Material Data Center is a leading international information system for the plastics industry. Material Data Center offers a comprehensive plastics database, calculation tools, CAE interfaces, a literature database and an application database. For more information about Material Data Center visit www.materialdatacenter.com.

This is the free Material Data Center Datasheet of NORYL™ Resin EM6100 - Europe - (PPE+PS) - Saudi Basic Industries Corporation (SABIC)

Material Data Center offers the following functions for NORYL™ Resin EM6100 - Europe:
unit conversion, PDF datasheet print, comparison with other plastics, snap fit calculation, beam deflection calculation, CAE Interfaces

Check here, which other Noryl datasheets, application examples or technical articles are available in Material Data Center

Use the following short links to get directly to the properties of interest in this datasheet:
Processing/Physical Characteristics - 기계적 특성 - 열적 특성 - 기타 특성 - Processing Recommendation Injection Molding
Any use of this information falls under the rules of our disclaimer.
제품 설명서
NORYL™ EM6100 is a non-reinforced blend of polyphenylene ether (PPE) + high impact polystyrene (HIPS). This grade exhibits a balance of flow/heat/impact, dimensional stability, along with paint adhesion. NORYL EM6100 resin is suitable for the automotive interior market in applications such as HVAC housings and radio components. MS-DB424, WSBM4D844-A9, GMP.PPE.007.

UL Yellow Card Link E121562-221232
Processing/Physical Characteristics값단위시험규격
ISO 데이터
용융 부피 - 흐름 속도, MVR 15 cm³/10min ISO 1133
온도 280 °C -
하중 5 kg -
ASTM 데이터
용융 흐름성, MFI 15 g/10min ASTM D 1238
온도 280 °C -
하중 5 kg -
기계적 특성값단위시험규격
ISO 데이터
인장탄성률 2050 MPa ISO 527
항복강도 42 MPa ISO 527
항복변형률 2.8 % ISO 527
파단시 강도 40 MPa ISO 527
파단시 신율 50 % ISO 527
굴곡 계수 2100 MPa ISO 178
굴곡 강도 65 MPa ISO 178
아이조드 노치 충격 강도, +23°C, 4mm 33 kJ/m² ISO 180/1A
아이조드 노치 충격 강도, -30°C, 4mm 15 kJ/m² ISO 180/1A
ASTM 데이터
인장탄성률 1900 MPa ASTM D 638
항복강도 43 MPa ASTM D 638
파단시 강도 40 MPa ASTM D 638
항복변형률 3 % ASTM D 638
파단시 신율 65 % ASTM D 638
굴곡 계수 2100 MPa ASTM D 790
아이조드 충격은 노치, 1/8 in 453 J/m ASTM D 256
아이조드 충격은 노치, Low-Temperature 250 J/m ASTM D 256
온도 -30 °C -
열적 특성값단위시험규격
ISO 데이터
하중하에서의 변형온도, 1.80 MPa 110 °C ISO 75-1/-2
하중하에서의 변형온도, 0.45 MPa 126 °C ISO 75-1/-2
비카트 연화 온도, B 119 °C ISO 306
비카트 연화 온도, 120°C/h 50N 123 °C ISO 306
1.5mm 평균두께에서의 난연성 HB class IEC 60695-11-10
테스트 두께 1.5 mm -
ASTM 데이터
DTUL @ 66 psi 124 °C ASTM D 648
DTUL @ 264 psi 106 °C ASTM D 648
기타 특성값단위시험규격
밀도 1050 kg/m³ ASTM D 792
Processing Recommendation Injection Molding값단위시험규격
Pre-drying - Temperature 95 - 105 °C -
Pre-drying - Time 3 - 4 h -
Processing humidity ≤0.02 % -
용융수지온도 265 - 295 °C -
성형온도 65 - 95 °C -
Zone 1 230 - 280 °C -
Zone 2 245 - 290 °C -
Zone 3 255 - 295 °C -
Screw speed 20 - 100 rpm -
Back pressure 0.3 - 0.7 MPa -
특징
생산 공정
사출 성형
응용
자동차의
지역별 검색
짱쨌쨈
Disclaimer
Copyright Altair Engineering GmbH. Altair Engineering GmbH assumes no liability for the system to be free of errors. The user takes sole responsibility for the use of this data under the exclusion of every liability from Altair Engineering GmbH; this is especially valid for claims of compensation resulting from consequential damages. Altair explicitly points out that any decision about the application of materials must be double checked with the producer of this material. This includes all contents of this system. Copyright laws are applicable for the content of this system.
Created: Source: www.materialdatacenter.com


Material Data Center is provided by M-Base Engineering + Software GmbH. M-Base Engineering + Software GmbH assumes no liability for the system to be free of errors. Any decision about the application of materials must be double checked with the producer of this material.

Additional information about this material, like producer contact address, etc. can be found at www.materialdatacenter.com. For access to this extra information a registration is requested. Free online registration is available.