Complete Set of CAMPUS® Data, ASTM Data, Biopolymer Database, Application Database, Tradename Database, Literature Database, Toolbox.

Material datasheets available free. Online registration at: www.materialdatacenter.com

Material Data Center is a leading international information system for the plastics industry. Material Data Center offers a comprehensive plastics database, calculation tools, CAE interfaces, a literature database and an application database. For more information about Material Data Center visit www.materialdatacenter.com.

This is the free Material Data Center Datasheet of ULTEM™ Resin 9011 - Asia - PEI - Saudi Basic Industries Corporation (SABIC)

Material Data Center offers the following functions for ULTEM™ Resin 9011 - Asia:
unit conversion, PDF datasheet print, comparison with other plastics, snap fit calculation, beam deflection calculation, CAE Interfaces

Check here, which other Ultem datasheets, application examples or technical articles are available in Material Data Center

Use the following short links to get directly to the properties of interest in this datasheet:
Processing/Physical Characteristics - 機械的特性 - 熱的特性 - 電気的特性. - その他の特性. - Processing Recommendation Injection Molding
Any use of this information falls under the rules of our disclaimer.
商品の説明文
Transparent, high flow Polyetherimide (Tg 217C). ECO Conforming. Improved processability for Fiber extrusion.
Processing/Physical Characteristics値単位テスト基準
ISO データ
メルトボリュームレイト, MVR 25 cm³/10min ISO 1133
温度 360 °C -
荷重 5 kg -
ASTM数据
メルトフローレイト, MFI 17.8 g/10min ASTM D 1238
温度 337 °C -
荷重 6.6 kg -
機械的特性値単位テスト基準
ISO データ
引張弾性率 3200 MPa ISO 527
降伏応力 105 MPa ISO 527
降伏ひずみ 6 % ISO 527
破壊応力 85 MPa ISO 527
破壊ひずみ 50 % ISO 527
曲げ弾性率 3300 MPa ISO 178
ノッチ付きシャルピー衝撃強さ, +23°C 3 kJ/m² ISO 179/1eA
Izod impact strength, +23°C, 4mm N kJ/m² ISO 180/1U
Izod impact strength, -30°C, 4mm N kJ/m² ISO 180/1U
ノッチ付きアイゾット衝撃強さ, +23°C, 4mm 5 kJ/m² ISO 180/1A
ノッチ付きアイゾット衝撃強さ, -30°C, 4mm 5 kJ/m² ISO 180/1A
ASTM数据
引張弾性率 3590 MPa ASTM D 638
降伏応力 110 MPa ASTM D 638
破壊応力 105 MPa ASTM D 638
降伏点伸び 7 % ASTM D 638
破断伸び 60 % ASTM D 638
曲げ弾性率 3520 MPa ASTM D 790
ノッチ付きIzod衝撃強さ, 1/8 in 32 J/m ASTM D 256
ノッチ付きIzod衝撃強さ, Low-Temperature 35 J/m ASTM D 256
温度 -30 °C -
アイゾット衝撃試験, 1/8 in 1340 J/m ASTM D 256
熱的特性値単位テスト基準
ISO データ
荷重たわみ温度, 1.80 MPa 193 °C ISO 75-1/-2
ビカット軟化温度, A 215 °C ISO 306
ビカット軟化温度, B 211 °C ISO 306
ビカット軟化温度, 120°C/h 50N 212 °C ISO 306
ASTM数据
DTUL @ 66 psi 205 °C ASTM D 648
DTUL @ 264 psi 197 °C ASTM D 648
ビカット軟化温度 219 °C ASTM D 1525
電気的特性.値単位テスト基準
ASTM数据
耐電圧, 短い時間 28 kV/mm ASTM D 149
体積抵抗率 >1E15 Ohm*cm ASTM D 257
その他の特性.値単位テスト基準
吸水率. 1.25 % Sim. to ISO 62
吸湿率 0.7 % Sim. to ISO 62
密度. 1270 kg/m³ ISO 1183
密度 1270 kg/m³ ASTM D 792
Processing Recommendation Injection Molding値単位テスト基準
Pre-drying - Temperature 150 °C -
Pre-drying - Time 4 - 6 h -
Processing humidity ≤0.02 % -
樹脂温度 350 - 400 °C -
金型温度 135 - 165 °C -
Zone 1 330 - 400 °C -
Zone 2 340 - 400 °C -
Zone 3 345 - 400 °C -
Screw speed 40 - 70 rpm -
Back pressure 0.3 - 0.7 MPa -
特殊な特性
成形加工法.
射出成形.
特殊な特性.
透明.
アプリケーション
自動車
領域別の利用可能性
アジア/太平洋地域.
Disclaimer
Copyright Altair Engineering GmbH. Altair Engineering GmbH assumes no liability for the system to be free of errors. The user takes sole responsibility for the use of this data under the exclusion of every liability from Altair Engineering GmbH; this is especially valid for claims of compensation resulting from consequential damages. Altair explicitly points out that any decision about the application of materials must be double checked with the producer of this material. This includes all contents of this system. Copyright laws are applicable for the content of this system.
Created: Source: www.materialdatacenter.com


Material Data Center is provided by M-Base Engineering + Software GmbH. M-Base Engineering + Software GmbH assumes no liability for the system to be free of errors. Any decision about the application of materials must be double checked with the producer of this material.

Additional information about this material, like producer contact address, etc. can be found at www.materialdatacenter.com. For access to this extra information a registration is requested. Free online registration is available.