Material Data Center is a leading international information system for the plastics industry. Material Data Center offers a comprehensive plastics database, calculation tools, CAE interfaces, a literature database and an application database. For more information about Material Data Center visit www.materialdatacenter.com.

This is the free Material Data Center Datasheet of Luran® 388S - SAN - INEOS Styrolution

Material Data Center offers the following functions for Luran® 388S:
unit conversion, PDF datasheet print, comparison with other plastics, flow length calculation, snap fit calculation, beam deflection calculation, cooling time calculation, parameters for material models, CAE Interfaces

Check here, which other Luran datasheets, application examples or technical articles are available in Material Data Center

Use the following short links to get directly to the properties of interest in this datasheet:
Any use of this information falls under the rules of our disclaimer.
商品の説明文
Speciality grade with highest mechanical strength and chemical resistance.
Processing/Physical Characteristics単位テスト基準
ISO データ
メルトボリュームレイト, MVR 7 cm³/10min ISO 1133
温度 220 °C -
荷重 10 kg -
溶融時の密度 970 kg/m³ -
溶融時の熱伝導率 0.17 W/(m K) -
溶融時の比熱 2300 J/(kg K) -
突き出し時の時の温度 99 °C -
機械的特性単位テスト基準
ISO データ
引張弾性率 3800 MPa ISO 527
破壊応力 79 MPa ISO 527
破壊ひずみ 4 % ISO 527
引張クリープ弾性率, 1h 3500 MPa ISO 899-1
引張クリープ弾性率, 1000h 2800 MPa ISO 899-1
シャルピー衝撃強さ, +23°C 21 kJ/m² ISO 179/1eU
シャルピー衝撃強さ, -30°C 19 kJ/m² ISO 179/1eU
ノッチ付きシャルピー衝撃強さ, +23°C 2.5 kJ/m² ISO 179/1eA
熱的特性単位テスト基準
ISO データ
荷重たわみ温度, 1.80 MPa 90 °C ISO 75-1/-2
荷重たわみ温度, 0.45 MPa 102 °C ISO 75-1/-2
ビカット軟化温度, B 107 °C ISO 306
線膨張係数, 平行 70 E-6/K ISO 11359-1/-2
1.5mm厚さでの燃焼性 HB class IEC 60695-11-10
試験片の厚さ 1.6 mm -
Yellow Card 可用 はい - -
酸素指数 18 % ISO 4589-1/-2
電気的特性.単位テスト基準
ISO データ
比誘電率, 100Hz 3 - IEC 62631-2-1
比誘電率, 1MHz 2.8 - IEC 62631-2-1
誘電正接, 100Hz 50 E-4 IEC 62631-2-1
誘電正接, 1MHz 80 E-4 IEC 62631-2-1
体積抵抗率 >1E13 Ohm*m IEC 62631-3-1
表面抵抗率 >1E15 Ohm IEC 62631-3-2
耐トラッキング性 475 - IEC 60112
その他の特性.単位テスト基準
吸湿率 0.3 % Sim. to ISO 62
密度 1080 kg/m³ ISO 1183
試験片の成形条件.単位テスト基準
ISO データ
射出成形, 樹脂温度 250 °C ISO 294
射出成形, 金型温度 60 °C ISO 294
射出成形, 射出速度 200 mm/s ISO 294
Processing Recommendation Injection Molding単位テスト基準
Pre-drying - Temperature 80 °C -
Pre-drying - Time 2 - 4 h -
樹脂温度 220 - 260 °C -
金型温度 40 - 80 °C -
機能
 粘度せん断速度. , Luran® 388S, SAN, INEOS Styrolution
 せん断応力-せん断速度. , Luran® 388S, SAN, INEOS Styrolution
 応力-ひずみ. , Luran® 388S, SAN, INEOS Styrolution
 割線弾性率−ひずみ. , Luran® 388S, SAN, INEOS Styrolution
 応力-ひずみ (等時的). 23°C, Luran® 388S, SAN, INEOS Styrolution
 クリープ弾性率−時間. 23°C, Luran® 388S, SAN, INEOS Styrolution
クリープ曲線 23°C, Luran® 388S, SAN, INEOS Styrolution
 応力-ひずみ (等時的). 40°C, Luran® 388S, SAN, INEOS Styrolution
 クリープ弾性率−時間. 40°C, Luran® 388S, SAN, INEOS Styrolution
クリープ曲線 40°C, Luran® 388S, SAN, INEOS Styrolution
 応力-ひずみ (等時的). 60°C, Luran® 388S, SAN, INEOS Styrolution
 クリープ弾性率−時間. 60°C, Luran® 388S, SAN, INEOS Styrolution
クリープ曲線 60°C, Luran® 388S, SAN, INEOS Styrolution
 応力-ひずみ (等時的). 80°C, Luran® 388S, SAN, INEOS Styrolution
 クリープ弾性率−時間. 80°C, Luran® 388S, SAN, INEOS Styrolution
クリープ曲線 80°C, Luran® 388S, SAN, INEOS Styrolution
 pvT , Luran® 388S, SAN, INEOS Styrolution
 引張弾性率-温度. , Luran® 388S, SAN, INEOS Styrolution
特殊な特性
成形加工法.
射出成形., 異形押出成形., シート押出成形., その他の押出成形., 熱成形.
納入形状.
ペレット.
特殊な特性.
透明.
領域別の利用可能性
その他の情報
村遜速揃
PREPROCESSING
Pre/Post-processing, Pre-drying, Temperature: 80 °C
Pre/Post-processing, Pre-drying, Time: 2 - 4 h

PROCESSING
injection molding, Melt temperature, range: 220 - 260 °C
injection molding, Melt temperature, recommended: 250 °C
injection molding, Mold temperature, range: 40 - 80 °C
injection molding, Mold temperature, recommended: 60 °C
その他の押出成形.
PREPROCESSING
Pre/Post-processing, Pre-drying, Temperature: 80 °C
Pre/Post-processing, Pre-drying, Time: 2 - 4 h

PROCESSING
Extrusion, Prepreg, Melt temperature: 220 - 240 °C
Extrusion, Pipes, Melt temperature: 220 - 240 °C
族臓遜造揃
PREPROCESSING
Pre/Post-processing, Pre-drying, Temperature: 80 °C
Pre/Post-processing, Pre-drying, Time: 2 - 4 h

PROCESSING
Extrusion, Profiles, Melt temperature: 240 °C
促揃臓村促速揃
PREPROCESSING
Pre/Post-processing, Pre-drying, Temperature: 80 °C
Pre/Post-processing, Pre-drying, Time: 2 - 4 h

PROCESSING
Extrusion, Plates, Melt temperature: 220 - 240 °C
Disclaimer
Copyright Altair Engineering GmbH. Altair Engineering GmbH assumes no liability for the system to be free of errors. The user takes sole responsibility for the use of this data under the exclusion of every liability from Altair Engineering GmbH; this is especially valid for claims of compensation resulting from consequential damages. Altair explicitly points out that any decision about the application of materials must be double checked with the producer of this material. This includes all contents of this system. Copyright laws are applicable for the content of this system.
Created: Source: www.materialdatacenter.com


Material Data Center is provided by M-Base Engineering + Software GmbH. M-Base Engineering + Software GmbH assumes no liability for the system to be free of errors. Any decision about the application of materials must be double checked with the producer of this material.

Additional information about this material, like producer contact address, etc. can be found at www.materialdatacenter.com. For access to this extra information a registration is requested. Free online registration is available.