Material Data Center is a leading international information system for the plastics industry. Material Data Center offers a comprehensive plastics database, calculation tools, CAE interfaces, a literature database and an application database. For more information about Material Data Center visit www.materialdatacenter.com.

This is the free Material Data Center Datasheet of NORYL GTX™ Resin GTX975 - Asia - (PPE+PA*)-MF18 - Saudi Basic Industries Corporation (SABIC)

Material Data Center offers the following functions for NORYL GTX™ Resin GTX975 - Asia:
unit conversion, PDF datasheet print, comparison with other plastics, snap fit calculation, beam deflection calculation, CAE Interfaces

Check here, which other Noryl datasheets, application examples or technical articles are available in Material Data Center

Use the following short links to get directly to the properties of interest in this datasheet:
Processing/Physical Characteristics - Mechanical properties - Thermal properties - Other properties - Processing Recommendation Injection Molding
Any use of this information falls under the rules of our disclaimer.
Product Texts
NORYL GTX™ 975 resin is a conductive, 18% mineral reinforced alloy of Polyphenylene Ether (PPE) + Polyamide (PA). This injection moldable grade combines high stiffness and excellent temperature resistance with conductivity for primerless electrostatic painting. NORYL GTX975 was designed for in- or on-line painted exterior automotive trim parts such as tank flaps and corner panels.
Processing/Physical CharacteristicsValueUnitTest Standard
ISO Data
Melt volume-flow rate, MVR 10 cm³/10min ISO 1133
Temperature 280 °C -
Load 5 kg -
ASTM Data
Melt Flow Index, MFI 15 g/10min ASTM D 1238
Temperature 280 °C -
Load 5 kg -
Mechanical propertiesValueUnitTest Standard
ISO Data
Tensile Modulus 4200 MPa ISO 527
Yield stress 65 MPa ISO 527
Yield strain 3.5 % ISO 527
Stress at break 65 MPa ISO 527
Strain at break 4 % ISO 527
Flexural modulus 4000 MPa ISO 178
Charpy impact strength, +23°C 40 kJ/m² ISO 179/1eU
Charpy impact strength, -30°C 35 kJ/m² ISO 179/1eU
Charpy notched impact strength, +23°C 3 kJ/m² ISO 179/1eA
Charpy notched impact strength, -30°C 3 kJ/m² ISO 179/1eA
Izod impact strength, +23°C, 4mm 40 kJ/m² ISO 180/1U
Izod impact strength, -30°C, 4mm 35 kJ/m² ISO 180/1U
Izod notched impact strength, +23°C, 4mm 4 kJ/m² ISO 180/1A
Izod notched impact strength, -30°C, 4mm 4 kJ/m² ISO 180/1A
ASTM Data
Tensile Modulus 4450 MPa ASTM D 638
Tensile Strength at Yield 69 MPa ASTM D 638
Tensile Strength at Break 68 MPa ASTM D 638
Elongation at Yield 3.5 % ASTM D 638
Elongation at Break 4.5 % ASTM D 638
Flexural Modulus 4000 MPa ASTM D 790
Izod Impact notched, 1/8 in 35 J/m ASTM D 256
Izod Impact notched, Low-Temperature 30 J/m ASTM D 256
Temperature -30 °C -
Thermal propertiesValueUnitTest Standard
ISO Data
Vicat softening temperature, B 195 °C ISO 306
Vicat softening temperature, 120°C/h 50N 200 °C ISO 306
Coeff. of linear therm. expansion, parallel 50 E-6/K ISO 11359-1/-2
Coeff. of linear therm. expansion, normal 65 E-6/K ISO 11359-1/-2
ASTM Data
DTUL @ 66 psi 210 °C ASTM D 648
Vicat Temperature 215 °C ASTM D 1525
Other propertiesValueUnitTest Standard
Water absorption 3.5 % Sim. to ISO 62
Humidity absorption 1.1 % Sim. to ISO 62
Density 1200 kg/m³ ISO 1183
Density 1250 kg/m³ ASTM D 792
Processing Recommendation Injection MoldingValueUnitTest Standard
Pre-drying - Temperature 100 - 110 °C -
Pre-drying - Time 2 - 3 h -
Processing humidity ≤0.02 % -
Melt temperature 280 - 300 °C -
Mold temperature 100 - 120 °C -
Feed temperature 80 - 100 °C -
Zone 1 260 - 280 °C -
Zone 2 270 - 290 °C -
Zone 3 280 - 300 °C -
Characteristics
Processing
Injection Molding
Applications
Automotive
Regional Availability
Asia Pacific
Disclaimer
Copyright Altair Engineering GmbH. Altair Engineering GmbH assumes no liability for the system to be free of errors. The user takes sole responsibility for the use of this data under the exclusion of every liability from Altair Engineering GmbH; this is especially valid for claims of compensation resulting from consequential damages. Altair explicitly points out that any decision about the application of materials must be double checked with the producer of this material. This includes all contents of this system. Copyright laws are applicable for the content of this system.
Created: Source: www.materialdatacenter.com