Material Data Center is a leading international information system for the plastics industry. Material Data Center offers a comprehensive plastics database, calculation tools, CAE interfaces, a literature database and an application database. For more information about Material Data Center visit www.materialdatacenter.com.

This is the free Material Data Center Datasheet of WONDERLOY PC-365 - (PC+ABS) - Chi Mei Corporation

Material Data Center offers the following functions for WONDERLOY PC-365:
unit conversion, PDF datasheet print, comparison with other plastics

Check here, which other Wonderloy datasheets, application examples or technical articles are available in Material Data Center

Use the following short links to get directly to the properties of interest in this datasheet:
Processing/Physical Characteristics - 機械的特性 - 熱的特性 - 電気的特性. - その他の特性. - Processing Recommendation Injection Molding
Any use of this information falls under the rules of our disclaimer.
Processing/Physical Characteristics値単位テスト基準
ISO データ
メルトボリュームレイト, MVR 20 cm³/10min ISO 1133
温度 260 °C -
荷重 5 kg -
成形収縮率, 平行 0.5 % ISO 294-4, 2577
ASTM数据
メルトフローレイト, MFI 20 g/10min ASTM D 1238
温度 260 °C -
荷重 5 kg -
成形収縮率., 平行 0.005 mm/mm ASTM D 955
機械的特性値単位テスト基準
ISO データ
降伏応力 54 MPa ISO 527
破壊応力 50 MPa ISO 527
曲げ弾性率, 23°C 2200 MPa ISO 178
曲げ強さ 80 MPa ISO 178
ノッチ付きシャルピー衝撃強さ, +23°C 50 kJ/m² ISO 179/1eA
ノッチ付きシャルピー衝撃強さ, -30ﾟC 45 kJ/m² ISO 179/1eA
ノッチ付きIzod衝撃強さ, +23°C 50 kJ/m² ISO 180/1A
ノッチ付きIzod衝撃強さ 45 kJ/m² ISO 180/1A
温度 -30 °C -
ASTM数据
降伏応力 53 MPa ASTM D 638
破断伸び 85 % ASTM D 638
曲げ弾性率 2256 MPa ASTM D 790
曲げ強さ 78.5 MPa ASTM D 790
ロックウェル硬度 R 115 - ASTM D 785
ノッチ付きIzod衝撃強さ, 1/8 in 539 J/m ASTM D 256
ノッチ付きIzod衝撃強さ, Low-Temperature 491 J/m ASTM D 256
温度 -34.4 °C -
熱的特性値単位テスト基準
ISO データ
荷重たわみ温度, 1.80 MPa 102 °C ISO 75-1/-2
ビカット軟化温度, A 138 °C ISO 306
ビカット軟化温度, B 127 °C ISO 306
線膨張係数, 平行 80 E-6/K ISO 11359-1/-2
1.5mm厚さでの燃焼性 HB class IEC 60695-11-10
試験片の厚さ 1.5 mm -
ASTM数据
UL94 燃焼性 HB - UL 94
追加試験片の厚さ 1.5 mm -
DTUL @ 264 psi 106 °C ASTM D 648
ビカット軟化温度 136 °C ASTM D 1525
電気的特性.値単位テスト基準
ISO データ
比誘電率, 1MHz 3.1 - IEC 62631-2-1
体積抵抗率 1E16 Ohm*m IEC 62631-3-1
表面抵抗率 1E16 Ohm IEC 62631-3-2
その他の特性.値単位テスト基準
密度. 1130 kg/m³ ISO 1183
密度 1130 kg/m³ ASTM D 792
Processing Recommendation Injection Molding値単位テスト基準
Pre-drying - Temperature 80 - 100 °C -
Pre-drying - Time 4 h -
金型温度 50 - 100 °C -
Zone 1 230 - 270 °C -
特殊な特性
成形加工法.
射出成形.
納入形状.
ペレット.
特殊な特性.
高耐衝撃及び耐衝撃改良., 熱安定化.
アプリケーション
自動車, 電気電子, 汎用
領域別の利用可能性
アジア/太平洋地域.
Disclaimer
Copyright Altair Engineering GmbH. Altair Engineering GmbH assumes no liability for the system to be free of errors. The user takes sole responsibility for the use of this data under the exclusion of every liability from Altair Engineering GmbH; this is especially valid for claims of compensation resulting from consequential damages. Altair explicitly points out that any decision about the application of materials must be double checked with the producer of this material. This includes all contents of this system. Copyright laws are applicable for the content of this system.
Created: Source: www.materialdatacenter.com