Material Data Center is a leading international information system for the plastics industry. Material Data Center offers a comprehensive plastics database, calculation tools, CAE interfaces, a literature database and an application database. For more information about Material Data Center visit www.materialdatacenter.com.

This is the free Material Data Center Datasheet of LEXAN™ VISUALFX™ Resin FXE1112T - Asia - PC - Saudi Basic Industries Corporation (SABIC)

Material Data Center offers the following functions for LEXAN™ VISUALFX™ Resin FXE1112T - Asia:
unit conversion, PDF datasheet print, comparison with other plastics, snap fit calculation, beam deflection calculation, CAE Interfaces

Check here, which other Lexan datasheets, application examples or technical articles are available in Material Data Center

Use the following short links to get directly to the properties of interest in this datasheet:
Caractéristiques des transformations/physiques - Propriétés mécaniques - Propriétés thermiques - Propriétés diverses - Recommandations pour la transformation Moulage par injection
Any use of this information falls under the rules of our disclaimer.
Informations produit
Lexan* FXE1112T Lexan* polycarbonate (PC) siloxane copolymer resin is a transparent injection molding grade. This resin offers good low temperature (-20 C) ductility in combination with high flow characteristics and excellent processability with opportunities for shorter IM cycle times compared to standard PC. Lexan FXE1112T resin may be an excellent candidate for a broad range of applications. This product is available in SABIC VISUALFX* resin Piano Black, Raven Black & Illuminate color range only.

UL Yellow Card Link E207780-633835
Caractéristiques des transformations/physiquesValeurUnitéNorme du test
ISO Data
Indice de fluidité à chaud en volume, MVR 19 cm³/10min ISO 1133
Température 300 °C -
Charge 1.2 kg -
ASTM Data
Indice de fluidité, MFI 20 g/10min ASTM D 1238
Température 300 °C -
Charge 1.2 kg -
Propriétés mécaniquesValeurUnitéNorme du test
ISO Data
Module en traction 2340 MPa ISO 527
Contrainte d'écoulement 57 MPa ISO 527
Déformation au seuil d'écoulement 5.4 % ISO 527
Contrainte à la rupture 56 MPa ISO 527
Déformation à la rupture 50 % ISO 527
Module de flexion 2140 MPa ISO 178
Résistance au choc Charpy, +23°C, 3mm N kJ/m² ISO 179/1eU
Résistance au choc Charpy, -30°C, 3mm N kJ/m² ISO 179/1eU
Résistance au choc Charpy (entaillé), +23°C, 3mm 65 kJ/m² ISO 179/1eA
Résistance au choc Charpy (entaillé), -30°C, 3mm 45 kJ/m² ISO 179/1eA
Résistance au choc Izod, +23°C N kJ/m² ISO 180/1U
Résistance au choc Izod (entaillé), +23°C, 3mm 65 kJ/m² ISO 180/1A
Résistance au choc Izod (entaillé), -30°C, 3mm 55 kJ/m² ISO 180/1A
ASTM Data
Module en traction 2260 MPa ASTM D 638
Module de traction d’élasticité 58 MPa ASTM D 638
Résistance de traction à la rupture 57 MPa ASTM D 638
Allongement d’élasticité 5.7 % ASTM D 638
Allongement à la rupture 118 % ASTM D 638
Module de flexion 2240 MPa ASTM D 790
Izod choc avec entaille, 1/8 in 736 J/m ASTM D 256
Izod choc avec entaille, bas température 618 J/m ASTM D 256
Température -30 °C -
Propriétés thermiquesValeurUnitéNorme du test
ISO Data
Température de fléchissement s/chrg, 1.80 MPa 116 °C ISO 75-1/-2
Température de ramolliss. Vicat, B 138 °C ISO 306
Température de ramolliss. Vicat, 120°C/h 50N 139 °C ISO 306
Inflammabilité pr. épaisseur h HB class IEC 60695-11-10
Epaisseur de l'éprouvette 0.5 mm -
Glow Wire Flammability Index (GWFI) 960 °C IEC 60695-2-12
Glow Wire Ignition Temperature (GWIT) 850 °C IEC 60695-2-13
GWIT - thickness tested (3) 3 mm -
ASTM Data
DTUL à 264 psi 121 °C ASTM D 648
Vicat température 138 °C ASTM D 1525
Propriétés diversesValeurUnitéNorme du test
Absorption d'eau 0.24 % Sim. to ISO 62
Absorption d'humidité 0.09 % Sim. to ISO 62
Masse volumique 1190 kg/m³ ISO 1183
Densité 1190 kg/m³ ASTM D 792
Recommandations pour la transformation Moulage par injectionValeurUnitéNorme du test
Pré-séchage - température 120 °C -
Pré-séchage - temps 3 - 4 h -
L'humidité de traitement ≤0.02 % -
Température de la matière fondue 295 - 315 °C -
Température du moule 70 - 95 °C -
Zone 1 270 - 295 °C -
Zone 2 280 - 305 °C -
Zone 3 295 - 315 °C -
Vitesse de rotation de vis 40 - 70 rpm -
Contre-pression 0.3 - 0.7 MPa -
Caractéristiques
Transformation
Moulage par injection
Propriétés spéciales
Transparent
Disponibilité régionale
Asia Pacific
Conditions générales
Copyright Altair Engineering GmbH. Altair Engineering GmbH assumes no liability for the system to be free of errors. The user takes sole responsibility for the use of this data under the exclusion of every liability from Altair Engineering GmbH; this is especially valid for claims of compensation resulting from consequential damages. Altair explicitly points out that any decision about the application of materials must be double checked with the producer of this material. This includes all contents of this system. Copyright laws are applicable for the content of this system.
Created: Source: www.materialdatacenter.com