1810EVUCL:
unit conversion, PDF datasheet print, comparison with other plastics, snap fit calculation, beam deflection calculation, CAE Interfaces

Check here, which other Ultem datasheets, application examples or technical articles are available in Material Data Center

Use the following short links to get directly to the properties of interest in this datasheet:
加工/物理特性 - 机械性能 - 热性能 - 其它性能 - 加工推荐（注塑）
Any use of this information falls under the rules of our disclaimer.
材料文字说明
Improved ductility, transparent, enhanced flow Polyetherimide blend (Tg 200C) with internal mold release and enhanced ductility.
加工/物理特性价值单位Test Standard
ISO数据
熔体体积流动速度, MVR 56 cm³/10min ISO 1133
温度 360 °C -
载荷 5 kg -
ASTM数据
熔融指数, MFI 43 g/10min ASTM D 1238
温度 337 °C -
负载 6.6 kg -
机械性能价值单位Test Standard
ISO数据
拉伸模量 2500 MPa ISO 527
屈服应力 98 MPa ISO 527
屈服伸长率 7 % ISO 527
断裂应力 80 MPa ISO 527
断裂伸长率 80 % ISO 527
弯曲模量, 23°C 3100 MPa ISO 178
简支梁缺口冲击强度, +23°C 2 kJ/m² ISO 179/1eA
悬臂梁缺口冲击强度, +23°C 2 kJ/m² ISO 180/1A
悬臂梁缺口冲击强度 2 kJ/m² ISO 180/1A
悬臂梁缺口冲击强度 - 温度 -30 °C -
ASTM数据
拉伸模量 3210 MPa ASTM D 638
屈服应力 103 MPa ASTM D 638
断裂拉伸强度 85 MPa ASTM D 638
屈服伸长率 7 % ASTM D 638
断裂伸长率 80 % ASTM D 638
弯曲模量 3320 MPa ASTM D 790
悬臂梁缺口冲击强度, 1/8 in 32 J/m ASTM D 256
低温悬臂梁缺口冲击强度, Low-Temperature 35 J/m ASTM D 256
温度 -30 °C -
Izod冲击强度, 1/8 in N J/m ASTM D 256
热性能价值单位Test Standard
ISO数据
热变形温度, 1.80 MPa 168 °C ISO 75-1/-2
维卡软化温度, B 192 °C ISO 306
线性热膨胀系数, 平行 55 E-6/K ISO 11359-1/-2
线性热膨胀系数, 垂直 55 E-6/K ISO 11359-1/-2
ASTM数据
热释放速率, 平行 60 E-6/K ASTM D 696
热释放速率, 垂直 60 E-6/K ASTM D 696
DTUL @ 264 psi 173 °C ASTM D 648
维卡温度 192 °C ASTM D 1525
其它性能价值单位Test Standard
吸水性 0.36 % 类似ISO 62
吸湿性 0.08 % 类似ISO 62
密度 1280 kg/m³ ISO 1183
密度 1280 kg/m³ ASTM D 792
加工推荐（注塑）价值单位Test Standard
预干燥-温度 135 °C -
预干燥-时间 4 - 6 h -
加工湿度 ≤0.02 % -
注塑熔体温度 330 - 355 °C -
模具温度 95 - 135 °C -
1区 310 - 330 °C -
2区 320 - 345 °C -
3区 330 - 355 °C -
喷嘴温度 325 - 350 °C -
螺杆转速 40 - 70 rpm -
背压 0.3 - 0.7 MPa -
典型数据
加工方法
注塑
添加剂
脱模助剂
特殊性能
阻燃的, 经热稳处理的/耐热的, 透明.
特征
无定形, 防蠕变, 脆性, 好粘附性能, 低烟量
耐化学试剂
通用耐化学性, 水解稳定
应用
电子电气
地区供应
北美, 欧洲, 亚太, 中南美洲
权利义务的法律声明
Copyright Altair Engineering GmbH. Altair Engineering GmbH assumes no liability for the system to be free of errors. The user takes sole responsibility for the use of this data under the exclusion of every liability from Altair Engineering GmbH; this is especially valid for claims of compensation resulting from consequential damages. Altair explicitly points out that any decision about the application of materials must be double checked with the producer of this material. This includes all contents of this system. Copyright laws are applicable for the content of this system.
Created: Source: www.materialdatacenter.com


Material Data Center is provided by M-Base Engineering + Software GmbH. M-Base Engineering + Software GmbH assumes no liability for the system to be free of errors. Any decision about the application of materials must be double checked with the producer of this material.

Additional information about this material, like producer contact address, etc. can be found at www.materialdatacenter.com. For access to this extra information a registration is requested. Free online registration is available.