Complete Set of CAMPUS® Data, ASTM Data, Biopolymer Database, Application Database, Tradename Database, Literature Database, Toolbox.

Material datasheets available free. Online registration at: www.materialdatacenter.com

Material Data Center is a leading international information system for the plastics industry. Material Data Center offers a comprehensive plastics database, calculation tools, CAE interfaces, a literature database and an application database. For more information about Material Data Center visit www.materialdatacenter.com.

This is the free Material Data Center Datasheet of SABIC® PPcompound 1920 - PP - Saudi Basic Industries Corporation (SABIC)

Material Data Center offers the following functions for SABIC® PPcompound 1920:
unit conversion, PDF datasheet print, comparison with other plastics, snap fit calculation, beam deflection calculation, CAE Interfaces

Check here, which other Sabic datasheets, application examples or technical articles are available in Material Data Center

Use the following short links to get directly to the properties of interest in this datasheet:
Processing/Physical Characteristics - 機械的特性 - 熱的特性 - その他の特性. - Processing Recommendation Injection Molding
Any use of this information falls under the rules of our disclaimer.
商品の説明文
SABIC® PPcompound 1920 is an FDA compliant, talc filled, heat stabilized homopolymer polypropylene compound. This compound exhibits high flow and is suitable for injection molding applications. IMDS ID: 482238095
Processing/Physical Characteristics値単位テスト基準
ISO データ
メルトフローレート, MFI 18 g/10min ISO 1133
温度 230 °C -
荷重 2.16 kg -
機械的特性値単位テスト基準
ISO データ
引張弾性率 3200 MPa ISO 527
降伏応力 36 MPa ISO 527
降伏ひずみ 4.5 % ISO 527
破壊応力 32 MPa ISO 527
破壊ひずみ 10.6 % ISO 527
曲げ弾性率, 23°C 3170 MPa ISO 178
ノッチ付きシャルピー衝撃強さ, +23°C 2 kJ/m² ISO 179/1eA
ノッチ付きシャルピー衝撃強さ, -30ﾟC 1 kJ/m² ISO 179/1eA
ノッチ付きIzod衝撃強さ 1 kJ/m² ISO 180/1A
ASTM数据
引張弾性率 2970 MPa ASTM D 638
降伏応力 36 MPa ASTM D 638
破壊応力 29 MPa ASTM D 638
降伏点伸び 5 % ASTM D 638
破断伸び 20.5 % ASTM D 638
曲げ弾性率 2490 MPa ASTM D 790
ショア硬さD 74 - ASTM D 2240
熱的特性値単位テスト基準
ISO データ
荷重たわみ温度, 1.80 MPa 73 °C ISO 75-1/-2
荷重たわみ温度, 0.45 MPa 128 °C ISO 75-1/-2
ビカット軟化温度, A 157 °C ISO 306
ASTM数据
DTUL @ 66 psi 129 °C ASTM D 648
DTUL @ 264 psi 73 °C ASTM D 648
その他の特性.値単位テスト基準
密度. 1050 kg/m³ ISO 1183
密度 1050 kg/m³ ASTM D 792
Processing Recommendation Injection Molding値単位テスト基準
Pre-drying - Temperature 80 - 100 °C -
Pre-drying - Time 2 - 4 h -
樹脂温度 210 - 270 °C -
金型温度 15 - 60 °C -
Zone 1 190 - 230 °C -
Zone 2 200 - 250 °C -
Zone 3 210 - 270 °C -
Nozzle temperature 210 - 270 °C -
Back pressure 1 - 1.5 MPa -
特殊な特性
成形加工法.
射出成形.
特殊な特性.
熱安定化.
な特性
Homopolymer
Certifications
Food approval FDA 21 CFR
Disclaimer
Copyright Altair Engineering GmbH. Altair Engineering GmbH assumes no liability for the system to be free of errors. The user takes sole responsibility for the use of this data under the exclusion of every liability from Altair Engineering GmbH; this is especially valid for claims of compensation resulting from consequential damages. Altair explicitly points out that any decision about the application of materials must be double checked with the producer of this material. This includes all contents of this system. Copyright laws are applicable for the content of this system.
Created: Source: www.materialdatacenter.com


Material Data Center is provided by M-Base Engineering + Software GmbH. M-Base Engineering + Software GmbH assumes no liability for the system to be free of errors. Any decision about the application of materials must be double checked with the producer of this material.

Additional information about this material, like producer contact address, etc. can be found at www.materialdatacenter.com. For access to this extra information a registration is requested. Free online registration is available.