Material Data Center is a leading international information system for the plastics industry. Material Data Center offers a comprehensive plastics database, calculation tools, CAE interfaces, a literature database and an application database. For more information about Material Data Center visit www.materialdatacenter.com.

This is the free Material Data Center Datasheet of Bayblend® T50 XF - (PC+ABS) - Covestro Deutschland AG

Material Data Center offers the following functions for Bayblend® T50 XF:
unit conversion, PDF datasheet print, comparison with other plastics, snap fit calculation, beam deflection calculation, parameters for material models, CAE Interfaces

Check here, which other Bayblend datasheets, application examples or technical articles are available in Material Data Center

Use the following short links to get directly to the properties of interest in this datasheet:
Any use of this information falls under the rules of our disclaimer.
제품 설명서
  • (PC ABS)-Blend
  • Vicat/B 120 temperature = 112 °C
  • excellent flow
  • good low temperature impact strength
Processing/Physical Characteristics단위시험규격
ISO 데이터
용융 부피 - 흐름 속도, MVR 19 cm³/10min ISO 1133
온도 260 °C -
하중 5 kg -
기계적 특성단위시험규격
ISO 데이터
인장탄성률 2100 MPa ISO 527
항복강도 50 MPa ISO 527
항복변형률 4.5 % ISO 527
열적 특성단위시험규격
ISO 데이터
하중하에서의 변형온도, 1.80 MPa 99 °C ISO 75-1/-2
하중하에서의 변형온도, 0.45 MPa 120 °C ISO 75-1/-2
비카트 연화 온도, B 113 °C ISO 306
선형 열팽창 계수, 평행 85 E-6/K ISO 11359-1/-2
선형 열팽창 계수, 수직 85 E-6/K ISO 11359-1/-2
두께 H인 제품의 난연성 HB class IEC 60695-11-10
테스트 두께 0.8 mm -
전기적 특성단위시험규격
ISO 데이터
상대 유전율, 100Hz 3.1 - IEC 62631-2-1
상대 유전뮬, 1MHz 3 - IEC 62631-2-1
소산 인자, 100Hz 25 E-4 IEC 62631-2-1
소산 인자, 1MHz 90 E-4 IEC 62631-2-1
부피 저항 >1E13 Ohm*m IEC 62631-3-1
표면 저항 >1E15 Ohm IEC 62631-3-2
전기 압력 40 kV/mm IEC 60243-1
CTI 250 - IEC 60112
기타 특성단위시험규격
물에서의 흡수성 0.7 % ISO 62와 유사
조건에서의 흡습성 0.2 % ISO 62와 유사
밀도 1110 kg/m³ ISO 1183
테스트 견본 생산단위시험규격
ISO 데이터
사출성형: 용융수지온도 260 °C ISO 294
사출성형: 금형온도 80 °C ISO 294
사출성형: 사출속도 240 mm/s ISO 294
Processing Recommendation Injection Molding단위시험규격
Pre-drying - Temperature 100 - 110 °C -
Pre-drying - Time 2 - 4 h -
Processing humidity ≤0.02 % -
용융수지온도 240 - 280 °C -
성형온도 70 - 100 °C -
도표
점도-변형률 , Bayblend® T50 XF, (PC+ABS), Covestro
전단-변형률 , Bayblend® T50 XF, (PC+ABS), Covestro
응력-신율 , Bayblend® T50 XF, (PC+ABS), Covestro
시컨트탄성율-신율 , Bayblend® T50 XF, (PC+ABS), Covestro
특징
생산 공정
사출 성형
인도 유형
펠렛 (입자,알갱이)
부가물
이형제
지역별 검색
기타 정보
사E성
PREPROCESSING
Max. Water content: 0.02 %
Drying temperature: 100 - 110 °C
(depending on the grade 10°C below the Vicat VST/B120 temperature, but not higher as the recommended values).
Drying time:
Circulating air drying oven (50 % fresh air) 4-8 h
Fresh air dryer (high speed dryer) 2-4 h
Dry air dryer 2-4 h

PROCESSING
Melt temperature: 240-280 °C
Mold temperature: 70-100 °C

Use open nozzle.
Disclaimer
Copyright Altair Engineering GmbH. Altair Engineering GmbH assumes no liability for the system to be free of errors. The user takes sole responsibility for the use of this data under the exclusion of every liability from Altair Engineering GmbH; this is especially valid for claims of compensation resulting from consequential damages. Altair explicitly points out that any decision about the application of materials must be double checked with the producer of this material. This includes all contents of this system. Copyright laws are applicable for the content of this system.
Created: Source: www.materialdatacenter.com