Material Data Center is a leading international information system for the plastics industry. Material Data Center offers a comprehensive plastics database, calculation tools, CAE interfaces, a literature database and an application database. For more information about Material Data Center visit www.materialdatacenter.com.

This is the free Material Data Center Datasheet of SPESIN® KP212G30V0BLS - PBT-GF30 - Kolon Industries

Material Data Center offers the following functions for SPESIN® KP212G30V0BLS:
unit conversion, PDF datasheet print

Check here, which other Spesin datasheets, application examples or technical articles are available in Material Data Center

Use the following short links to get directly to the properties of interest in this datasheet:
Any use of this information falls under the rules of our disclaimer.
Processing/Physical Characteristics単位テスト基準
ASTM数据
成形収縮率., 平行 0.0085 mm/mm ASTM D 955
機械的特性単位テスト基準
ISO データ
引張強度 138 MPa ISO 527
曲げ弾性率, 23°C 9190 MPa ISO 178
ノッチ付きシャルピー衝撃強さ, +23°C 6.6 kJ/m² ISO 179/1eA
ロックウェル硬度 R 120 - ISO 2039-2
ASTM数据
引張強度 132 MPa ASTM D 638
曲げ弾性率 8826 MPa ASTM D 790
曲げ強さ 206 MPa ASTM D 790
ロックウェル硬度 R 120 - ASTM D 785
ノッチ付きIzod衝撃強さ, 1/8 in 78 J/m ASTM D 256
熱的特性単位テスト基準
ISO データ
溶融温度, 10゚C/min 224 °C ISO 11357-1/-3
荷重たわみ温度, 1.80 MPa 200 °C ISO 75-1/-2
厚さhでの燃焼性 V-0 class IEC 60695-11-10
試験片の厚さ 0.8 mm -
ASTM数据
UL94 燃焼性 V-0 - UL 94
追加試験片の厚さ 0.8 mm -
線膨張係数, 平行 40 E-6/K ASTM D 696
DTUL @ 66 psi 220 °C ASTM D 648
DTUL @ 264 psi 200 °C ASTM D 648
溶融温度 224 °C ASTM D 3418
電気的特性.単位テスト基準
ASTM数据
耐電圧, 短い時間 27 kV/mm ASTM D 149
比誘電率, 1 MHz 3.7 - ASTM D 150
耐アーク 110 s ASTM D 495
その他の特性.単位テスト基準
密度. 1630 kg/m³ ISO 1183
密度 1630 kg/m³ ASTM D 792
Processing Recommendation Injection Molding単位テスト基準
Pre-drying - Temperature 100 - 120 °C -
Pre-drying - Time 3 - 5 h -
Processing humidity ≤0.05 % -
金型温度 60 - 80 °C -
Zone 1 240 °C -
Zone 2 245 °C -
Zone 3 250 °C -
Nozzle temperature 250 °C -
特殊な特性
成形加工法.
射出成形.
納入形状.
特殊な特性.
難燃.
耐薬品性
Hydrolytically Stable
領域別の利用可能性
北アメリカ., アジア/太平洋地域.
Disclaimer
Copyright Altair Engineering GmbH. Altair Engineering GmbH assumes no liability for the system to be free of errors. The user takes sole responsibility for the use of this data under the exclusion of every liability from Altair Engineering GmbH; this is especially valid for claims of compensation resulting from consequential damages. Altair explicitly points out that any decision about the application of materials must be double checked with the producer of this material. This includes all contents of this system. Copyright laws are applicable for the content of this system.
Created: Source: www.materialdatacenter.com


Material Data Center is provided by M-Base Engineering + Software GmbH. M-Base Engineering + Software GmbH assumes no liability for the system to be free of errors. Any decision about the application of materials must be double checked with the producer of this material.

Additional information about this material, like producer contact address, etc. can be found at www.materialdatacenter.com. For access to this extra information a registration is requested. Free online registration is available.