Material Data Center is a leading international information system for the plastics industry. Material Data Center offers a comprehensive plastics database, calculation tools, CAE interfaces, a literature database and an application database. For more information about Material Data Center visit www.materialdatacenter.com.

This is the free Material Data Center Datasheet of RAVAMID® C GF35 BK IK - PA666-GF35 - Ravago Group

Material Data Center offers the following functions for RAVAMID® C GF35 BK IK:
unit conversion, PDF datasheet print, comparison with other plastics, snap fit calculation, beam deflection calculation, CAE Interfaces

Check here, which other Ravamid datasheets, application examples or technical articles are available in Material Data Center

Use the following short links to get directly to the properties of interest in this datasheet:
Any use of this information falls under the rules of our disclaimer.
Processing/Physical Characteristics単位テスト基準
ASTM数据
成形収縮率., 平行 0.0016 mm/mm ASTM D 955
成形収縮率, 直角 0.0081 mm/mm ASTM D 955
機械的特性単位テスト基準
ISO データ
引張弾性率 6500 MPa ISO 527
降伏応力 110 MPa ISO 527
破壊ひずみ 3 % ISO 527
曲げ弾性率, 23°C 7000 MPa ISO 178
ノッチ付きIzod衝撃強さ, +23°C 6.5 kJ/m² ISO 180/1A
熱的特性単位テスト基準
ISO データ
荷重たわみ温度, 1.80 MPa 220[ann.] °C ISO 75-1/-2
ビカット軟化温度, B 205 °C ISO 306
1.5mm厚さでの燃焼性 HB class IEC 60695-11-10
試験片の厚さ 1.6 mm -
厚さhでの燃焼性 HB class IEC 60695-11-10
試験片の厚さ 3.2 mm -
グローワイヤ燃焼性指数 (GWFI) 650 °C IEC 60695-2-12
GWFI - 試験片の厚さ 2 mm -
ann.: annealed
その他の特性.単位テスト基準
吸湿率 0.15 % Sim. to ISO 62
密度. 1410 kg/m³ ISO 1183
Processing Recommendation Injection Molding単位テスト基準
Pre-drying - Temperature 85 °C -
Pre-drying - Time 3 - 4 h -
Processing humidity ≤0.12 % -
樹脂温度 240 - 280 °C -
金型温度 60 - 80 °C -
Zone 1 230 - 240 °C -
Zone 2 250 - 260 °C -
Zone 3 260 - 270 °C -
Nozzle temperature 260 - 265 °C -
Screw speed 50 - 80 rpm -
Back pressure 0.4 - 0.8 MPa -
後硬化時間 6 - 8 MPa -
特殊な特性
成形加工法.
射出成形.
納入形状.
な特性
Copolymer
Certifications
Recycled Resin Content
領域別の利用可能性
ヨーロッパ.
Disclaimer
Copyright Altair Engineering GmbH. Altair Engineering GmbH assumes no liability for the system to be free of errors. The user takes sole responsibility for the use of this data under the exclusion of every liability from Altair Engineering GmbH; this is especially valid for claims of compensation resulting from consequential damages. Altair explicitly points out that any decision about the application of materials must be double checked with the producer of this material. This includes all contents of this system. Copyright laws are applicable for the content of this system.
Created: Source: www.materialdatacenter.com