Material Data Center is a leading international information system for the plastics industry. Material Data Center offers a comprehensive plastics database, calculation tools, CAE interfaces, a literature database and an application database. For more information about Material Data Center visit www.materialdatacenter.com.

This is the free Material Data Center Datasheet of NORYL™ Resin GFN2 - Asia - (PPE+PS)-GF20 - Saudi Basic Industries Corporation (SABIC)

Material Data Center offers the following functions for NORYL™ Resin GFN2 - Asia:
unit conversion, PDF datasheet print, comparison with other plastics, snap fit calculation, beam deflection calculation, CAE Interfaces

Check here, which other Noryl datasheets, application examples or technical articles are available in Material Data Center

Use the following short links to get directly to the properties of interest in this datasheet:
加工/物理特性 - 机械性能 - 热性能 - 其它性能 - 加工推荐（注塑）
Any use of this information falls under the rules of our disclaimer.
材料文字说明
NORYL™ GFN2 resin is a 20% glass reinforced blend of polyphenylene ether (PPE) + high impact polystyrene (HIPS). This general-purpose injection moldable grade exhibits very low moisture absorption, high strength, hydrolytic stability, Low warpage, low specific gravity, and dimensional stability. NORYL GFN2 carries a UL746C outdoor suitability rating of F1 and is an excellent candidate for a variety of indoor and outdoor applications including construction, electrical components + displays, lawn and garden equipment. *See NORYL GFN2F resin for FDA food compliant / NSF version.

UL Yellow Card Link E45587-237020
加工/物理特性价值单位Test Standard
ISO数据
熔体体积流动速度, MVR 2 cm³/10min ISO 1133
温度 280 °C -
载荷 5 kg -
ASTM数据
熔融指数, MFI 11.7 g/10min ASTM D 1238
温度 300 °C -
负载 5 kg -
机械性能价值单位Test Standard
ISO数据
拉伸模量 6000 MPa ISO 527
屈服应力 90 MPa ISO 527
断裂伸长率 3 % ISO 527
弯曲模量 5400 MPa ISO 178
简支梁缺口冲击强度, +23°C 8 kJ/m² ISO 179/1eA
Izod impact strength, +23°C, 4mm 30 kJ/m² ISO 180/1U
悬臂梁缺口冲击强度, +23°C, 4mm 10 kJ/m² ISO 180/1A
悬臂梁缺口冲击强度, -30°C, 4mm 9 kJ/m² ISO 180/1A
ASTM数据
拉伸模量 6500 MPa ASTM D 638
屈服应力 100 MPa ASTM D 638
断裂伸长率 3 % ASTM D 638
悬臂梁缺口冲击强度, 1/8 in 88 J/m ASTM D 256
Izod冲击强度, 1/8 in 550 J/m ASTM D 256
热性能价值单位Test Standard
ISO数据
热变形温度, 1.80 MPa 135 °C ISO 75-1/-2
维卡软化温度, B 140 °C ISO 306
维卡软化温度, 120°C/h 50N 147 °C ISO 306
1.5mm名义厚度时的燃烧性 HB class IEC 60695-11-10
测试用试样的厚度 1.5 mm -
ASTM数据
DTUL @ 264 psi 137 °C ASTM D 648
其它性能价值单位Test Standard
吸湿性 0.04 % 类似ISO 62
密度 1230 kg/m³ ASTM D 792
加工推荐（注塑）价值单位Test Standard
预干燥-温度 110 - 120 °C -
预干燥-时间 3 - 4 h -
加工湿度 ≤0.02 % -
注塑熔体温度 300 - 325 °C -
模具温度 80 - 110 °C -
1区 265 - 315 °C -
2区 275 - 320 °C -
3区 290 - 325 °C -
螺杆转速 20 - 100 rpm -
背压 0.3 - 0.7 MPa -
典型数据
加工方法
注塑
耐化学试剂
水解稳定
Certifications
可食品接触的, FDA 21 CFR认证
应用
汽车
地区供应
亚太
权利义务的法律声明
Copyright Altair Engineering GmbH. Altair Engineering GmbH assumes no liability for the system to be free of errors. The user takes sole responsibility for the use of this data under the exclusion of every liability from Altair Engineering GmbH; this is especially valid for claims of compensation resulting from consequential damages. Altair explicitly points out that any decision about the application of materials must be double checked with the producer of this material. This includes all contents of this system. Copyright laws are applicable for the content of this system.
Created: Source: www.materialdatacenter.com


Material Data Center is provided by M-Base Engineering + Software GmbH. M-Base Engineering + Software GmbH assumes no liability for the system to be free of errors. Any decision about the application of materials must be double checked with the producer of this material.

Additional information about this material, like producer contact address, etc. can be found at www.materialdatacenter.com. For access to this extra information a registration is requested. Free online registration is available.