Complete Set of CAMPUS® Data, ASTM Data, Biopolymer Database, Application Database, Tradename Database, Literature Database, Toolbox.

Material datasheets available free. Online registration at: www.materialdatacenter.com

Material Data Center is a leading international information system for the plastics industry. Material Data Center offers a comprehensive plastics database, calculation tools, CAE interfaces, a literature database and an application database. For more information about Material Data Center visit www.materialdatacenter.com.

This is the free Material Data Center Datasheet of NORYL™ Resin PKN4775 - Europe - (PPE+PS) - Saudi Basic Industries Corporation (SABIC)

Material Data Center offers the following functions for NORYL™ Resin PKN4775 - Europe:
unit conversion, PDF datasheet print, comparison with other plastics, snap fit calculation, beam deflection calculation, CAE Interfaces

Check here, which other Noryl datasheets, application examples or technical articles are available in Material Data Center

Use the following short links to get directly to the properties of interest in this datasheet:
Processing/Physical Characteristics - 機械的特性 - 熱的特性 - その他の特性.
Any use of this information falls under the rules of our disclaimer.
商品の説明文
NORYL PKN4775 resin is a non-reinforced, opaque blend of polyphenylene ether (PPE) + high impact polystyrene (HIPS). This high heat, thin wall extrusion and injection moldable grade is an improved version of NORYL PKN4736 resin and exhibits modulus at elevated temperature and good chemical resistance. NORYL PKN4775 resin is an excellent candidate for applications in high performance packaging. *See NORYL PKN4775F resin for FDA food compliant version.
Processing/Physical Characteristics値単位テスト基準
ISO データ
メルトボリュームレイト, MVR 14 cm³/10min ISO 1133
温度 300 °C -
荷重 5 kg -
ASTM数据
メルトフローレイト, MFI 15.3 g/10min ASTM D 1238
温度 300 °C -
荷重 5 kg -
機械的特性値単位テスト基準
ISO データ
引張弾性率 2120 MPa ISO 527
降伏応力 51 MPa ISO 527
降伏ひずみ 4.1 % ISO 527
破壊応力 47 MPa ISO 527
破壊ひずみ 29.3 % ISO 527
曲げ弾性率 2160 MPa ISO 178
ノッチ付きシャルピー衝撃強さ, +23°C 19 kJ/m² ISO 179/1eA
ノッチ付きアイゾット衝撃強さ, +23°C, 4mm 20 kJ/m² ISO 180/1A
ノッチ付きアイゾット衝撃強さ, -30°C, 4mm 11 kJ/m² ISO 180/1A
ASTM数据
引張弾性率 2120 MPa ASTM D 638
降伏応力 51 MPa ASTM D 638
破壊応力 47 MPa ASTM D 638
降伏点伸び 5.1 % ASTM D 638
破断伸び 35 % ASTM D 638
曲げ弾性率 2210 MPa ASTM D 790
ノッチ付きIzod衝撃強さ, 1/8 in 268 J/m ASTM D 256
ノッチ付きIzod衝撃強さ, Low-Temperature 161 J/m ASTM D 256
温度 -30 °C -
熱的特性値単位テスト基準
ISO データ
荷重たわみ温度, 1.80 MPa 122 °C ISO 75-1/-2
ビカット軟化温度, B 142 °C ISO 306
ビカット軟化温度, 120°C/h 50N 144 °C ISO 306
ASTM数据
DTUL @ 66 psi 138 °C ASTM D 648
DTUL @ 264 psi 122 °C ASTM D 648
ビカット軟化温度 142 °C ASTM D 1525
その他の特性.値単位テスト基準
吸水率. 0.25 % Sim. to ISO 62
吸湿率 0.05 % Sim. to ISO 62
密度. 1050 kg/m³ ISO 1183
密度 1050 kg/m³ ASTM D 792
特殊な特性
成形加工法.
シート押出成形.
耐薬品性
General Chemical Resistance
領域別の利用可能性
ヨーロッパ.
Disclaimer
Copyright Altair Engineering GmbH. Altair Engineering GmbH assumes no liability for the system to be free of errors. The user takes sole responsibility for the use of this data under the exclusion of every liability from Altair Engineering GmbH; this is especially valid for claims of compensation resulting from consequential damages. Altair explicitly points out that any decision about the application of materials must be double checked with the producer of this material. This includes all contents of this system. Copyright laws are applicable for the content of this system.
Created: Source: www.materialdatacenter.com


Material Data Center is provided by M-Base Engineering + Software GmbH. M-Base Engineering + Software GmbH assumes no liability for the system to be free of errors. Any decision about the application of materials must be double checked with the producer of this material.

Additional information about this material, like producer contact address, etc. can be found at www.materialdatacenter.com. For access to this extra information a registration is requested. Free online registration is available.