Material Data Center is a leading international information system for the plastics industry. Material Data Center offers a comprehensive plastics database, calculation tools, CAE interfaces, a literature database and an application database. For more information about Material Data Center visit www.materialdatacenter.com.

This is the free Material Data Center Datasheet of NORYL™ Resin N850 - Europe - (PPE+PS) - Saudi Basic Industries Corporation (SABIC)

Material Data Center offers the following functions for NORYL™ Resin N850 - Europe:
unit conversion, PDF datasheet print, comparison with other plastics, snap fit calculation, beam deflection calculation, CAE Interfaces

Check here, which other Noryl datasheets, application examples or technical articles are available in Material Data Center

Use the following short links to get directly to the properties of interest in this datasheet:
加工/物理特性 - 机械性能 - 热性能 - 其它性能 - 加工推荐（注塑）
Any use of this information falls under the rules of our disclaimer.
材料文字说明
NORYL™ N850 resin is a non-reinforced blend of polyphenylene ether (PPE) + high impact polystyrene (HIPS). This high flow, injection moldable grade contains non-brominated, non-chlorinated flame retardant and carries a UL94 flame rating of 5VA at 3mm and V0 at 1.5mm along with UL746C Outdoor Suitability rating of F2. NORYL N850 resin exhibits high impact strength, dimensional stability, hydrolytic stability, and very low moisture absorption. This material is an excellent candidate for electrical and business equipment applications.
加工/物理特性价值单位Test Standard
ASTM数据
熔融指数, MFI 18 g/10min ASTM D 1238
温度 260 °C -
负载 3.8 kg -
机械性能价值单位Test Standard
ISO数据
拉伸模量 2950 MPa ISO 527
屈服应力 66 MPa ISO 527
屈服伸长率 3.2 % ISO 527
断裂应力 61 MPa ISO 527
断裂伸长率 4.5 % ISO 527
弯曲模量 2600 MPa ISO 178
悬臂梁缺口冲击强度, +23°C, 4mm 10 kJ/m² ISO 180/1A
ASTM数据
拉伸模量 2620 MPa ASTM D 638
屈服应力 62 MPa ASTM D 638
断裂拉伸强度 48 MPa ASTM D 638
屈服伸长率 3.6 % ASTM D 638
断裂伸长率 18 % ASTM D 638
弯曲模量 2410 MPa ASTM D 790
悬臂梁缺口冲击强度, 1/8 in 213 J/m ASTM D 256
热性能价值单位Test Standard
ISO数据
热变形温度, 1.80 MPa 82 °C ISO 75-1/-2
热变形温度, 0.45 MPa 95 °C ISO 75-1/-2
维卡软化温度, 120°C/h 50N 108 °C ISO 306
1.5mm名义厚度时的燃烧性 V-0 class IEC 60695-11-10
测试用试样的厚度 1.5 mm -
厚度为h时的燃烧性 HB class IEC 60695-11-10
测试用试样的厚度 1.0 mm -
厚度为h时的5V燃烧性 5VA class IEC 60695-11-20
测试用试样的厚度 3.0 mm -
ASTM数据
DTUL @ 66 psi 93 °C ASTM D 648
DTUL @ 264 psi 82 °C ASTM D 648
维卡温度 101 °C ASTM D 1525
其它性能价值单位Test Standard
密度 1130 kg/m³ ASTM D 792
加工推荐（注塑）价值单位Test Standard
预干燥-温度 75 - 80 °C -
预干燥-时间 3 - 4 h -
加工湿度 ≤-0.02 % -
注塑熔体温度 250 - 275 °C -
模具温度 55 - 75 °C -
1区 215 - 265 °C -
2区 225 - 270 °C -
3区 240 - 275 °C -
螺杆转速 20 - 100 rpm -
背压 0.3 - 0.7 MPa -
典型数据
加工方法
注塑
添加剂
阻燃剂
特殊性能
阻燃的
耐化学试剂
水解稳定
地区供应
欧洲
权利义务的法律声明
Copyright Altair Engineering GmbH. Altair Engineering GmbH assumes no liability for the system to be free of errors. The user takes sole responsibility for the use of this data under the exclusion of every liability from Altair Engineering GmbH; this is especially valid for claims of compensation resulting from consequential damages. Altair explicitly points out that any decision about the application of materials must be double checked with the producer of this material. This includes all contents of this system. Copyright laws are applicable for the content of this system.
Created: Source: www.materialdatacenter.com


Material Data Center is provided by M-Base Engineering + Software GmbH. M-Base Engineering + Software GmbH assumes no liability for the system to be free of errors. Any decision about the application of materials must be double checked with the producer of this material.

Additional information about this material, like producer contact address, etc. can be found at www.materialdatacenter.com. For access to this extra information a registration is requested. Free online registration is available.