Material Data Center is a leading international information system for the plastics industry. Material Data Center offers a comprehensive plastics database, calculation tools, CAE interfaces, a literature database and an application database. For more information about Material Data Center visit www.materialdatacenter.com.

This is the free Material Data Center Datasheet of LEXAN™ Copolymer FST9405 - Europe - PC - Saudi Basic Industries Corporation (SABIC)

Material Data Center offers the following functions for LEXAN™ Copolymer FST9405 - Europe:
unit conversion, PDF datasheet print, comparison with other plastics, snap fit calculation, beam deflection calculation, CAE Interfaces

Check here, which other Lexan datasheets, application examples or technical articles are available in Material Data Center

Use the following short links to get directly to the properties of interest in this datasheet:
Caracteristicas de procesamiento y fisicas - Propiedades mecánicas - Propiedades térmicas - Otras propiedades - Recomendación para procesamiento Moldeo por inyección
Any use of this information falls under the rules of our disclaimer.
Texto del producto
LEXAN FST9405 resin is a high flow PC Copolymer Resin, suitable for injection molding. This halogen-free flame retardant resin is OSU55/55 and FAR25.853 compliant and an ideal candidate for aircraft interior applications. Available in opaque colors.
Caracteristicas de procesamiento y fisicasValorUnidadesMétodo de ensayo
ISO Data
Indice de fluidez volumétrico, MVR 10 cm³/10min ISO 1133
Temperatura 300 °C -
Carga 1.2 kg -
ASTM Data
Índice de fluidez, MFI 9 g/10min ASTM D 1238
Temperatura 300 °C -
Carga 1.2 kg -
Propiedades mecánicasValorUnidadesMétodo de ensayo
ISO Data
Módulo de tracción 2600 MPa ISO 527
Esfuerzo de fluencia 77 MPa ISO 527
Alarg. en límite elástico 6 % ISO 527
Resistencia a la tracción 70 MPa ISO 527
Alargamiento a rotura 50 % ISO 527
Modulo de Flexión 2500 MPa ISO 178
Resistencia al impacto Charpy, +23°C N kJ/m² ISO 179/1eU
Resistencia al impacto Charpy, -30°C N kJ/m² ISO 179/1eU
Resistencia al impacto Charpy, +23°C, 3mm N kJ/m² ISO 179/1eU
Resistencia al impacto Charpy, -30°C, 3mm N kJ/m² ISO 179/1eU
Resistencia al impacto Charpy c/entalla, +23°C N kJ/m² ISO 179/1eA
Resistencia al impacto Charpy c/entalla, -30°C N kJ/m² ISO 179/1eA
Resistencia al impacto Charpy c/entalla, +23°C, 3mm N kJ/m² ISO 179/1eA
Resistencia al impacto Charpy c/entalla, -30°C, 3mm N kJ/m² ISO 179/1eA
Resistencia al impacto Izod, +23°C N kJ/m² ISO 180/1U
Res. impacto Izod c/entalla, +23°C, 4mm 11 kJ/m² ISO 180/1A
Res. impacto Izod c/entalla, -30°C, 4mm 9 kJ/m² ISO 180/1A
. impacto Izod c/entalla, +23°C, 3mm 12 kJ/m² ISO 180/1A
ASTM Data
Módulo de tracción 2600 MPa ASTM D 638
Esfuerzo de fluencia a tracción 77 MPa ASTM D 638
Esfuerzo de fractura a tracción 70 MPa ASTM D 638
Alargamiento a la fluencia 6 % ASTM D 638
Alargamiento a la rotura 75 % ASTM D 638
Módulo de flexión 2700 MPa ASTM D 790
Resistencia al impacto Izod con entalla, 1/8 in 130 J/m ASTM D 256
Resistencia al impacto Izod con entalla, baja temperatura 85 J/m ASTM D 256
Temperatura -30 °C -
Propiedades térmicasValorUnidadesMétodo de ensayo
ISO Data
Estabilidad al calor, 1.80 MPa 94 °C ISO 75-1/-2
Estabilidad al calor, 0.45 MPa 104 °C ISO 75-1/-2
Temp. reblandecimiento Vicat, 120°C/h 50N 113 °C ISO 306
ASTM Data
Estabilidad al calor @ 66 psi 105 °C ASTM D 648
Estabilidad al calor @ 264 psi 95 °C ASTM D 648
Temperatura Vicat 114 °C ASTM D 1525
Otras propiedadesValorUnidadesMétodo de ensayo
Densidad 1330 kg/m³ ISO 1183
Densidad 1330 kg/m³ ASTM D 792
Recomendación para procesamiento Moldeo por inyecciónValorUnidadesMétodo de ensayo
Temperatura de pre-secado 95 - 100 °C -
Tiempo de pre-secado 6 - 8 h -
Temperatura de la masa 250 - 280 °C -
Temperatura del molde 50 - 80 °C -
Zona 1 230 - 250 °C -
Zona 2 240 - 270 °C -
Zona 3 250 - 280 °C -
Velocidad de giro de husillo 40 - 70 rpm -
Contrapresión 0.3 - 0.7 MPa -
Características
Procesamiento y forma de entrega
Moldeo por inyección
Aditivos
Ignifugante
Características especiales
Resistencia mejorada al fuego
Applicaciones
Automotriz
Disponibilidad regional
Europa
Disclaimer
Copyright Altair Engineering GmbH. Altair Engineering GmbH assumes no liability for the system to be free of errors. The user takes sole responsibility for the use of this data under the exclusion of every liability from Altair Engineering GmbH; this is especially valid for claims of compensation resulting from consequential damages. Altair explicitly points out that any decision about the application of materials must be double checked with the producer of this material. This includes all contents of this system. Copyright laws are applicable for the content of this system.
Created: Source: www.materialdatacenter.com