Material Data Center is a leading international information system for the plastics industry. Material Data Center offers a comprehensive plastics database, calculation tools, CAE interfaces, a literature database and an application database. For more information about Material Data Center visit www.materialdatacenter.com.

This is the free Material Data Center Datasheet of NORYL™ Resin PX0844 - Americas - (PPE+PS) - Saudi Basic Industries Corporation (SABIC)

Material Data Center offers the following functions for NORYL™ Resin PX0844 - Americas:
unit conversion, PDF datasheet print, comparison with other plastics, snap fit calculation, beam deflection calculation, CAE Interfaces

Check here, which other Noryl datasheets, application examples or technical articles are available in Material Data Center

Use the following short links to get directly to the properties of interest in this datasheet:
Processing/Physical Characteristics - 기계적 특성 - 열적 특성 - 기타 특성 - Processing Recommendation Injection Molding
Any use of this information falls under the rules of our disclaimer.
제품 설명서
NORYL™ PX0844 resin is a non-reinforced blend of polyphenylene ether (PPE) + high impact polystyrene (HIPS). This grade exhibits very low moisture absorption, hydrolytic stability, dimensional stabilty, good foam adhesion, and property retention over a wide temperature range. NORYL PX0844 resin is inherently UL94 HB and is an excellent candidate for automotive interior applications such as instrument panels, audio components, speaker housings, and interior trim. *see NORYL PX0888 resin for higher heat resistance.
Processing/Physical Characteristics값단위시험규격
ASTM 데이터
용융 흐름성, MFI 13.7 g/10min ASTM D 1238
온도 280 °C -
하중 5 kg -
기계적 특성값단위시험규격
ISO 데이터
인장탄성률 2350 MPa ISO 527
항복강도 47 MPa ISO 527
항복변형률 2.9 % ISO 527
파단시 강도 43 MPa ISO 527
파단시 신율 43 % ISO 527
굴곡 계수 2400 MPa ISO 178
굴곡 강도 78 MPa ISO 178
아이조드 노치 충격 강도, +23°C, 4mm 17 kJ/m² ISO 180/1A
아이조드 노치 충격 강도, -30°C, 4mm 10 kJ/m² ISO 180/1A
ASTM 데이터
인장탄성률 2290 MPa ASTM D 638
항복강도 49 MPa ASTM D 638
파단시 강도 44 MPa ASTM D 638
항복변형률 3 % ASTM D 638
파단시 신율 30 % ASTM D 638
굴곡 계수 2550 MPa ASTM D 790
로크웰 경도 R 114 - ASTM D 785
아이조드 충격은 노치, 1/8 in 234 J/m ASTM D 256
아이조드 충격은 노치, Low-Temperature 133 J/m ASTM D 256
온도 -40 °C -
열적 특성값단위시험규격
ISO 데이터
비카트 연화 온도, B 125 °C ISO 306
비카트 연화 온도, 120°C/h 50N 128 °C ISO 306
ASTM 데이터
DTUL @ 66 psi 120 °C ASTM D 648
DTUL @ 264 psi 105 °C ASTM D 648
기타 특성값단위시험규격
밀도 1060 kg/m³ ASTM D 792
Processing Recommendation Injection Molding값단위시험규격
Pre-drying - Temperature 105 - 110 °C -
Pre-drying - Time 3 - 4 h -
Processing humidity ≤0.02 % -
용융수지온도 275 - 305 °C -
성형온도 70 - 100 °C -
Zone 1 245 - 295 °C -
Zone 2 255 - 300 °C -
Zone 3 265 - 305 °C -
Screw speed 20 - 100 rpm -
Back pressure 0.3 - 0.7 MPa -
특징
생산 공정
사출 성형
내화학성에
Hydrolytically Stable
응용
자동차의
지역별 검색
쨘횕쩐횈쨍횧쨍짰횆짬
Disclaimer
Copyright Altair Engineering GmbH. Altair Engineering GmbH assumes no liability for the system to be free of errors. The user takes sole responsibility for the use of this data under the exclusion of every liability from Altair Engineering GmbH; this is especially valid for claims of compensation resulting from consequential damages. Altair explicitly points out that any decision about the application of materials must be double checked with the producer of this material. This includes all contents of this system. Copyright laws are applicable for the content of this system.
Created: Source: www.materialdatacenter.com