Processing/Physical Characteristics | Value | Unit | Test Standard |
ISO Data |
Melt volume-flow rate, MVR |
5 |
cm³/10min |
ISO 1133 |
Temperature |
300 |
°C |
- |
Load |
1.2 |
kg |
- |
Molding shrinkage, parallel |
0.6 |
% |
ISO 294-4, 2577 |
Molding shrinkage, normal |
0.6 |
% |
ISO 294-4, 2577 |
Mechanical properties | Value | Unit | Test Standard |
ISO Data |
Yield stress |
65 |
MPa |
ISO 527 |
Nominal strain at break |
70 |
% |
ISO 527 |
Flexural modulus, 23°C |
2300 |
MPa |
ISO 178 |
Flexural strength |
90 |
MPa |
ISO 178 |
Rockwell hardness |
R 120 |
- |
ISO 2039-2 |
Thermal properties | Value | Unit | Test Standard |
ISO Data |
Temp. of deflection under load, 1.80 MPa |
125 |
°C |
ISO 75-1/-2 |
Temp. of deflection under load, 0.45 MPa |
140 |
°C |
ISO 75-1/-2 |
Coeff. of linear therm. expansion, parallel |
65 |
E-6/K |
ISO 11359-1/-2 |
Burning behav. at 1.5 mm nom. thickn. |
V-0 |
class |
IEC 60695-11-10 |
Thickness tested |
1.5 |
mm |
- |
Burning behav. at thickness h |
V-2 |
class |
IEC 60695-11-10 |
Thickness tested |
0.4 |
mm |
- |
Burning behav. 5V at thickness h |
5VA |
class |
IEC 60695-11-20 |
Thickness tested |
4.0 |
mm |
- |
Electrical properties | Value | Unit | Test Standard |
ISO Data |
Electric strength |
30 |
kV/mm |
IEC 60243-1 |
Other Standards[S] |
Relative permittivity, 1MHz |
2.85 |
- |
IEC 60250 |
S: | These properties are reported by the producer according standards that are different to our defaults. |
Optical properties | Value | Unit | Test Standard |
ISO Data |
Luminous transmittance |
87[1] |
% |
ISO 13468-1, -2 |
Other properties | Value | Unit | Test Standard |
Density |
1200 |
kg/m³ |
ISO 1183 |
Processing Recommendation Injection Molding | Value | Unit | Test Standard |
Pre-drying - Temperature |
120 |
°C |
- |
Pre-drying - Time |
5 - 8 |
h |
- |
Mold temperature |
80 - 120 |
°C |
- |
Zone 1 |
260 - 300 |
°C |
- |
Characteristics
Processing
Injection Molding
Special Characteristics
Flame retardant, Transparent
Regional Availability
North America, Europe, Asia Pacific
Disclaimer
Copyright Altair Engineering GmbH. Altair Engineering GmbH assumes no liability for the system to be free of errors. The user takes sole responsibility for the use of this data under the exclusion of every liability from Altair Engineering GmbH; this is especially valid for claims of compensation resulting from consequential damages. Altair explicitly points out that any decision about the application of materials must be double checked with the producer of this material. This includes all contents of this system. Copyright laws are applicable for the content of this system.
Created: Source: www.materialdatacenter.com