Material Data Center is a leading international information system for the plastics industry. Material Data Center offers a comprehensive plastics database, calculation tools, CAE interfaces, a literature database and an application database. For more information about Material Data Center visit www.materialdatacenter.com.

This is the free Material Data Center Datasheet of NORYL PPX™ Resin PPX7115 - Americas - (PPE+PP) - Saudi Basic Industries Corporation (SABIC)

Material Data Center offers the following functions for NORYL PPX™ Resin PPX7115 - Americas:
unit conversion, PDF datasheet print, comparison with other plastics, snap fit calculation, beam deflection calculation, CAE Interfaces

Check here, which other Noryl datasheets, application examples or technical articles are available in Material Data Center

Use the following short links to get directly to the properties of interest in this datasheet:
Processing/Physical Characteristics - 機械的特性 - 熱的特性 - その他の特性. - Processing Recommendation Injection Molding
Any use of this information falls under the rules of our disclaimer.
商品の説明文
NORYL PPX™ 7115 resin is a non-reinforced alloy of polyphenylene ether (PPE) + polypropylene (PP). This injection moldable grade exhibits high modulus, high-temperature performance, excellent melt strength, impact resistance, hydrolytic and dimensional stability. NORYL PPX7115 resin is an excellent candidate for applications requiring high modulus and chemical resistance.

UL Yellow Card Link E121562-221243
Processing/Physical Characteristics値単位テスト基準
ISO データ
メルトボリュームレイト, MVR 12 cm³/10min ISO 1133
温度 260 °C -
荷重 5 kg -
ASTM数据
メルトフローレイト, MFI 14 g/10min ASTM D 1238
温度 260 °C -
荷重 5 kg -
機械的特性値単位テスト基準
ISO データ
引張弾性率 1370 MPa ISO 527
降伏応力 35 MPa ISO 527
破壊ひずみ 50 % ISO 527
ASTM数据
引張弾性率 1240 MPa ASTM D 638
降伏応力 35 MPa ASTM D 638
破壊応力 34 MPa ASTM D 638
降伏点伸び 8 % ASTM D 638
破断伸び 125 % ASTM D 638
曲げ弾性率 1370 MPa ASTM D 790
ノッチ付きIzod衝撃強さ, 1/8 in 534 J/m ASTM D 256
熱的特性値単位テスト基準
ISO データ
ビカット軟化温度, A 131 °C ISO 306
1.5mm厚さでの燃焼性 HB class IEC 60695-11-10
試験片の厚さ 1.5 mm -
ASTM数据
DTUL @ 66 psi 112 °C ASTM D 648
DTUL @ 264 psi 85 °C ASTM D 648
ビカット軟化温度 86 °C ASTM D 1525
その他の特性.値単位テスト基準
密度 990 kg/m³ ASTM D 792
Processing Recommendation Injection Molding値単位テスト基準
Pre-drying - Temperature 60 - 65 °C -
Pre-drying - Time 2 - 4 h -
Processing humidity ≤0.02 % -
樹脂温度 260 - 290 °C -
金型温度 30 - 50 °C -
Zone 1 225 - 275 °C -
Zone 2 240 - 280 °C -
Zone 3 250 - 290 °C -
Screw speed 20 - 100 rpm -
Back pressure 0.3 - 0.7 MPa -
特殊な特性
成形加工法.
射出成形.
領域別の利用可能性
北アメリカ.
Disclaimer
Copyright Altair Engineering GmbH. Altair Engineering GmbH assumes no liability for the system to be free of errors. The user takes sole responsibility for the use of this data under the exclusion of every liability from Altair Engineering GmbH; this is especially valid for claims of compensation resulting from consequential damages. Altair explicitly points out that any decision about the application of materials must be double checked with the producer of this material. This includes all contents of this system. Copyright laws are applicable for the content of this system.
Created: Source: www.materialdatacenter.com


Material Data Center is provided by M-Base Engineering + Software GmbH. M-Base Engineering + Software GmbH assumes no liability for the system to be free of errors. Any decision about the application of materials must be double checked with the producer of this material.

Additional information about this material, like producer contact address, etc. can be found at www.materialdatacenter.com. For access to this extra information a registration is requested. Free online registration is available.