Complete Set of CAMPUS® Data, ASTM Data, Biopolymer Database, Application Database, Tradename Database, Literature Database, Toolbox.

Material datasheets available free. Online registration at: www.materialdatacenter.com

Material Data Center is a leading international information system for the plastics industry. Material Data Center offers a comprehensive plastics database, calculation tools, CAE interfaces, a literature database and an application database. For more information about Material Data Center visit www.materialdatacenter.com.

This is the free Material Data Center Datasheet of NORYL™ Resin PX0844 - Americas - (PPE+PS) - Saudi Basic Industries Corporation (SABIC)

Material Data Center offers the following functions for NORYL™ Resin PX0844 - Americas:
unit conversion, PDF datasheet print, comparison with other plastics, snap fit calculation, beam deflection calculation, CAE Interfaces

Check here, which other Noryl datasheets, application examples or technical articles are available in Material Data Center

Use the following short links to get directly to the properties of interest in this datasheet:
Processing/Physical Characteristics - 機械的特性 - 熱的特性 - その他の特性. - Processing Recommendation Injection Molding
Any use of this information falls under the rules of our disclaimer.
商品の説明文
NORYL™ PX0844 resin is a non-reinforced blend of polyphenylene ether (PPE) + high impact polystyrene (HIPS). This grade exhibits very low moisture absorption, hydrolytic stability, dimensional stabilty, good foam adhesion, and property retention over a wide temperature range. NORYL PX0844 resin is inherently UL94 HB and is an excellent candidate for automotive interior applications such as instrument panels, audio components, speaker housings, and interior trim. *see NORYL PX0888 resin for higher heat resistance.
Processing/Physical Characteristics値単位テスト基準
ASTM数据
メルトフローレイト, MFI 13.7 g/10min ASTM D 1238
温度 280 °C -
荷重 5 kg -
機械的特性値単位テスト基準
ISO データ
引張弾性率 2350 MPa ISO 527
降伏応力 47 MPa ISO 527
降伏ひずみ 2.9 % ISO 527
破壊応力 43 MPa ISO 527
破壊ひずみ 43 % ISO 527
曲げ弾性率 2400 MPa ISO 178
曲げ強さ 78 MPa ISO 178
ノッチ付きアイゾット衝撃強さ, +23°C, 4mm 17 kJ/m² ISO 180/1A
ノッチ付きアイゾット衝撃強さ, -30°C, 4mm 10 kJ/m² ISO 180/1A
ASTM数据
引張弾性率 2290 MPa ASTM D 638
降伏応力 49 MPa ASTM D 638
破壊応力 44 MPa ASTM D 638
降伏点伸び 3 % ASTM D 638
破断伸び 30 % ASTM D 638
曲げ弾性率 2550 MPa ASTM D 790
ロックウェル硬度 R 114 - ASTM D 785
ノッチ付きIzod衝撃強さ, 1/8 in 234 J/m ASTM D 256
ノッチ付きIzod衝撃強さ, Low-Temperature 133 J/m ASTM D 256
温度 -40 °C -
熱的特性値単位テスト基準
ISO データ
ビカット軟化温度, B 125 °C ISO 306
ビカット軟化温度, 120°C/h 50N 128 °C ISO 306
ASTM数据
DTUL @ 66 psi 120 °C ASTM D 648
DTUL @ 264 psi 105 °C ASTM D 648
その他の特性.値単位テスト基準
密度 1060 kg/m³ ASTM D 792
Processing Recommendation Injection Molding値単位テスト基準
Pre-drying - Temperature 105 - 110 °C -
Pre-drying - Time 3 - 4 h -
Processing humidity ≤0.02 % -
樹脂温度 275 - 305 °C -
金型温度 70 - 100 °C -
Zone 1 245 - 295 °C -
Zone 2 255 - 300 °C -
Zone 3 265 - 305 °C -
Screw speed 20 - 100 rpm -
Back pressure 0.3 - 0.7 MPa -
特殊な特性
成形加工法.
射出成形.
耐薬品性
Hydrolytically Stable
アプリケーション
自動車
領域別の利用可能性
北アメリカ.
Disclaimer
Copyright Altair Engineering GmbH. Altair Engineering GmbH assumes no liability for the system to be free of errors. The user takes sole responsibility for the use of this data under the exclusion of every liability from Altair Engineering GmbH; this is especially valid for claims of compensation resulting from consequential damages. Altair explicitly points out that any decision about the application of materials must be double checked with the producer of this material. This includes all contents of this system. Copyright laws are applicable for the content of this system.
Created: Source: www.materialdatacenter.com


Material Data Center is provided by M-Base Engineering + Software GmbH. M-Base Engineering + Software GmbH assumes no liability for the system to be free of errors. Any decision about the application of materials must be double checked with the producer of this material.

Additional information about this material, like producer contact address, etc. can be found at www.materialdatacenter.com. For access to this extra information a registration is requested. Free online registration is available.