Material Data Center is a leading international information system for the plastics industry. Material Data Center offers a comprehensive plastics database, calculation tools, CAE interfaces, a literature database and an application database. For more information about Material Data Center visit www.materialdatacenter.com.

This is the free Material Data Center Datasheet of LEXAN™ Copolymer FST3403 - Americas - PC - Saudi Basic Industries Corporation (SABIC)

Material Data Center offers the following functions for LEXAN™ Copolymer FST3403 - Americas:
unit conversion, PDF datasheet print, comparison with other plastics, snap fit calculation, beam deflection calculation, CAE Interfaces

Check here, which other Lexan datasheets, application examples or technical articles are available in Material Data Center

Use the following short links to get directly to the properties of interest in this datasheet:
加工/物理特性 - 机械性能 - 热性能 - 其它性能 - 加工推荐（注塑）
Any use of this information falls under the rules of our disclaimer.
材料文字说明
LEXAN FST3403 resin is a high flow PC Copolymer Resin, suitable for injection molding. This halogen-free flame retardant resin is EN45545 R6 HL3 compliant and an ideal candidate for train interior applications (category R6). It also meets requirements of DIN5510-2, NFPA-130 and PN-K-02511 standards. Available in opaque colors.
加工/物理特性价值单位Test Standard
ISO数据
熔体体积流动速度, MVR 10 cm³/10min ISO 1133
温度 300 °C -
载荷 1.2 kg -
ASTM数据
熔融指数, MFI 12 g/10min ASTM D 1238
温度 300 °C -
负载 1.2 kg -
机械性能价值单位Test Standard
ISO数据
拉伸模量 2600 MPa ISO 527
屈服应力 77 MPa ISO 527
屈服伸长率 6 % ISO 527
断裂应力 70 MPa ISO 527
断裂伸长率 50 % ISO 527
弯曲模量 2700 MPa ISO 178
简支梁冲击强度, +23°C N kJ/m² ISO 179/1eU
简支梁冲击强度, -30°C N kJ/m² ISO 179/1eU
简支梁冲击强度, +23°C, 3mm N kJ/m² ISO 179/1eU
简支梁冲击强度, -30°C, 3mm N kJ/m² ISO 179/1eU
简支梁缺口冲击强度, +23°C 14 kJ/m² ISO 179/1eA
简支梁缺口冲击强度, -30°C 10 kJ/m² ISO 179/1eA
简支梁缺口冲击强度, +23°C, 3mm 13 kJ/m² ISO 179/1eA
简支梁缺口冲击强度, -30°C, 3mm 5 kJ/m² ISO 179/1eA
Izod冲击强度, +23°C N kJ/m² ISO 180/1U
Izod impact strength, +23°C, 4mm N kJ/m² ISO 180/1U
Izod impact strength, -30°C, 4mm N kJ/m² ISO 180/1U
悬臂梁缺口冲击强度, +23°C, 4mm 12 kJ/m² ISO 180/1A
悬臂梁缺口冲击强度, -30°C, 4mm 10 kJ/m² ISO 180/1A
悬臂梁缺口冲击强度, +23°C, 3mm 13 kJ/m² ISO 180/1A
悬臂梁缺口冲击强度, -30°C, 3mm 6 kJ/m² ISO 180/1A
ASTM数据
拉伸模量 2600 MPa ASTM D 638
屈服应力 77 MPa ASTM D 638
断裂拉伸强度 70 MPa ASTM D 638
屈服伸长率 6 % ASTM D 638
断裂伸长率 80 % ASTM D 638
弯曲模量 2500 MPa ASTM D 790
悬臂梁缺口冲击强度, 1/8 in 130 J/m ASTM D 256
低温悬臂梁缺口冲击强度, Low-Temperature 90 J/m ASTM D 256
温度 -30 °C -
热性能价值单位Test Standard
ISO数据
热变形温度, 1.80 MPa 95 °C ISO 75-1/-2
热变形温度, 0.45 MPa 105 °C ISO 75-1/-2
维卡软化温度, B 114 °C ISO 306
维卡软化温度, 120°C/h 50N 115 °C ISO 306
ASTM数据
DTUL @ 66 psi 104 °C ASTM D 648
DTUL @ 264 psi 93 °C ASTM D 648
维卡温度 114 °C ASTM D 1525
其它性能价值单位Test Standard
密度 1330 kg/m³ ISO 1183
密度 1330 kg/m³ ASTM D 792
加工推荐（注塑）价值单位Test Standard
预干燥-温度 95 - 100 °C -
预干燥-时间 6 - 8 h -
注塑熔体温度 250 - 290 °C -
模具温度 50 - 80 °C -
1区 230 - 260 °C -
2区 240 - 280 °C -
3区 250 - 290 °C -
螺杆转速 40 - 70 rpm -
背压 0.3 - 0.7 MPa -
典型数据
加工方法
注塑
添加剂
阻燃剂
特殊性能
阻燃的
地区供应
北美
权利义务的法律声明
Copyright Altair Engineering GmbH. Altair Engineering GmbH assumes no liability for the system to be free of errors. The user takes sole responsibility for the use of this data under the exclusion of every liability from Altair Engineering GmbH; this is especially valid for claims of compensation resulting from consequential damages. Altair explicitly points out that any decision about the application of materials must be double checked with the producer of this material. This includes all contents of this system. Copyright laws are applicable for the content of this system.
Created: Source: www.materialdatacenter.com


Material Data Center is provided by M-Base Engineering + Software GmbH. M-Base Engineering + Software GmbH assumes no liability for the system to be free of errors. Any decision about the application of materials must be double checked with the producer of this material.

Additional information about this material, like producer contact address, etc. can be found at www.materialdatacenter.com. For access to this extra information a registration is requested. Free online registration is available.