Complete Set of CAMPUS® Data, ASTM Data, Biopolymer Database, Application Database, Tradename Database, Literature Database, Toolbox.

Material datasheets available free. Online registration at: www.materialdatacenter.com

Material Data Center is a leading international information system for the plastics industry. Material Data Center offers a comprehensive plastics database, calculation tools, CAE interfaces, a literature database and an application database. For more information about Material Data Center visit www.materialdatacenter.com.

This is the free Material Data Center Datasheet of NORYL GTX™ Resin GTX918A - (PPE+PA*) - Saudi Basic Industries Corporation (SABIC)

Material Data Center offers the following functions for NORYL GTX™ Resin GTX918A:
unit conversion, PDF datasheet print, comparison with other plastics

Check here, which other Noryl datasheets, application examples or technical articles are available in Material Data Center

Use the following short links to get directly to the properties of interest in this datasheet:
Processing/Physical Characteristics - 機械的特性 - 熱的特性 - その他の特性. - Processing Recommendation Injection Molding
Any use of this information falls under the rules of our disclaimer.
商品の説明文
NORYL GTX™ 918A resin is a non-reinforced alloy of Polyphenylene Ether (PPE) + Polyamide (PA). This injection moldable grade exhibits high heat resistance, excellent chemical resistance, high melt flow, and added mold release. NORYL GTX918A resin may be an excellent candidate for automotive under-the-hood and electrical applications requiring the retention of properties while under thermal load.
Processing/Physical Characteristics値単位テスト基準
ISO データ
メルトボリュームレイト, MVR 5 cm³/10min ISO 1133
温度 280 °C -
荷重 1.2 kg -
ASTM数据
メルトフローレイト, MFI 45 g/10min ASTM D 1238
温度 280 °C -
荷重 5 kg -
機械的特性値単位テスト基準
ISO データ
降伏応力 60 MPa ISO 527
降伏ひずみ 4.5 % ISO 527
破壊応力 55 MPa ISO 527
破壊ひずみ 30 % ISO 527
曲げ弾性率 2200 MPa ISO 178
ノッチ付きシャルピー衝撃強さ, +23°C 20 kJ/m² ISO 179/1eA
ノッチ付きシャルピー衝撃強さ, -30ﾟC 10 kJ/m² ISO 179/1eA
ノッチ付きアイゾット衝撃強さ, +23°C, 4mm 20 kJ/m² ISO 180/1A
ノッチ付きアイゾット衝撃強さ, -30°C, 4mm 10 kJ/m² ISO 180/1A
ASTM数据
引張弾性率 810 MPa ASTM D 638
降伏応力 62 MPa ASTM D 638
破壊応力 57 MPa ASTM D 638
降伏点伸び 11.4 % ASTM D 638
破断伸び 53 % ASTM D 638
曲げ弾性率 2360 MPa ASTM D 790
ノッチ付きIzod衝撃強さ, 1/8 in 202 J/m ASTM D 256
熱的特性値単位テスト基準
ISO データ
ビカット軟化温度, A 245 °C ISO 306
ビカット軟化温度, B 190 °C ISO 306
ビカット軟化温度, 120°C/h 50N 195 °C ISO 306
線膨張係数, 平行 80 E-6/K ISO 11359-1/-2
線膨張係数, 直角 80 E-6/K ISO 11359-1/-2
ASTM数据
DTUL @ 66 psi 188 °C ASTM D 648
DTUL @ 264 psi 148 °C ASTM D 648
ビカット軟化温度 242 °C ASTM D 1525
熱伝導率, ソリッド 0.036 W/(m K) ASTM C 177
その他の特性.値単位テスト基準
密度 1090 kg/m³ ASTM D 792
Processing Recommendation Injection Molding値単位テスト基準
Pre-drying - Temperature 95 - 105 °C -
Pre-drying - Time 3 - 4 h -
Processing humidity ≤0.07 % -
樹脂温度 270 - 295 °C -
金型温度 65 - 95 °C -
Zone 1 255 - 295 °C -
Zone 2 260 - 295 °C -
Zone 3 265 - 295 °C -
Screw speed 20 - 100 rpm -
Back pressure 0.3 - 1.4 MPa -
特殊な特性
成形加工法.
射出成形.
アプリケーション
自動車
領域別の利用可能性
北アメリカ., ヨーロッパ., アジア/太平洋地域.
Disclaimer
Copyright Altair Engineering GmbH. Altair Engineering GmbH assumes no liability for the system to be free of errors. The user takes sole responsibility for the use of this data under the exclusion of every liability from Altair Engineering GmbH; this is especially valid for claims of compensation resulting from consequential damages. Altair explicitly points out that any decision about the application of materials must be double checked with the producer of this material. This includes all contents of this system. Copyright laws are applicable for the content of this system.
Created: Source: www.materialdatacenter.com


Material Data Center is provided by M-Base Engineering + Software GmbH. M-Base Engineering + Software GmbH assumes no liability for the system to be free of errors. Any decision about the application of materials must be double checked with the producer of this material.

Additional information about this material, like producer contact address, etc. can be found at www.materialdatacenter.com. For access to this extra information a registration is requested. Free online registration is available.