Material Data Center is a leading international information system for the plastics industry. Material Data Center offers a comprehensive plastics database, calculation tools, CAE interfaces, a literature database and an application database. For more information about Material Data Center visit www.materialdatacenter.com.

This is the free Material Data Center Datasheet of LEXAN™ Copolymer EXL4412 - PC-GF20 - Saudi Basic Industries Corporation (SABIC)

Material Data Center offers the following functions for LEXAN™ Copolymer EXL4412:
unit conversion, PDF datasheet print, comparison with other plastics, snap fit calculation, beam deflection calculation, CAE Interfaces

Check here, which other Lexan datasheets, application examples or technical articles are available in Material Data Center

Use the following short links to get directly to the properties of interest in this datasheet:
Processing/Physical Characteristics - 機械的特性 - 熱的特性 - その他の特性. - Processing Recommendation Injection Molding
Any use of this information falls under the rules of our disclaimer.
商品の説明文
LEXAN EXL4412 copolymer is a 20% glass fiber reinforced Polycarbonate Copolymer, medium flow, impact modified, injection moldable grade. EXL4412 is available in opaque colors only and is an excellent candidate for a broad range of applications that require a combination of stiffness and ductility.

UL Yellow Card Link E207780-103834023
Processing/Physical Characteristics値単位テスト基準
ISO データ
メルトボリュームレイト, MVR 10 cm³/10min ISO 1133
温度 300 °C -
荷重 1.2 kg -
ASTM数据
メルトフローレイト, MFI 11 g/10min ASTM D 1238
温度 300 °C -
荷重 1.2 kg -
機械的特性値単位テスト基準
ISO データ
引張弾性率 6500 MPa ISO 527
破壊応力 110 MPa ISO 527
破壊ひずみ 3 % ISO 527
曲げ弾性率 5700 MPa ISO 178
ノッチ付きシャルピー衝撃強さ, +23°C, 3mm 17 kJ/m² ISO 179/1eA
ノッチ付きシャルピー衝撃強さ, -30°C, 3mm 12 kJ/m² ISO 179/1eA
ノッチ付きアイゾット衝撃強さ, +23°C, 3mm 17 kJ/m² ISO 180/1A
ノッチ付きアイゾット衝撃強, -30°C, 3mm 12 kJ/m² ISO 180/1A
ASTM数据
引張弾性率 6300 MPa ASTM D 638
破壊応力 100 MPa ASTM D 638
破断伸び 3 % ASTM D 638
曲げ弾性率 5800 MPa ASTM D 790
ノッチ付きIzod衝撃強さ, 1/8 in 140 J/m ASTM D 256
アイゾット衝撃試験, 1/8 in 700 J/m ASTM D 256
熱的特性値単位テスト基準
ISO データ
ビカット軟化温度, 120°C/h 50N 142 °C ISO 306
厚さhでの燃焼性 V-1 class IEC 60695-11-10
試験片の厚さ 2.0 mm -
ASTM数据
DTUL @ 66 psi 135 °C ASTM D 648
DTUL @ 264 psi 132 °C ASTM D 648
その他の特性.値単位テスト基準
吸水率. 0.1 % Sim. to ISO 62
吸湿率 0.03 % Sim. to ISO 62
密度. 1330 kg/m³ ISO 1183
密度 1330 kg/m³ ASTM D 792
Processing Recommendation Injection Molding値単位テスト基準
Pre-drying - Temperature 110 °C -
Pre-drying - Time 3 - 6 h -
Processing humidity ≤0.02 % -
樹脂温度 285 - 310 °C -
金型温度 80 - 110 °C -
Zone 1 260 - 280 °C -
Zone 2 270 - 290 °C -
Zone 3 280 - 300 °C -
Screw speed 50 - 90 rpm -
Back pressure 0.1 - 0.3 MPa -
特殊な特性
成形加工法.
射出成形.
特殊な特性.
高耐衝撃及び耐衝撃改良.
領域別の利用可能性
北アメリカ., ヨーロッパ., アジア/太平洋地域.
Disclaimer
Copyright Altair Engineering GmbH. Altair Engineering GmbH assumes no liability for the system to be free of errors. The user takes sole responsibility for the use of this data under the exclusion of every liability from Altair Engineering GmbH; this is especially valid for claims of compensation resulting from consequential damages. Altair explicitly points out that any decision about the application of materials must be double checked with the producer of this material. This includes all contents of this system. Copyright laws are applicable for the content of this system.
Created: Source: www.materialdatacenter.com