Material Data Center is a leading international information system for the plastics industry. Material Data Center offers a comprehensive plastics database, calculation tools, CAE interfaces, a literature database and an application database. For more information about Material Data Center visit www.materialdatacenter.com.

This is the free Material Data Center Datasheet of NORYL™ Resin BN9003G - Americas - (PPE+PS) - Saudi Basic Industries Corporation (SABIC)

Material Data Center offers the following functions for NORYL™ Resin BN9003G - Americas:
unit conversion, PDF datasheet print, comparison with other plastics, snap fit calculation, beam deflection calculation, CAE Interfaces

Check here, which other Noryl datasheets, application examples or technical articles are available in Material Data Center

Use the following short links to get directly to the properties of interest in this datasheet:
Caractéristiques des transformations/physiques - Propriétés mécaniques - Propriétés thermiques - Propriétés diverses - Recommandations pour la transformation Moulage par injection - Recommandations pour la transformation Extrusion
Any use of this information falls under the rules of our disclaimer.
Informations produit
NORYL™ BN0039 resin is a non-reinforced blend of polyphenylene ether (PPE) + high impact polystyrene (HIPS). This blow moldable grade exhibits a good balance of impact resistance and surface aesthetics. NORYL BN0039 resin, with its Low warpage and dimensional stability, is an excellent candidate for automotive exterior components including spoilers.
Caractéristiques des transformations/physiquesValeurUnitéNorme du test
ISO Data
Indice de fluidité à chaud en volume, MVR 12 cm³/10min ISO 1133
Température 280 °C -
Charge 5 kg -
ASTM Data
Indice de fluidité, MFI 10 g/10min ASTM D 1238
Température 280 °C -
Charge 5 kg -
Propriétés mécaniquesValeurUnitéNorme du test
ISO Data
Module en traction 2170 MPa ISO 527
Contrainte d'écoulement 47 MPa ISO 527
Déformation au seuil d'écoulement 3.4 % ISO 527
Contrainte à la rupture 42 MPa ISO 527
Déformation à la rupture 30.4 % ISO 527
Module de flexion 2190 MPa ISO 178
Résistance au choc Charpy, +23°C N kJ/m² ISO 179/1eU
Résistance au choc Charpy, -30°C 107 kJ/m² ISO 179/1eU
Résistance au choc Charpy (entaillé), +23°C 26 kJ/m² ISO 179/1eA
Résistance au choc Charpy (entaillé), -30°C 12 kJ/m² ISO 179/1eA
Izod impact strength, +23°C, 4mm N kJ/m² ISO 180/1U
Izod impact strength, -30°C, 4mm 54 kJ/m² ISO 180/1U
Résistance au choc Izod (entaillé), +23°C, 4mm 25 kJ/m² ISO 180/1A
Résistance au choc Izod (entaillé), -30°C, 4mm 10 kJ/m² ISO 180/1A
ASTM Data
Module en traction 2240 MPa ASTM D 638
Module de traction d’élasticité 48 MPa ASTM D 638
Résistance de traction à la rupture 42 MPa ASTM D 638
Allongement d’élasticité 3.6 % ASTM D 638
Allongement à la rupture 45 % ASTM D 638
Module de flexion 2150 MPa ASTM D 790
Izod choc avec entaille, 1/8 in 320 J/m ASTM D 256
Izod choc avec entaille, bas température 127 J/m ASTM D 256
Température -30 °C -
Résistance au choc Izod, 1/8 in N J/m ASTM D 256
Propriétés thermiquesValeurUnitéNorme du test
ISO Data
Température de fléchissement s/chrg, 1.80 MPa 110 °C ISO 75-1/-2
Température de fléchissement s/chrg, 0.45 MPa 126 °C ISO 75-1/-2
Température de ramolliss. Vicat, B 127 °C ISO 306
Température de ramolliss. Vicat, 120°C/h 50N 130 °C ISO 306
ASTM Data
DTUL à 66 psi 124 °C ASTM D 648
DTUL à 264 psi 108 °C ASTM D 648
Vicat température 141 °C ASTM D 1525
Propriétés diversesValeurUnitéNorme du test
Absorption d'eau 0.25 % Sim. to ISO 62
Absorption d'humidité 0.05 % Sim. to ISO 62
Masse volumique 1060 kg/m³ ISO 1183
Densité 1060 kg/m³ ASTM D 792
Recommandations pour la transformation Moulage par injectionValeurUnitéNorme du test
Pré-séchage - température 80 - 85 °C -
Recommandations pour la transformation ExtrusionValeurUnitéNorme du test
Pré-séchage - température 80 - 85 °C -
Pré-séchage - temps 2 - 4 h -
Température de la matière fondue 235 - 260 °C -
Température du moule 65 - 95 °C -
Zone 1 260 - 225 °C -
Zone 2 230 - 260 °C -
Zone 3 235 - 260 °C -
Zone 4 235 - 260 °C -
Zone 5 235 - 260 °C -
Caractéristiques
Transformation
Soufflage
Disponibilité régionale
Amérique du nord
Conditions générales
Copyright Altair Engineering GmbH. Altair Engineering GmbH assumes no liability for the system to be free of errors. The user takes sole responsibility for the use of this data under the exclusion of every liability from Altair Engineering GmbH; this is especially valid for claims of compensation resulting from consequential damages. Altair explicitly points out that any decision about the application of materials must be double checked with the producer of this material. This includes all contents of this system. Copyright laws are applicable for the content of this system.
Created: Source: www.materialdatacenter.com


Material Data Center is provided by M-Base Engineering + Software GmbH. M-Base Engineering + Software GmbH assumes no liability for the system to be free of errors. Any decision about the application of materials must be double checked with the producer of this material.

Additional information about this material, like producer contact address, etc. can be found at www.materialdatacenter.com. For access to this extra information a registration is requested. Free online registration is available.